Mechanical properties and dry sliding wear behaviour of Al--Si--Mg alloy by equal channel angular pressing.

This study investigated the microstructure, hardness, tensile and tribological behaviour of a cooling slope Al--Si--Mg alloy following ECAP and T6 heat treatment. The optical and scanning electron microscopes were applied to investigate the microstructure of the as-cast material and heattreated ECAPed Al--Si--Mg alloy. The dry sliding wear test was tested with three different loads of 10 N, 50 N, and 100 N with constant sliding speed and sliding distance at 1.0 m/s and 9000 m, respectively, using the pin-on-disc tribometer. The hardness and tensile properties were evaluated through microhardness, UTS, and YS measurement for the as-cast Al--Si--Mg alloy, both heat-treated with and without ECAPed alloys. Moreover, wear rate and COF in the Al--Si--Mg alloy with different loads were analysed and linked with microstructural and strength behaviour after the ECAP process. Meanwhile, these analyses of results were correlated with the behaviour of the as-cast Al--Si--Mg aluminium alloy and heat-treated non-ECAPed alloy. Results demonstrated that a combination of ECAP processing and T6 heat treatment improves the mechanical behaviour, while the COF and wear rate are improved at a load of 100 N. [ABSTRACT FROM AUTHOR]