Preparation and properties of porous ceramics from nickel slag by aerogel gelcasting.

To further resource industrial solid waste, porous ceramics with high porosity were prepared by a gelcasting method using nickel slag and kaolin as raw materials and hydrophilic nontoxic SiO 2 aerogel as a gelling agent. The effects of nickel slag content, dispersant and solid content on the properties and microstructure of porous ceramics were investigated in detail in terms of density, compressive strength, porosity, phase composition and micromorphology. The results confirmed that a certain amount of nickel slag can effectively improve the porosity of porous ceramics, while the addition of dispersant can promote the flow of the slurry, enhanced the denseness of the raw billet and significantly improved the compressive strength. However, its excessive use had a negative effect on the ceramic density and porosity. At the same time, the solid content played a key role in the performance of porous ceramics prepared by gelcasting, and too much solid content was also not conducive to the generation of pores. When the nickel slag content was 55%, the amount of dispersant was 2%, and the solid content was 60 vol%, the porous ceramic had a better overall performance, the density of the porous ceramic was 510 kg/m3, the compressive strength was 1.3 MPa, and the porosity reached 80.1%. The major crystalline phases of porous ceramics prepared by nickel slag were cordierite and anorthite. [ABSTRACT FROM AUTHOR]