Synthesis of Layered Double Hydroxides with Phosphate Tailings and Its Effect on Flame Retardancy of Epoxy Resin.

In this work, phosphate tailings (PTs) were used as raw materials for the preparation of Ca-Mg-Al layered double hydroxides (LDHs-1) and Ca-Mg-Al-Fe layered double hydroxides (LDHs-2) by co-precipitation method. The as-prepared samples were characterized by FT-IR, SEM, XRD, and XPS and applied as a flame retardant to improve the fire safety of epoxy resin (EP). The results showed that both LDHs-1 and LDHs-2 exhibited layered structure and high crystallinity. Compared with neat EP, the value of limiting oxygen index (LOI) increased from 25.8 to 29.3 and 29.9 with 8 wt% content of LDHs-1 and LDHs-2, respectively. The flame retardant properties of the composite material were characterized by cone calorimeter (CC), and the results showed that the peak value of the smoke production rate (SPR) decreased more than 45% and 74%, total smoke production (TSP) reduced nearly 64% and 85% with the addition of LDHs-1 and LDHs-2. Meanwhile, the value of the total heat release (THR) reduced more than 28% and 63%. The conversion from LDHs to layered double oxide (LDO) might be conducive to the fire safety of EP. Moreover, the transformation of Fe-OH to Fe-O could promote the early cross-linking of polymer. In summary, LDHs-2 could significantly improve the carbonization process of EP and suppress the smoke released during the combustion process. [ABSTRACT FROM AUTHOR]