Effect of phenyl side groups on the dielectric properties and dielectric behavior of polysiloxane.

Over the past decades, polysiloxane-based dielectric elastomers (DEs) have attracted significant research attention; however, the low dielectric constant and poor breakdown strength of polysiloxane limit its application in DEs. In this study, the effect of phenyl side groups on the dielectric properties and unique dielectric relaxation behavior of polymethyl phenyl siloxane (PMPS) was investigated. The dielectric constant of PMPS was slightly improved from 3.45 to 3.60 by introducing appropriate amount of the phenyl side groups into polysiloxane. Moreover, the electrical breakdown strength of PMPS increased from 31.70 to 35.91 kV mm−1. The contribution of the α - and β -relaxations significantly increased the dielectric loss of PMPS. To better understand the effect of the phenyl side groups on these properties, the dielectric relaxation behavior of copolymers with different phenyl contents was studied in detail via broadband dielectric spectroscopy and thermally stimulated depolarization current measurements. This study paves a new path to design and prepare polysiloxane-based soft materials with high dielectric constant and improved electrical breakdown strength. [Display omitted] • 1, Polymethyl phenyl siloxanes random copolymers were synthesized. • 2, Breakdown strength of polysiloxanes were significantly improved. • 3, The relationship between polymer chains structure and dielectric behavior was revealed. [ABSTRACT FROM AUTHOR]