Study on anti-aged durability of HMA based on inherent and improved performance.

Purpose: The purpose of this study is to compare and analyze the anti-aging durability of asphalt and asphalt mixture under the conditions of inherent and improved performance. The research contents include: the mechanical properties (dynamic stability, bending strain, freeze-thaw splitting tensile strength ratio (TSR)) of different modified asphalt mixtures were tested by using the best modified asphalt. Design/methodology/approach: The anti-aging durability of different modified asphalt was analyzed by using the results of macro tests such as penetration and softening point as evaluation indexes. Meanwhile, the change of the asphalt colloid instability index (Ic) in the aging process was used as the evaluation index to verify the results of the macroscopic test, and the best modified asphalt was obtained. On this basis, the composition of different modified asphalt mixtures was designed by using the best modified asphalt. Meanwhile, water stability was used as evaluation indexes to study the anti-aging durability of different modified asphalt mixtures. Findings: The results show that styrene-butadiene-styrene (SBS) modified asphalt has better aging resistance. Due to the special storage time, the performance of rubber asphalt is also the best. Meanwhile, in terms of modified asphalt mixture, its high temperature performance and durability of anti-aging is as follows: 4% SBS /16% rubber modified asphalt mixture (IV) > 4% SBS modified asphalt mixture (II) > asphalt mixture (90#) (I) > 16% rubber modified asphalt mixture (III). The low temperature performance and durability of anti-aging is as follows: Ⅱ > IV > Ⅰ > Ⅲ. The water stability performance and durability of anti-aging is as follows: IV > Ⅲ > Ⅱ > Ⅰ. Originality/value: The research results have important theoretical and guiding significance for exploring the change of intrinsic properties and improved properties of asphalt and asphalt mixture in the aging process and revealing the anti-aging mechanism of different modified asphalt mixtures. [ABSTRACT FROM AUTHOR]