ВАКУУМНЕ ПАЯННЯ РІЗНОРІДНИХ З’ЄДНАНЬ КОВАР–МОЛІБДЕН.

The features of spreading of brazing filler metal of Cu-Mn-Co system over molybdenum and Kovar were established based on the performed studies. Micro X-ray spectral analysis determined that zonal crystallization of a brazing filler metal droplet on the base metal substrate occurs during spreading: pronounced areas of copper-based solid solution (Cu-12.92Mn-4.69Co) form along the outer perimeter of the droplet, and dendrites of manganese-based solid solution, characterized by a higher melting point, are crystallized in the drop central part. It has been experimentally proven that an increase in the heating temperature contributes to an increase in the spreading area of the brazing filler metal by improving the spreading of copper-based solid solution. It was found that a copper-based solid solution forms in the brazed seam of Kovar-molybdenum dissimilar joints, and a molybdenum-based reaction layer (about 1 μm wide), crystallizes at the molybdenum-brazing filler metal interface. This layer is enriched in cobalt (15.80%) and manganese (14.12%) and contains a small amount of copper (1.63%). %). As a result of mechanical tests of Kovar-molybdenum overlap joints under static loads at room temperature, destruction occurs partly along the brazed seam and partly along the base metal - molybdenum. 14 Ref., 2 Tabl., 6 Fig. [ABSTRACT FROM AUTHOR]