粉末冶金Ta-Ru合金的制备及力学性能.

In this paper, high purity Ta-Ru alloy was prepared by powder metallurgy hot press sintering. Tantalum ruthenium powder with high purity was mixed in different composition ratio on planetary ball mill, and hot pressed for 3 h at 1 700 ℃ and 20 MPa in vacuum hot pressing sintering furnace. The effect of different Ru contents on the phase composition, microstructure and mechanical properties of Ta-Ru alloys were investigated by XRD, SEM, EDS, tensile strength test and other analytical methods. The results show that, with increasing Ru content, several intermetallic compounds such as TaRu, Ta3Ru, and TaRu4 were successively formed in the alloy. The density and tensile strength of the alloy increased gradually, and the microhardness increased first and then decreased. The fracture mode changed from cleavage fracture to intergranular fracture and ductile fracture. [ABSTRACT FROM AUTHOR]