High-performance flexible electromagnetic shielding polyimide fabric prepared by nickel-tungsten-phosphorus electroless plating.

Abstract In this paper, functional polyimide (PI) fabric with high electrically conductive and electromagnetic shielding effect was prepared by nickel-tungsten-phosphorus (Ni-W-P) electroless plating. Firstly, a wave-absorbing and conductive polyaniline (PANI) layer was in-situ polymerized on the surface of fabric. Secondly, the PANI reduced the palladium ions to palladium particles acting as catalytically active sites. Finally, Ni-W-P electroless plating was initiated and formed a uniform and dense layer. The features of Ni-W-P alloy layer on PI fabric were characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). The thermal stability of the sample was also evaluated by thermogravimetric analysis (TGA). The results showed that the electrical conductivity was 0.08 Ω/sq and the outstanding electromagnetic shielding effectiveness (SE) could reach 103 dB. Moreover, the robust SE performance after multiple ultrasonic washing and bending tests also implied the resultant material had a great potential in the textile protection fields. Highlights • High conductivity and electromagnetic shielding PI fabrics was fabricated. • The fabric is prepared by nickel-tungsten-phosphorus electroless plating. • The mechanism is synergistic effect of wave reflection and wave absorption. [ABSTRACT FROM AUTHOR]