Evaluating the effect of manufacturing method on the radial compressive force of the bioresorbable tubes.

Highlights • A novel single step biaxial expansion method is used for bioresorbable tube fabrication. • Biaxially expanded tubes have better radial compressive properties. • Brittle behaviour of PLA changes to ductile by addition of 5 wt% PCL. Abstract Bioresorbable stents is going to become the future modality for the treatment of coronary artery disease (CAD). However, the main limitation of the polymeric stent is its poor mechanical properties. For the proper functioning of a stent in the artery; it is required to enhance the radial stiffness of the polymeric stent. Polymeric tube manufacturing is the first and most important step in the stent manufacturing process. Usually, post processing operation which enhances the mechanical properties such as annealing, blowing and die drawing near glass transition are used after tube extrusion. In this study, along with conventional tube extrusion process (SE), a single step biaxial expansion method (BAE) was employed during the tube extrusion. The effect of manufacturing method on the radial compressive strength of the extruded tubes is thereby evaluated. For further determining the tubes radial resistive force, parallel plate crush testing as per ISO 25539-2 was performed and it is observed that tubes extruded by BAE method have better performance during crush testing as compared to the SE tubes of the same material. SEM was used for observing the cross-sectional morphology of the Cryo-fractured surface of fabricated bioresorbable tubes. [ABSTRACT FROM AUTHOR]