Phase composition and magnetic properties in hot deformed magnets based on Misch-metal.

In this paper, the Rare-earth Iron Boron (RE-Fe-B) magnets were fabricated successfully by using the double main phase method through mixing the Neodymium Iron Boron (Nd-Fe-B) powders and Misch-metal Iron Boron (MM-Fe-B) powders with different ratio. Aiming at the nanocrystalline RE 2 Fe 14 B magnets prepared by using spark plasma sintering technology, phase structure and magnetic properties were investigated. It is found that the Misch-metal (MM) alloys promote the domain nucleation during the the process of magnetization reversal and then damage the coercivity ( H cj ) of isotropic RE 2 Fe 14 B magnets, while the H cj could still remain more than 1114.08 kA/m when the mass proportion of MM (simplified as: “a”) is 30%. Curie temperature and phase structure were also researched. Two kinds of mixed-solid-solution (MSS) main phases with different Lanthanum (La) and Cerium (Ce) content were believed to be responsible for the two curie temperature of the RE 2 Fe 14 B magnets with “a” ≥20%. This is resulted from the inhomogeneous elemental distribution of RE 2 Fe 14 B phase. [ABSTRACT FROM AUTHOR]