Influence of squeeze casting pressure and heat treatment on microstructure and mechanical properties of Mg94Ni2Y4 alloy with LPSO structure.

Ternary Mg 94 Ni 2 Y 4 (at%) alloy was prepared by conventional gravity casting or direct squeezing casting and then subjected to T6 heat treatment. The influence of squeeze casting pressure and heat treatment on microstructure evolution and mechanical properties of Mg 94 Ni 2 Y 4 alloy containing long period stacking ordered (LPSO) structure was studied. The results show that gravity cast Mg 94 Ni 2 Y 4 alloy consisted of primary α-Mg, 18 R LPSO and eutectic structure containing α-Mg, LPSO and Mg 2 Ni phases. The application of pressure cannot change phase constituents and the type of LPSO phase. With the increase of squeeze casting pressure, microstructure was refined, the volume fraction of LPSO was decreased while that of eutectic structure was increased. Under the highest pressure of 320 MPa, kinking of LPSO phase was induced and the best mechanical properties were obtained, with the ultimate tensile strength of 250 MPa, the yield strength of 140 MPa and the elongation of 8%. They were improved by 20.2%, 22.8% and 45.5%, respectively, than those of gravity cast Mg 94 Ni 2 Y 4 . After heat treatment, bulk-shaped LPSO phase transformed into rod-shaped one, but no lamellar 14 H LPSO was precipitated in the matrix. Besides, the application of squeeze casting pressure prevented LPSO from delaminating during heat treatment. [ABSTRACT FROM AUTHOR]