1,2,3-Triazole mediated Li+-ion conductivity in poly(ethylene oxide) based electrolytes.

Poly(ethylene oxide) (PEO) based electrolytes are of great importance for applications in electrochemical devices. Since their ion conductivity is severely hampered by crystallization, several approaches are carried out to enhance the low temperature ion conductivity of PEO such as the addition of polar solvents or the synthesis of more complex polymer architectures. In this study, solvent-like defects are introduced in the center of the PEO chain to reduce its crystallinity with the aim to enhance ion conductivity. The ion conductivities of four polymer electrolytes, containing either a 1,4-disubstituted 1,2,3-triazole (TR) or ortho- , meta- or para- disubstituted benzene defects are measured by impedance spectroscopy after addition of lithium perchlorate (LiClO 4 , EO:Li = 50:1) to the polymer. The TR containing sample shows a 15 to 700 times higher ion conductivity at T = − 10 °C as compared to the benzene containing PEOs with different substitution pattern. This can be explained by the lower glass transition temperature of the TR containing electrolytes compared to the benzene containing electrolytes. Furthermore, the dependence of the ion conductivity on the LiClO 4 concentration in the melt at T = 70 °C is studied for TR containing electrolytes and compared to the respective defect free PEO 22 electrolytes. The electrolytes with the TR defect have higher conductivities in the concentration range (50:1 ≥ EO:Li ≥ 8:1) compared to the uninterrupted PEO 22 revealing that the incorporation of a solvent-like defect with high dielectric constant into a PEO chain is an effective strategy to enhance the ion conductivity of PEO electrolytes. This is also supported by 7 Li NMR spectroscopy showing that LiClO 4 is soluble 1,2,3-triazole but insoluble in benzene. Additionally, 1,2,3-triazoles can also coordinate Li + -ions and, thus, actively contribute to the transport of the Li + -ions. [ABSTRACT FROM AUTHOR]