Laboratory study on cement admixed marine silt bricks.

For the purpose of efficient utilization of sediments dredged from harbor, a new method was proposed in this study. Marine silt bricks were made by mixing sediments with cement and gypsum, placing it in a cubic mold with 240 mm in length, 115 mm in width, and 53 mm in height, and curing for certain days. To investigate the effects of cement and initial water content of soil on the mechanical behavior of marine silt bricks, unconfined compressive and flexural strength tests were carried out. Given the same curing time and cement content, the higher the initial water content, the lower the compressive and flexural strength. After 60 days of curing, the compressive strength of marine silt bricks with cement content = 20% and water content = LL (liquid limit) reached approximately 5 MPa. The flexural strength was relatively low. The flexural strength of marine silt bricks with 20% cement and water content = LL was around 1.5 MPa. The compressive and flexural strength decreased with the increase of water/cement ratio. As for the curing time, longer curing time had a positive impact on the compressive strength. The ratio of flexural to compressive strength varied slightly in the range of 0.4–0.5. [ABSTRACT FROM AUTHOR]