- Source :
-
Mechanics of Materials . Sep2016, Vol. 100, p198-208. 11p. - Publication Year :
- 2016
-
Abstract
- Axially loaded push-pull tests of a low strength Cr−Ni−Mo−V steel welds using cross-weld specimens with different sizes were conducted up to the very high cycle fatigue regime under ultrasonic frequency. Results showed that smaller samples had higher fatigue strength with interior cracking predominant at the weld metal. Fine granular area characteristic of polycrystalline features close to micro-defects was indicative of higher fatigue strength with implications of cyclic hardening, and was related to localization of plastic deformation. A physical criterion for formation of fine granular area was proposed as the ratio of accumulation to release rates of cyclic plastic energy was higher than one. It was found that the size effect on fatigue strength of the low strength welds was coupled with frequency effect, an issue that both current deterministic and probabilistic approaches were unable to rationalize, was actually dependent on tensile strength as well as extrinsic factors such as cyclic hardening and micro-defect distribution. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 01676636
- Volume :
- 100
- Database :
- Academic Search Index
- Journal :
- Mechanics of Materials
- Publication Type :
- Academic Journal
- Accession number :
- 117095833
- Full Text :
- https://doi.org/10.1016/j.mechmat.2016.06.017