Dielectric relaxation and ferroelectric phase transition in Sr4BiRTi4Nb6O30 (R = Sm, Eu) ceramics.

Sr 4 BiRTi 4 Nb 6 O 30 (R = Sm, Eu) ceramics with tetragonal tungsten bronze structure were prepared by the conventional solid state reaction method. The crystalline structure, microstructure, dielectric and ferroelectric properties of the ceramics were investigated. Structural analysis using the powder x-ray diffraction patterns revealed the formation of tetragonal tungsten bronze structure in space group P 4 bm . Columnar grains with a homogeneous distribution were formed in Sr 4 BiEuTi 4 Nb 6 O 30 ceramics, while in Sr 4 BiSmTi 4 Nb 6 O 30 ceramics the microstructure became inhomogeneous and some abnormal grains were also formed. The dielectric properties of the ceramics exhibited relaxor type phase transition which can be attributed to the random distribution of Bi and Sm/Eu ions at A1-sites and Ti and Nb ions at the B-sites of the TTB structure. The peak temperature shifted towards the higher temperatures and the magnitude of the dielectric constant decreased with increasing frequency. Moreover, the temperature of the dielectric maximum T m increased as the radius of the R ion getting decreased. From the P-E hysteresis loops, remnant polarization of 0.83 μC/cm 2 and 0.6 μC/cm 2 were obtained for Sr 4 BiEuTi 4 Nb 6 O 30 and Sr 4 BiSmTi 4 Nb 6 O 30 , respectively. [ABSTRACT FROM AUTHOR]