Solidification microstructures of the undercooled Co-24 at%Sn eutectic alloy containing 0.5 at%Mn.

Solidification samples of undercooled Co-24 at%Sn eutectic alloy containing a small amount of Mn (<1.0 at%) were prepared by the glass fluxing technique. The surface and internal solidification microstructures of the samples were observed by a scanning electron microscope (SEM) and an optical microscope (OM), respectively. The experiment results revealed that the addition of 0.5 at%Mn remarkably changed the solidification behaviors of the undercooled Co-24 at%Sn eutectic alloy. The addition of 0.5 at%Mn influenced the morphological selection of eutectic growth interface by increasing the interface energy anisotropy during the solidification of the undercooled Co-24 at%Sn eutectic melt. As undercooling increases, the coupled eutectic growth interface morphology successively experienced dendritic pattern, factual seaweed pattern and compact seaweed pattern. Besides, the addition of 0.5 at%Mn decreased the critical undercooling for the formation of anomalous eutectic by introducing a new formation mechanism of anomalous eutectic, i.e. divorce eutectic mechanism. [ABSTRACT FROM AUTHOR]