High-pressure synthesis, crystal structure, and magnetic properties of KSbO3-type 5d oxides K0.84OsO3 and Bi2.93Os3O11.
- Source :
-
Science & Technology of Advanced Materials . Dec2014, Vol. 15 Issue 6, p1-N.PAG. 1p. - Publication Year :
- 2014
-
Abstract
- 5d Solid-state oxides K0.84OsO3 (Os5.16+; 5d2.84) and Bi2.93Os3O11 (Os4.40+; 5d3.60) were synthesized under high-pressure and high-temperature conditions (6 GPa and 1500–1700 °C). Their crystal structures were determined by synchrotron x-ray diffraction and their 5d electronic properties and tunnel-like structure motifs were investigated. A KSbO3-type structure with a space group of Im-3 and Pn-3 was determined for K0.84OsO3 and Bi2.93Os3O11, respectively. The magnetic and electronic transport properties of the polycrystalline compounds were compared with those obtained theoretically. It was revealed that the 5d tunnel-like structures are paramagnetic with metallic charge conduction at temperatures above 2 K. This was similar to what was observed for structurally relevant 5d oxides, including Bi3Re3O11 (Re4.33+; 5d2.66) and Ba2Ir3O9 (Ir4.66+; 5d4.33). The absence of long-range magnetic order seems to be common among 5d KSbO3-like oxides, regardless of the number of 5d electrons (between 2.6 and 4.3 per 5d atom). [ABSTRACT FROM AUTHOR]
- Subjects :
- *CRYSTAL structure
*CRYSTALLOGRAPHY
*MAGNETIC properties
*BUYS-Ballot's laws
*OXIDES
Subjects
Details
- Language :
- English
- ISSN :
- 14686996
- Volume :
- 15
- Issue :
- 6
- Database :
- Academic Search Index
- Journal :
- Science & Technology of Advanced Materials
- Publication Type :
- Academic Journal
- Accession number :
- 100249473
- Full Text :
- https://doi.org/10.1088/1468-6996/15/6/064901