Crack-healing ability and strength recovery of different hot-pressed TZ3Y20A–SiC ceramics by heat treatment in air.

Authors :
Zhang, Xiu-Ping
Ouyang, Jia-Hu
Liu, Zhan-Guo
Wang, Yu-Jin
Wang, Ya-Ming
Zhou, Yu
Source :
Materials & Design. Feb2015, Vol. 67, p324-329. 6p.
Publication Year :
2015

Abstract

Crack-healing ability and strength recovery of different ZrO 2 (Y 2 O 3 )–Al 2 O 3 –SiC (TZ3Y20A–SiC) ceramics have been investigated by tailoring heat treatment temperature, heat treatment time, SiC content and crack size. Heat treatment in air enhances distinctly the flexural strength of TZ3Y20A–SiC ceramics. A complete crack-healing of TZ3Y20A–10 vol%SiC ceramic can be realized by optional heat treatments at 1073 K for 30 h, 1273 K for 10 h or 1373 K for 5 h, respectively. With increasing the content of nanosize SiC particles from 10 to 20 vol%, the crack-healing process of TZ3Y20A–SiC ceramics speeds up at identical temperature levels. The pre-existing cracks with a width up to 0.45 μm are healed completely under the optimum heat treatment conditions, and the flexural strengths of crack-healed TZ3Y20A–SiC ceramics are completely recovered to the value of smooth specimens. Crack closure and rebonding of crack wall due to the formation of SiO 2 glassy phase by oxidation reaction between SiC and the oxidizing atmosphere are dominant healing mechanisms in TZ3Y20A–SiC ceramics. [ABSTRACT FROM AUTHOR]

Details

Language :
English
ISSN :
02641275
Volume :
67
Database :
Academic Search Index
Journal :
Materials & Design
Publication Type :
Academic Journal
Accession number :
100191205
Full Text :
https://doi.org/10.1016/j.matdes.2014.11.053