Search

This research observes changes in the properties of commercially available hemp office papers exposed to photo-oxidation for artificial aging. In order to accelerate the changes that naturally occur in paper, photo-oxidation was performed using a Xenon light source. The electromagnetic radiation was administered in doses of 550?W/m2 over 24 hours with a temperature of 60°C. Three types of hemp office papers that differ in chemical composition and manufacturing process were used as samples. The strength properties (tensile index, elongation at break, tear index), surface properties (Bendtsen roughness, Bekk smoothness), pH of paper extracts, and optical properties were observed. The listed properties of artificially aged samples were compared to those of unaged commercial paper samples. The results show that, after only 24 hours, accelerated aging with a Xenon arc lamp affects all observed paper properties. For all analyzed office papers, the values of the tensile index, Bekk smoothness, and pH of paper extracts decreased, while the values of elongation break, tear index, and Bendtsen roughness increased due accelerated aging. Regarding the CIE L*a*b* color space value, lightness (L*) generally decreased after the aging treatment, and all paper samples became less reddish (a* decreased) and more yellow (b* increased). The obtained results of this research reveal that pulp with hemp fibers can produce higher-quality office paper that is more stable against light and temperature influences than those made with post-consumer fibers. However, to increase the durability of manufactured paper, hemp fibers must be bleached.

This research observes changes in the properties of commercially available hemp office papers exposed to photo-oxidation for artificial aging. In order to accelerate the changes that naturally occur in paper, photo-oxidation was performed using a Xenon light source. The electromagnetic radiation was administered in doses of 550 W/m2 over 24 hours with a temperature of 60°C. Three types of hemp office papers that differ in chemical composition and manufacturing process were used as samples. The strength properties (tensile index, elongation at break, tear index), surface properties (Bendtsen roughness, Bekk smoothness), pH of paper extracts, and optical properties were observed. The listed properties of artificially aged samples were compared to those of unaged commercial paper samples. The results show that, after only 24 hours, accelerated aging with a Xenon arc lamp affects all observed paper properties. For all analyzed office papers, the values of the tensile index, Bekk smoothness, and pH of paper extracts decreased, while the values of elongation break, tear index, and Bendtsen roughness increased due accelerated aging. Regarding the CIE L*a*b* color space value, lightness (L*) generally decreased after the aging treatment, and all paper samples became less reddish (a* decreased) and more yellow (b* increased). The obtained results of this research reveal that pulp with hemp fibers can produce higher-quality office paper that is more stable against light and temperature influences than those made with post-consumer fibers. However, to increase the durability of manufactured paper, hemp fibers must be bleached. [ABSTRACT FROM AUTHOR]

Objective: To determine whether heat generated by endoscope light sources during ear surgery is safe.Methods: Transcanal endoscopic ear surgery (TEES) was simulated using 2.7-mm or 4-mm endoscopes coupled to xenon or LED light sources and a 3D model of human temporal bone. The endoscope tip was fixed at the center of tympanic annulus. Light sources were tested at clinical (30% for xenon and 40% for LED) and 100% settings. Temperatures were measured using thermocouples attached to the endoscope tip and three points within the middle ear cavity: promontory, horizontal portion of the facial nerve and lateral semicircular canal.Results: Maximum temperatures measured within the middle ear cavity were below 31°C at clinical settings, while the temperatures rose to 44.1°C using a 4-mm endoscope with a xenon light source set at 100%. Temperatures measured at the tip were all safe at clinical settings, but rose dramatically to 110.1°C for the 4-mm endoscope with xenon at 100%.Conclusion: Endoscopes can be safely used within the middle ear at clinical settings. However, operators should not exceed clinical settings, particularly with 4-mm endoscopes with a xenon light source, to ensure temperatures generated within the middle ear cavity are safe. [ABSTRACT FROM AUTHOR]