Search

The synthesis of core–shell magnetic mesoporous nanoparticles (MMSNs) through a phase transfer process is usually performed at the 100–250 mg scale. At the gram scale, nanoparticles without cores or with multicore systems are observed. Iron oxide core nanoparticles (IO) were synthesized through a thermal decomposition procedure of α-FeO(OH) in oleic acid. A phase transfer from chloroform to water was then performed in order to wrap the IO nanoparticles with a mesoporous silica shell through the sol–gel procedure. MMSNs were then functionalized with DTPA (diethylenetriaminepentacetic acid) and used for the separation of metal ions. Their toxicity was evaluated. The phase transfer procedure was crucial to obtaining MMSNs on a large scale. Three synthesis parameters were rigorously controlled: temperature, time and glassware. The homogeneous dispersion of MMSNs on the gram scale was successfully obtained. After functionalization with DTPA, the MMSN-DTPAs were shown to have a strong affinity for Ni ions. Furthermore, toxicity was evaluated in cells, zebrafish and seahorse cell metabolic assays, and the nanoparticles were found to be nontoxic. We developed a method of preparing MMSNs at the gram scale. After functionalization with DTPA, the nanoparticles were efficient in metal ion removal and separation; furthermore, no toxicity was noticed up to 125 µg mL−1 in zebrafish. [ABSTRACT FROM AUTHOR]

The synthesis of core–shell magnetic mesoporous nanoparticles (MMSNs) through a phase transfer process is usually performed at the 100–250 mg scale. At the gram scale, nanoparticles without cores or with multicore systems are observed. Iron oxide core nanoparticles (IO) were synthesized through a thermal decomposition procedure of α-FeO(OH) in oleic acid. A phase transfer from chloroform to water was then performed in order to wrap the IO nanoparticles with a mesoporous silica shell through the sol–gel procedure. MMSNs were then functionalized with DTPA (diethylenetriaminepentacetic acid) and used for the separation of metal ions. Their toxicity was evaluated. The phase transfer procedure was crucial to obtaining MMSNs on a large scale. Three synthesis parameters were rigorously controlled: temperature, time and glassware. The homogeneous dispersion of MMSNs on the gram scale was successfully obtained. After functionalization with DTPA, the MMSN-DTPAs were shown to have a strong affinity for Ni ions. Furthermore, toxicity was evaluated in cells, zebrafish and seahorse cell metabolic assays, and the nanoparticles were found to be nontoxic. We developed a method of preparing MMSNs at the gram scale. After functionalization with DTPA, the nanoparticles were efficient in metal ion removal and separation; furthermore, no toxicity was noticed up to 125 µg mL−1 in zebrafish.

We demonstrate the synthesis of copper nanocolloids by the thermal decomposition of copper formate in oleylamine under ambient conditions. By progressively increasing the loading of copper formate in the reaction mixture and imposing sufficiently high conversion rates, we demonstrate the formation of nanocrystals that are more than 97% pure copper without using an inert atmosphere. We attribute this result to the excess of copper formate relative to initially dissolved oxygen, and to the suppression of oxygen influx in the reactor. By adjusting the precursor and ligand concentrations, we obtain copper nanocrystals with sizes ranging from 10 to 200 nm. In view of applications, we show that the reaction can be upscaled to a 1 L reaction volume to produce over 50 g of copper nanocrystals. Moreover, we formulate a conductive ink based on the copper nanocolloids obtained here with which we printed copper films exhibiting a resistivity of 23 μΩ cm after thermal sintering under N2. We conclude that the approach presented here constitutes a next step toward the cost-effective production of metallic copper nanocrystals for printed electronics. [ABSTRACT FROM AUTHOR]