Search

The improvement of gel strength and absorption properties through the surface-crosslinking of superabsorbent polymers (SAPs) is essential for sanitary industry applications. We prepared core-SAP via aqueous solution copolymerization, and then surface-crosslinked the core-SAP under various conditions. The structure of the SAP was characterized using Fourier transform infrared (FT-IR) spectroscopy. Central composite design (CCD) of response surface methodology (RSM) has been applied to determine the optimum surface-crosslinking conditions such as surface-crosslinker content, reaction temperature, and reaction time. The optimal surface-crosslinking conditions were identified at a surface-crosslinker content of 2.22 mol%, reaction temperature of 160 °C, and reaction time of 8.7 min. The surface-crosslinked SAP showed excellent absorbency under load of 50 g/g with a permeability of 50 s. Other absorption properties were also evaluated by measuring the free absorbency and centrifuge retention capacity in saline solution. [ABSTRACT FROM AUTHOR]

Most superabsorbent polymers (SAPs) are prepared based on synthetic polymers (from petroleum resources), making them costly, nondegradable, and not ecofriendly. To overcome these drawbacks, biodegradable and renewable natural materials are proposed as additions into SAPs. In this article, a new SAP composite was synthesized by using AA, AM, α-cellulose, and modified zeolite (MZE). The prepared SAP composites were analysed by FTIR spectroscopy, XRD, SEM and TGA. Then, their water absorbency and water retention capacity results were evaluated. AA and AM were successfully grafted to the α-cellulose chains, and MZE was uniformly dispersed in the SAP composite matrix as an inorganic filler, which endowed the SAP composites with a more undulant and coarser surface along with more abundant hydrophilic groups. In contrast with poly(AA-co-AM), the water absorbency of the prepared SAP composites increased by 93.88% in distilled water and 89.58% in 0.9 wt.% NaCl solution. Additionally, the water retention time of these SAP composites was 11.2 h when evaluated at 50 °C, which was a 71.79% increase. Moreover, both the Tonset and Tpeak of the prepared SAP composites slightly increased compared with those of α-cellulose-poly(AA-co-AM), showing that the introduction of MZE could slightly improve the thermal stability of the SAP composites. These novel SAP composites with their excellent water absorbency and retention capacity could be applied to the agricultural and horticultural fields as water-keeping materials. [ABSTRACT FROM AUTHOR]

The improvement of gel strength and absorption properties through the surface-crosslinking of superabsorbent polymers (SAPs) is essential for sanitary industry applications. We prepared core-SAP via aqueous solution copolymerization, and then surface-crosslinked the core-SAP under various conditions. The structure of the SAP was characterized using Fourier transform infrared (FT-IR) spectroscopy. Central composite design (CCD) of response surface methodology (RSM) has been applied to determine the optimum surface-crosslinking conditions such as surface-crosslinker content, reaction temperature, and reaction time. The optimal surface-crosslinking conditions were identified at a surface-crosslinker content of 2.22 mol%, reaction temperature of 160 °C, and reaction time of 8.7 min. The surface-crosslinked SAP showed excellent absorbency under load of 50 g/g with a permeability of 50 s. Other absorption properties were also evaluated by measuring the free absorbency and centrifuge retention capacity in saline solution.

Herein, core-superabsorbent polymer (CSAP) composites are prepared from oxidized starch (OS) via aqueous solution copolymerization using ammonium persulfate as the initiator, and 1,6-hexanediol diacrylate as the inner-crosslinker. The surface-crosslinking process is performed using various surface-crosslinkers, including bisphenol A diglycidyl ether (BADGE), poly(ethylene glycol) diglycidyl ether (PEGDGE), ethylene glycol diglycidyl ether (EGDGE), and diglycidyl ether (DGE). The structures of the CSAP composites and their surface-crosslinked SAPs (SSAPs) are characterized using Fourier transform infrared (FT-IR) spectroscopy, their absorption properties are measured via centrifuge retention capacity (CRC), absorbency under load (AUL), permeability, and re-swellability tests, and their gel strengths according to surface-crosslinker type and EGDGE content are examined via rheological analysis. The results indicate that an EGDGE content of 0.75 mol provides the optimum surface-crosslinking and SSAP performance, with a CRC of 34.8 g/g, an AUL of 27.2 g/g, and a permeability of 43 s. The surface-crosslinking of the CSAP composites using OS is shown to improve the gel strength, thus enabling the SAP to be used in disposable diapers.

Herein, core-superabsorbent polymer (CSAP) composites are prepared from oxidized starch (OS) via aqueous solution copolymerization using ammonium persulfate as the initiator, and 1,6-hexanediol diacrylate as the inner-crosslinker. The surface-crosslinking process is performed using various surface-crosslinkers, including bisphenol A diglycidyl ether (BADGE), poly(ethylene glycol) diglycidyl ether (PEGDGE), ethylene glycol diglycidyl ether (EGDGE), and diglycidyl ether (DGE). The structures of the CSAP composites and their surface-crosslinked SAPs (SSAPs) are characterized using Fourier transform infrared (FT-IR) spectroscopy, their absorption properties are measured via centrifuge retention capacity (CRC), absorbency under load (AUL), permeability, and re-swellability tests, and their gel strengths according to surface-crosslinker type and EGDGE content are examined via rheological analysis. The results indicate that an EGDGE content of 0.75 mol provides the optimum surface-crosslinking and SSAP performance, with a CRC of 34.8 g/g, an AUL of 27.2 g/g, and a permeability of 43 s. The surface-crosslinking of the CSAP composites using OS is shown to improve the gel strength, thus enabling the SAP to be used in disposable diapers. [ABSTRACT FROM AUTHOR]