Search

International audience; Scaling process is the main problem encountered in industrial plants using water. Several factors, (pH, temperature, hydrodynamic conditions, metal surface, and especially, water composition),can affect the scaling kinetics of calcium carbonate (CaCO3), one of the main component of scaling. In addition, some foreign ions added can considerably modified the scaling rates. In thiswork, the inhibiting effects of Zn2+ and Cu2+ cations on CaCO3 precipitation were studied in a 50°F synthetic carbonic solution by using fast controlled precipitation (FCP) and scaling quartz crystal microbalance (SQCM) methods, for homogeneous and heterogeneous scaling deposition, respectively. Results showed that Zn2+ and Cu2+ ions are efficient, at high concentrations (≥ 1mg/L), to delay or even to prevent nucleation/growth of CaCO3. FCP measurements showed a complete inhibition of the homogeneous CaCO3 precipitation after 120 min in synthetic solutioncontaining 5 mg/L and 4 mg/L of Cu2+ and Zn2+, respectively. SQCM measurements showed that the surface coverage of the metallic substrate by a layer of CaCO3 is reduced when the amount of these cations increased. Zn2+ cations inhibited the heterogeneous CaCO3 precipitation moree fficiently than Cu2+. SEM and XRD results indicated that both cations affect calcium carbonatenucleation by changing the morphology of CaCO3 crystals

Scaling phenomenon, mainly related to the precipitation of calcium carbonate(CaCO3), is widely encountered in industry using water. It is necessary to find solutions inorder to control scale deposition.This thesis describes the influence of two metallic cations, copper (II) and zinc (II),on the CaCO3 precipitation. The first part focuses on the inhibitory effect of these ions onscaling in synthetic waters of 25 and 50 °F. Investigations are conducted using FastControlled Precipitation method (FCP) and Scaling Quartz Crystal Microbalance (SQCM).These measurements make it possible to follow the nucleation and growth processes ofcalcium carbonate in solution and on the pre-calcareous metallic surface. The results showthat Zn2+ and Cu2+ ions play an important role in the kinetics of CaCO3 formation. They actas retarders of the scaling phenomenon.The second part is devoted to the study of the scaling phenomenon on a steel surfacepretreated with an organic-inorganic hybrid film (polysiloxane-based films) already testedagainst corrosion, developed in an original way using the sol–gel process. The QCM andchronoamperometric (CA) methods allowed the monitoring of calcium carbonateprecipitation kinetics on the surface covered by the synthesized polymers doped with copperand zinc cations. The idea is to act directly on the metallic surface in contact with the waterwithout modifying the composition and the nature of the water in question. The obtainedresults show that the doping of the metal cations improves the anti-scaling effect of the film.; Le phénomène d’entartrage, principalement lié à la précipitation du carbonate decalcium (CaCO3) est très largement rencontré dans les industries et les circuits utilisant del’eau. Sa présence entraîne des problèmes à la fois techniques et économiques. La préventionet la mise en place de moyens de lutte contre l’entartrage constituent une préoccupationmajeure des chercheurs qui s’intéressent à ce phénomène.Ce travail de thèse décrit l’influence des cations métalliques cuivre (II) et zinc (II)sur la précipitation de CaCO3. La première partie met l’accent sur l’effet inhibiteur de cesions vis-à-vis de l’entartrage, dans des eaux synthétiques de 25 et 50°F. Les investigationssont menées en utilisant la méthode de précipitation contrôlée rapide (PCR) et lamicrobalance à cristal de quartz avec une surface pré-entartrée (SQCM). Ces mesurespermettent de suivre le processus de germination et de croissance du carbonate de calciumen solution et sur la surface métallique pré-entartrée. Les résultats montrent que les ions Zn2+et Cu2+ jouent un rôle important sur la cinétique de la formation de CaCO3. Ils agissentcomme des retardateurs du phénomène d’entartrage.La deuxième partie est dédiée à l’étude du phénomène d’entartrage sur une surfaceen acier prétraitée par un film hybride organique-inorganique (films à bases depolysiloxanes) déjà testé contre la corrosion, élaboré par le procédé sol–gel. Les méthodesQCM et la chronoampérométrie (CA) ont permis le suivi de la cinétique de précipitation ducarbonate de calcium sur la surface recouverte par les polymères synthétisés dopés auxcations cuivre et zinc. L’idée est d’agir directement sur la surface métallique en contact del’eau sans modifier la composition et la nature de l’eau en question. Les résultats obtenusont montré que le dopage des cations métalliques améliore l’effet antitartre du film.