Copyright of Railway Standard Design is the property of Railway Standard Design Editorial Office and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Weathering steel is used more and more widely in various fields of production and life.A rust layer stabilization treatment on the surface of weathering steel before usage can enhance both material life extension and beautification，promoting the mutual coordination between weathering steel and its service environment.In this paper，the research status of surface stabilization treatment technique of rust layer on weathering steel was summarized，which mainly included the formation，composition，structure and protection mechanism of rust layer，especially the disadvantages of traditional technology and novel technology.Finally，the further development of the surface rust layer stabilization treatment was prospected.

The water treatment experiment for rust layer stabilization for Q500qENH weathering steel was carried out in seven different locations for 8 weeks to determine the applicability of the optimal treatment process. Results showed that with the prolonging of the stabilization treatment period, the weight loss and corrosion thinning of the samples increased, the corrosion rate presented a downward trend, and the color of the rust layer on the surface of the samples changed from orange to brown. In addition, the thickness of the rust layer increased gradually. The electrochemical analysis results indicated that the self - corrosion current density of the samples decreased, and the self - corrosion potential gradually shifted positively with the prolonging of the stabilization treatment period. Meanwhile, the results of XRD analysis revealed that the unstable phase (γ - FeOOH) gradually transformed into stable phase (α - FeOOH), and the proportion of stable phase (α - FeOOH) gradually increased with the extension of stabilization treatment period. To sum up the above results, Q500qENH weathering steel was treated by different rust layer stabilization water treatment processes in 3 kinds of typical locations, and a relatively stable rust layer could be obtained after 4～6 weeks.