This study aimed to compare polishing systems on color stability, surface roughness, and gloss of additively manufactured permanent and conventional resin composites. Totally 250 disc specimens (6 mm*2 mm) were prepared from resin-based materials [G-ænial Posterior (GP), Clearfil Majesty Esthetic (CME), SonicFill-2 (SF), Tescera (Tes), and Crowntec (CT)]. Following baseline color (ΔE00), gloss (GU), and surface roughness (Ra) measurements, the specimens were randomly divided into 5 groups (n = 10/group) according to polishing systems: Control (mylar strips); OneGloss; OneGloss + Platina Hi-Gloss; OptiDisc; and OptiDisc + Platina Hi-Gloss. Specimens were immersed in coffee for 144 h following polishing. ΔE00, GU, and Ra measurements were repeated. Atomic force microscopy images were taken in all groups. Spearman's rho correlation coefficient, Robust ANOVA, and Bonferroni correction were used for statistical analysis. Significance level was taken as p < 0.050. Significant differences in ΔE00 values were found among resin-based materials, polishing systems, and their interactions (p < 0.001,p < 0.01, and p = 0.001). Regardless of polishing system, the lowest ΔE00 values were observed in CT, while lowest gloss (GU) values were found in Tes. The lowest surface roughness (Ra) values were detected at OptiDisc group (p < 0.001). A single type of polishing system may not be sufficient to achieve optimal results in resin-based materials. [ABSTRACT FROM AUTHOR]

ABSTRACT Objective Materials and Methods Results Conclusions Clinical Significance To map the evidence regarding the clinical performance of posterior restorations with bulk‐fill resin composites and identify research gaps.This mapping review was conducted following PRISMA‐ScR guidelines for scoping reviews, and its protocol was registered on the Open Science Framework platform. Systematic searches were conducted, considering studies published between 2013 and February 2024 in the PubMed, Embase, and Cochrane databases. Clinical studies investigating the performance of bulk‐fill resin composite restorations in class I and/or class II preparations with increments of 4 to 5 mm were included.A total of 147 articles were identified, and based on the eligibility criteria, 26 studies were selected for descriptive analysis. Of the reviewed studies, 73% (n = 19) investigated high‐viscosity bulk‐fill composites, while 30% (n = 8) focused on low‐viscosity bulk‐fill composites. Evaluation periods ranged from 1 week to 10 years. Reported annual failure rates varied from 0% to 3%, with survival rates between 78.9% and 100%.Bulk‐fill resin composites of high viscosity were the most analyzed in the published studies, with evaluation periods of up to 10 years. The review of available scientific evidence showed clinically acceptable performance for composite bulk‐fill restorations, with high survival rates and minimal annual failure rates. There is a need for long‐term clinical studies on bulk‐fill resin composites.This review demonstrates that both high and low‐viscosity bulk‐fill resin composites exhibit satisfactory clinical performance, which can help clinicians optimize chairside time. However, it is important to highlight the need for further studies with longer follow‐up periods. [ABSTRACT FROM AUTHOR]

This study aimed to investigate the effects of crown seating speed, crown seating force, quantity of cement used, and type of implant cement on the amount of remnant cement in the subgingival region (RCS) after cementation. Cement-retained implant crowns were cemented to titanium abutments using the following methods: four types of implant cement (TBN: TEMP BOND NE, NR: NEXUS RMGI, ME: MAXCEM ELITE, and U200: RELYX U200), three quantities of cement (0.02 ml, 0.04 ml, and 0.06 ml), three crown seating speeds (5 mm/s, 10 mm/s, and 15 mm/s), and two crown seating forces (25 N, 50 N). The surface area and length of the RCS were measured using a 3D intraoral scanner. The total RCS weight was measured using an analytical balance. The RCS increased significantly as the seating speed increased, the seating force increased, and the quantity of cement increased (p < 0.05). The RCS values were the highest for TBN, followed by U200, NR, and ME (p < 0.05). The lower seating speed, smaller quantity of cement used, and smaller seating force applied in cement-retained implant restorations minimized the RCS in cement-retained prostheses. The type of cement is a factor that determines the aspects of the RCS. [ABSTRACT FROM AUTHOR]

The purpose was to compare the effects of rapid (3 s) and conventional (20 s) polymerization protocols (PP) of mono- and multichip LED curing units (LCU) on shrinkage stress (SS) and monomer elution (ME) in bulk-fill resin-based composites (RBC) with and without addition-fragmentation chain-transfer (AFCT) monomer. Cylindrical (5x4mm) specimens were prepared from two RBCs containing different AFCT monomers (Filtek OneBulk-FOB; Tetric PowerFill-TPF) and one without (Tetric EvoCeram Bulk-TEC). After soaking for 3, 10, and 14 days (75 % ethanol), ME was quantified using standard monomers by High-Performance Liquid Chromatography. SS was measured from the start of polymerization to 5 min using a Materials Testing Machine. The radiant exitance of LCUs was measured using a spectrophotometer. ANOVA and Tukey's post-hoc test, multivariate analysis and partial eta-squared statistics were used to analyze the data (p < 0.05). AFCT-modification significantly decreased ME (p < 0.001). ME was reduced by half by day 10 and by one tenth by the end of the 14-day compared to the 3-day sampling. ME itself was dependent, whereas the percentage of monomers released was independent of the PP used (p > 0.05). FOB showed the lowest SS (p < 0.001), while there was no significant difference between TPF and TEC (p = 0.124). Both ME and SS were significantly influenced by material type and PP. The incorporation of the AFCT monomer reduced ME, but this was inversely related to a decrease in exposure time. SS values reduced by rapid PP in parallel with increasing ME values. The utilization of the AFCT molecule in conjunction with an appropriate resin-, initiator-system is of significant consequence for the kinetics of polymerization and the incorporation of monomers into the network. [ABSTRACT FROM AUTHOR]

The biodegradation of methacrylate (MA)-based dental restoratives has been suggested to contribute to a loss of adhesion and subsequent detachment, or secondary caries, both major causes of restoration failure. Previous studies have demonstrated that intermolecular interactions between resin monomers may affect the hydrolytic-susceptibility of composites. Altering the intermolecular interactions by shielding or masking the hydrolytically-susceptible ester groups found in MA monomers could be an effective strategy to mitigate the biodegradation of resin composites. The objective of this work was to assess whether shielding/masking MAs using fluorinated groups could improve the biostability of experimental composites. Eight fluorinated monomers (FM) were synthesized, characterized (1H NMR), and formulated into experimental resin composites (FC, 65 wt%, microfill). FCs were assessed for interactions with water (water contact angle, water sorption, gel fraction), mechanical properties (both compressive and flexural strength and modulus), cytocompatibility, resistance to biodegradation using simulated human salivary esterase (SHSE) and compared to a control composite (CC) without FM. Integration of FMs was found to generally decrease both the physical and mechanical properties under all incubation conditions when compared to the CC. Additionally, all FCs had a negative influence on composite biodegradation following immersion in SHSE when compared to the CC. Shielding/masking MA-esters inherently inserts molecular spaces between the polymer chains within the resin network, and shielding is likely not possible while also maintaining the necessary cohesive forces that regulate the physical and mechanical properties of resin composites. Novel dental resin development should seek to remove/replace vulnerable ester-containing MAs rather that adopting a shielding/masking approach. [ABSTRACT FROM AUTHOR]

This experimental study was performed to assess whether applying a metal primer containing 10-MDP multiple times affected the repair shear bonding ability of base metal alloys to resin composites. Ten base metal alloys were randomly assigned to each group in the manner described, following multiple applications of a metal primer (Clearfil Ceramic Primer Plus), namely one to five applications, and no primer application as a negative control. On the specimens' prepared surfaces, the resin composite was pushed into the mold and then light-activated for 40 s. The bonded samples were kept for 24 h at 37 °C in distilled water in an incubator. The shear bond strength was determined using a universal testing device. A stereomicroscope was used to determine the debonded surface. The one-way ANOVA and Tukey's test were implemented to statistically analyze. The lowest shear bond strength was found in group 6 (6.14 ± 1.12 MPa), demonstrating a significant difference (p = 0.000) when compared to groups 1 to 5. The shear bond strength of group 3 was highest at 21.49 ± 1.33 MPa; there was no significant difference between group 3 and groups 4 and 5 (20.21 ± 2.08 MPa and 20.98 ± 2.69 MPa, respectively) (p = 0.773, p = 1.000, respectively). All fractured specimens in groups 1, 2, and 6 were identified as adhesive failure. Groups 3 and 4 exhibited the highest percentage of mixed failures. To achieve the repair shear bonding ability of base metal alloys to resin composites, the sandblasted base metal alloys should be coated with three applications of a metal primer before applying the adhesive agent. [ABSTRACT FROM AUTHOR]

ABSTRACT Objective Material and Methods Results Conclusion Clinical Significance To evaluate the effect of different modeling agents on color changes, surface roughness, and translucency parameters over time in Bulkfill resin composites.Sixty specimens were prepared using three Bulkfill resin composites (Tetric N‐Ceram Bulkfill, Filtek One Bulkfill and Opus Bulkfill) and three modeling agents (Wetting Resin, Optibond FL and Ambar APS). All specimens were subjected to a simulated tooth‐brushing (Baseline, 50.000 cycles, 100.000 cycles), and surface roughness was measured at each interval. Surface topography was evaluated. The translucency parameter and color changes were assessed after 24‐h, 7‐, 14‐ and 30‐day immersion in water, wine, and coffee. Data was analyzed using ANOVA and Bonferroni test.All specimens increased roughness after simulated tooth‐brushing (p < 0.05). Wetting Resin decreased roughness on Tetric N‐Ceram Bulkfill (p < 0.05). The translucency parameter remained unaltered for all groups. All groups changed color after 30‐days of immersion in wine and coffee (p < 0.05). Ambar APS and Wetting Resin on Tetric N‐Ceram Bulkfill showed higher color changes when immersed in coffee (p < 0.05).The use of modeling agents does not jeopardize translucency properties but may affect surface roughness and color properties of Bulkfill resin composites depending on their composition.The findings of this study suggest that surface roughness and color properties are affected by the differences in the composition between modeling agents and Bulkfill resins composites. [ABSTRACT FROM AUTHOR]

The purpose of this study is to evaluate the influence of the matrix system on proximal contact tightness (PCT) of posterior composite resin restorations. Standardized class II cavities on 180 first lower molar dentiform model teeth (Frasaco GmbH, Tettnang, Germany) were prepared. Three groups were formed considering the matrix system: Group-IM: Ivory matrix (Hahnenkratt GmbH, Königsbach-Stein, Germany), Group-OM: Omni matrix (Ultradent, South Jordan, UT, USA), and Group-PM: Palodent V3 sectional matrix (Dentsply, Charlotte, NC, USA). Teeth were restored with resin composite mounted in a manikin head to simulate the clinical environment. Proximal contact tightness (PCT) was measured using a custom-made portable dental pressure meter (PDPM), and the validation of the PCT results was performed with a histogram analysis acquired from bite-wing radiography. All data were statistically analyzed by ANOVA and t-test in SPSS software (v.27.0) (p < 0.05). PM group showed statistically tighter contacts on both mesial (PCTm: 228.28 ± 59.17 N) and distal surfaces (PCTd: 254.91 ± 65.69 N) (p > 0.05). Mesial contacts were found to be significantly tighter than distal contacts among all (p < 0.05). According to the histogram results, only in the PM group, the difference between the mesial and distal areas is significant (p < 0.05). Histogram results confirmed that the tightest contact values were achieved in the PM group, followed by the OM and IM groups, respectively (p < 0.05). The use of sectional matrix systems and separation rings is more effective in creating tighter contact than conventional matrix systems. The use of anatomical wedges will help to create a more natural approximal contour and narrow contact area. [ABSTRACT FROM AUTHOR]

This study aimed to investigate the mechanical behavior of resin composites and hybrid glass ionomer cement in class I adhesive dental restorations under loading and shrinkage conditions. Three CAD models of a mandibular first molar with class I cavities were created and restored with different techniques: a bi-layer of Equia Forte HT with Filtek One Bulk Fill Restorative composite (model A), a single layer of adhesive and Filtek One Bulk Fill Restorative (model B), and a single layer of Equia forte HT (model C). Each model was exported to computer-aided engineering software, and 3D finite element models were created. Models A and B exhibited a similar pattern of stress distribution along the enamel–restoration interface, with stress peaks of 12.5 MPa and 14 MPa observed in the enamel tissue. The sound tooth, B, and C models showed a similar trend along the interface between dentine and restoration. A stress peak of about 0.5 MPa was detected in the enamel of both the sound tooth and B models. Model C showed a reduced stress peak of about 1.2 MPa. A significant stress reduction in 4 mm deep class I cavities in lower molars was observed in models where non-shrinking dental filling materials, like the hybrid glass ionomer cement used in model C, were applied. Stress reduction was also achieved in model A, which employed a bi-layer technique with a shrinking polymeric filling material (bulk resin composite). Model C's performance closely resembled that of a sound tooth. [ABSTRACT FROM AUTHOR]

Abstract This study aimed to investigate the effects of crown seating speed, crown seating force, quantity of cement used, and type of implant cement on the amount of remnant cement in the subgingival region (RCS) after cementation. Cement-retained implant crowns were cemented to titanium abutments using the following methods: four types of implant cement (TBN: TEMP BOND NE, NR: NEXUS RMGI, ME: MAXCEM ELITE, and U200: RELYX U200), three quantities of cement (0.02 ml, 0.04 ml, and 0.06 ml), three crown seating speeds (5 mm/s, 10 mm/s, and 15 mm/s), and two crown seating forces (25 N, 50 N). The surface area and length of the RCS were measured using a 3D intraoral scanner. The total RCS weight was measured using an analytical balance. The RCS increased significantly as the seating speed increased, the seating force increased, and the quantity of cement increased (p

Abstract Background Several calcium silicate-based sealers have recently emerged in endodontics. This study aimed to compare the immediate and delayed shear bond strength between the bioceramic and calcium hydroxide-based sealers and different resin-based restorative materials. Methods One hundred and twenty specimens with a 3-mm depth and a 3-mm diameter were prepared. They were evenly divided into two groups, the bioceramic sealer and calcium hydroxide-based sealer groups. Each primary group was subdivided into two subgroups based on the restorative material used; i.e., the flowable resin composite and resin-modified glass ionomer subgroups. Moreover, each subgroup was further divided into the restoration process’s timing: either immediately post-sealing or delayed after setting the sealers for seven days. The mode of failure was assessed by stereomicroscopic examination. Results The highest shear bond strength was found when the bioceramic sealer was used and restored with the flowable resin composite. The strengths were 8.45 (1.17) and 6.67 (1.60) megapascals (MPa) in the immediate and delayed restoration groups, respectively. In contrast, the lowest strength, 2.91 (1.22) MPa, was recorded when calcium hydroxide-based sealer was employed and restored after allowing the sealer to set completely with resin-modified glass ionomer. Notably, there were no cohesive fractures within the tested restorative materials. All observed fractures occurred within the sealer materials, at the interface of the sealer and restorative material, or in combination. Moreover, the most common failure was a mixed failure. Conclusions When flowable resin composite was used immediately before complete setting, bioceramic sealers showed a higher bond strength than calcium hydroxide-based sealers.

Abstract Backgrounds This study aimed to compare the effects of different energy drinks on the surface roughness, weight loss, and color change of various bioactive restorative materials. Methods Charisma Diamond One, Activa™ BioActive Restorative, Activa™ Presto™ and Equia Forte HT Fil samples were prepared using plastic molds (8 × 2 mm) (n = 10/groups). After polishing, the samples were weighed, their colors were recorded using a spectrophotometer according to the CIEDE2000 system, and their surface roughness was measured using a profilometer. The samples were immersed in Powerade, Burn, Monster and distilled water for 7 days. After immersion, all the measurements were repeated. Statistical analyses were performed using the Wilcoxon signed-rank test and the Mann‒Whitney U test (p

Introduction: Resin composites have been commonly used in restorative dentistry over the years. The longevity of restorations depends upon various physical properties like as solubility. Composite solubility can lead to deleterious effects on the polymer structure. Aim: To evaluate and compare the solubility of a single shade resin composite in comparison to a conventional resin composite in artificial saliva. Materials and Methods: In the present in-vitro study, 44 pellets (10 mm × 1 mm) were prepared from each material. The pellets were divided into two groups (n=22) based on the immersion period of two days and seven days. They were incubated, weighed using an analytical balance, and then immersed in artificial saliva. Weighing was done again after the completion of the immersion period, and solubility was calculated. Paired and independent sample t-tests were used to compare the solubility of both materials after two days and seven days. Results: The differences of solubility values for the single shade composite and conventional composite at two and seven-day intervals were (p=0.031) and (p=0.019), respectively, which were statistically significant. On inter-group comparison, the difference in solubility of the single shade composite at two days was significantly lower compared to conventional composites (p=0.024). Whereas, no significant difference was observed in solubility values between both groups at seven days (p=0.102). Conclusion: The performance of the single shade composite in terms of solubility was better in comparison with conventional composite.

Abstract Background The temperature changes, chemical agents, and brushing activity that resin composite restorations are exposed to in the oral environment can cause changes in surface roughness. In this study, the aim was to investigate in vitro the clinical one-year surface roughness changes of different types of composites (flowable or conventional) from the same companies by subjecting them to immersion in solutions, brushing, and thermal cycling procedures to simulate intraoral conditions. Methods Four different resin composite brands were included in the study using both their conventional (Charisma Smart, 3M Filtek Ultimate Universal, Omnichroma, Beautifil II) and flowable resin composites (Charisma Flow, 3M Filtek Ultimate Flowable, Omnichroma Flow, Beautifil Flow Plus F00), giving 4 groups with 2 types of resin composite in each. 40 samples were prepared for each group/resin type, for a total of 320 samples. After initial surface roughness measurements by a mechanical profilometer, the samples were divided into 4 subgroups (n = 10) and immersed in solutions (distilled water, tea, coffee, or wine) for 12 days. The samples were then subjected to 10,000 cycles of brushing simulation and 10,000 cycles of thermal aging. Surface roughness measurements were repeated after the procedures. For statistical analysis, the 3-way analysis of variance and the Tukey test were used (p

Abstract Background This study aimed to investigate the effect of whitening toothpastes on the color stability and surface roughness of resin composites stained with coffee and cigarette smoke. Methods Seventy-two disk-shaped specimens (6 × 2 mm) of suprananohybrid resin composite were randomly divided into two groups and exposed to coffee and cigarette smoke (n = 36). After staining, the samples randomly divided into four groups according to whitening toothpastes and were brushed for 4 min: Opalescence Whitening (OW); Colgate Optic White (COW); Curaprox Black is White (CPX) and, distilled water (control) (n = 9). Color was measured with spectrophotometer at the initial, after staining, and after brushing, and surface roughness was measured with profilometer at the initial and after brushing. A surface morphology analysis was examined using scanning electron microscopy and atomic force microscopy. The obtained data were statistically analyzed. (p

This study explores the effect of using dental brushes with or without metacrylate-based modeling resins on long-term color stability and surface topographies of resin-based composites. This study examined the effects of two variables: (1) the type of brush used (Art brush, Micro-brush, or Mylar strip) and (2) the application of a modeling resin (applied or not applied). The specimens were artificially aged through 10,000 cycles of thermocycling and subsequently immersed in coffee for 30 days. Measurements of color and surface roughness were taken at baseline and after the aging, using a non-contact profilometer for surface roughness and a spectrophotometer for color. Data were analyzed using paired t-tests and one-way ANOVA. Resin-based composites smoothed with dental brushes or micro brushes without modeling resins exhibited lower color change (ΔE) than other groups. Paired t-tests revealed significant differences in average surface roughness (Ra) and valley depth (Rv) for each surfacing technique before and after aging (p ⩽ 0.01). The root means square average of the profile heights (Rq) significantly increased in the control and micro-brush groups (p ⩽ 0.01). In conclusion, the use of brushes in resin-based composites placement does not increase the susceptibility to staining. Instead, the inclusion of resin modeling contributes to discoloration over time. [ABSTRACT FROM AUTHOR]

Backgrounds: This study aimed to compare the effects of different energy drinks on the surface roughness, weight loss, and color change of various bioactive restorative materials. Methods: Charisma Diamond One, Activa™ BioActive Restorative, Activa™ Presto™ and Equia Forte HT Fil samples were prepared using plastic molds (8 × 2 mm) (n = 10/groups). After polishing, the samples were weighed, their colors were recorded using a spectrophotometer according to the CIEDE2000 system, and their surface roughness was measured using a profilometer. The samples were immersed in Powerade, Burn, Monster and distilled water for 7 days. After immersion, all the measurements were repeated. Statistical analyses were performed using the Wilcoxon signed-rank test and the Mann‒Whitney U test (p < 0.05). Results: All energy drinks roughened the surface of Equia Forte HT Fil (p < 0.05). Powerade and Monster increased the Ra of all materials after 7 days (p < 0.05). Burns affected all materials except the Activa Bioactive (p < 0.05). Significant weight loss was observed in the Equia Forte group after immersion in all the energy drinks, whereas no weight loss was observed in the other groups. According to the color measurements, ΔE00 values were greater in the Burn and Monster groups, except for the Equia Forte HT Fil group (p < 0.05). Conclusion: Energy drinks affected bioactive materials to varying degrees. The glass hybrid material was the most affected, and the bioactive restorative materials based on the resin matrix were the least. [ABSTRACT FROM AUTHOR]

Introduction: Resin composites have been commonly used in restorative dentistry over the years. The longevity of restorations depends upon various physical properties like as solubility. Composite solubility can lead to deleterious effects on the polymer structure. Aim: To evaluate and compare the solubility of a single shade resin composite in comparison to a conventional resin composite in artificial saliva. Materials and Methods: In the present in-vitro study, 44 pellets (10 mm x 1 mm) were prepared from each material. The pellets were divided into two groups (n=22) based on the immersion period of two days and seven days. They were incubated, weighed using an analytical balance, and then immersed in artificial saliva. Weighing was done again after the completion of the immersion period, and solubility was calculated. Paired and independent sample t-tests were used to compare the solubility of both materials after two days and seven days. Results: The differences of solubility values for the single shade composite and conventional composite at two and seven-day intervals were (p=0.031) and (p=0.019), respectively, which were statistically significant. On inter-group comparison, the difference in solubility of the single shade composite at two days was significantly lower compared to conventional composites (p=0.024). Whereas, no significant difference was observed in solubility values between both groups at seven days (p=0.102). Conclusion: The performance of the single shade composite in terms of solubility was better in comparison with conventional composite. [ABSTRACT FROM AUTHOR]

This study investigates the tribological properties of resin composites reinforced with the fillers of glass powder and micro-bubbles. Resin composites were prepared with varying concentrations from 1% to 5% wt of fillers. Tribological tests were conducted using a block-on-ring scheme under dry friction conditions. The measurements of friction coefficient and wear values were performed under variable rotation speeds and loading conditions. The study showed that resin composites with 2–3% glass powder fillers and resin composites with 3–4% micro-bubbles exhibited optimal tribological properties. The resin glass powder modifications reduce the wear by 63% and resin micro-bubbles reduce wear by 32%. SEM analysis of the surfaces revealed surface imperfections and structural damage mechanisms, including abrasive and fatigue wear. The study concludes that specific filler concentrations improve the friction and wear resistance of resin composites, highlighting the importance of material preparation and surface quality in tribological performance. The increased wear resistance on both composites would hopefully expand the usage of additive manufactured composite, namely industrial moving components such as polymer gear, wheel, pulley, etc. [ABSTRACT FROM AUTHOR]

The restoration of endodontically treated teeth (ETT) remains a significant challenge in modern dentistry. These teeth often suffer from substantial structural damage due to both the original pathology and the invasive nature of endodontic procedures. Consequently, ETT are more susceptible to fractures compared to vital teeth, necessitating restorative strategies that can effectively restore both function and aesthetics while minimizing the risk of failure. In recent years, advances in adhesive dentistry and the development of high-strength ceramics have further expanded the restorative options for ETT. Bonded restorations have gained popularity as they preserve more tooth structure and enhance the overall strenght of the tooth-restoration complex. The choice of restorative material and technique is influenced by numerous factors, including the amount of remaining tooth structure, the functional requirements of the tooth, and the aesthetic demands of the patient. Despite the plethora of available materials and techniques, the optimal approach to restoring ETT remains a topic of ongoing research and debate. In this comprehensive review, the current state of and recent advances in restoring damaged endodontically treated teeth are explored. Numerous therapeutic options exist, involving a wide range of materials. This article aims to present the biomaterial advancements of the past decade and their applications, offering alternative approaches to treating damaged ETT with the goal of prolonging their retention on the dental arch and serving as a valuable resource for dental practitioners who face this issue daily. [ABSTRACT FROM AUTHOR]

Background: The temperature changes, chemical agents, and brushing activity that resin composite restorations are exposed to in the oral environment can cause changes in surface roughness. In this study, the aim was to investigate in vitro the clinical one-year surface roughness changes of different types of composites (flowable or conventional) from the same companies by subjecting them to immersion in solutions, brushing, and thermal cycling procedures to simulate intraoral conditions. Methods: Four different resin composite brands were included in the study using both their conventional (Charisma Smart, 3M Filtek Ultimate Universal, Omnichroma, Beautifil II) and flowable resin composites (Charisma Flow, 3M Filtek Ultimate Flowable, Omnichroma Flow, Beautifil Flow Plus F00), giving 4 groups with 2 types of resin composite in each. 40 samples were prepared for each group/resin type, for a total of 320 samples. After initial surface roughness measurements by a mechanical profilometer, the samples were divided into 4 subgroups (n = 10) and immersed in solutions (distilled water, tea, coffee, or wine) for 12 days. The samples were then subjected to 10,000 cycles of brushing simulation and 10,000 cycles of thermal aging. Surface roughness measurements were repeated after the procedures. For statistical analysis, the 3-way analysis of variance and the Tukey test were used (p < 0.05). Results: It was concluded that composite groups and types had an effect on surface roughness at time t0 (p < 0.001). At time t1, the highest surface roughness value was obtained in the Beautifil-conventional interaction. When the surface roughness values between time t0 and t1 were compared, an increase was observed in the Beautifil II and Beautifil Flow Plus F00, while a decrease was observed in the other composite groups. Conclusion: Composite groups, types, and solutions had an effect on the surface roughness of resin composites. After aging procedures, it was concluded that the Beautifil group could not maintain the surface structure as it exceeded the threshold value of 0.2 μm for bacterial adhesion. [ABSTRACT FROM AUTHOR]

Background: This study aimed to investigate the effect of whitening toothpastes on the color stability and surface roughness of resin composites stained with coffee and cigarette smoke. Methods: Seventy-two disk-shaped specimens (6 × 2 mm) of suprananohybrid resin composite were randomly divided into two groups and exposed to coffee and cigarette smoke (n = 36). After staining, the samples randomly divided into four groups according to whitening toothpastes and were brushed for 4 min: Opalescence Whitening (OW); Colgate Optic White (COW); Curaprox Black is White (CPX) and, distilled water (control) (n = 9). Color was measured with spectrophotometer at the initial, after staining, and after brushing, and surface roughness was measured with profilometer at the initial and after brushing. A surface morphology analysis was examined using scanning electron microscopy and atomic force microscopy. The obtained data were statistically analyzed. (p < 0.05). Results: Cigarette smoke caused a significantly higher color change than coffee in the resin composite (p < 0.05). Brushing with hydrogen peroxide and silica-containing whitening toothpaste showed significant differences in color change (p < 0.05). The lowest whitening effect was found in activated charcoal-containing toothpaste. While all toothpastes increased the degree of surface roughness of resin composites, the highest roughness was caused by whitening toothpastes containing activated charcoal. (p < 0.05). Conclusions: The color stability and surface properties of resin composites can be affected by brushing them with whitening toothpaste. The utilization of whitening toothpaste containing hydrogen peroxide can be considered a safe method for increasing the whiteness of discolored resin composites. [ABSTRACT FROM AUTHOR]

This study aimed to evaluate the long-term clinical performance of Giomer and a self-etch adhesive system compared with a nanofilled resin composite and etch-and-rinse adhesive system in Class I and Class II restorations. The study was designed to be double-blinded with intra-individual control. 48 patients with 54 pairs of cavities (class I or class II) were recruited. Each pair of restorations was placed with either BEAUTIFIL II (BF) and FL-BOND II (FL) or Filtek Z350 (Z350) and Scotchbond Multi-Purpose (SMP). Clinical evaluation was performed at baseline, 6-month, 18-month, 4-year and 8-year after placement according to modified USPHS criteria. Kaplan-Meier survival analysis and log rank tests were performed (SPSS 20.0, IBM Corporation, US) to compare the survival probability of different restorations.A generalized linear mixed model (GLMM) was adopted to assess the performance of the materials. The McNemar test was used to show significant changes for all the evaluation criteria and difference between them. At the eight-year recall, 32 patients with 67 restorations were present. There were twelve restorations in total recorded as failure due to loss of retention, restoration fracture, secondary caries, tooth fracture or endodontic treatment due to pulp necrosis. The survival probabilities and calculated annual failure rate(AFR) of BF and Z350 restorations at 8-year were 87.2 % vs 87.8 % and 1.6 % vs 1.5 % respectively with no significant difference (p > 0.05)between the two materials. Over the recall time range of eight years, decreased possibility of alpha rating was observed for retention, marginal adaptation, marginal staining and surface roughness for both materials (p < 0.05). Decreased possibility of alpha rating was observed for surface staining and secondary caries for Z350 (p < 0.05) and restoration fracture for BF (p < 0.05), respectively. Comparing the two restorative systems over eight years, no significant difference was seen for linear decline of the possibility of alpha rating for any of the criteria evaluated (p > 0.05). Giomer material and the self-etch adhesive system had comparable clinical performance with nanofilled resin composite and etch-and-rinse adhesive system over the observation period of eight years. • The retention rate for the Giomer and nano-filled composite restoration systems are comparable. • There is no difference between the two restoration systems for any of the evaluation parameters evaluated over 8 years. • Class II restoration showed less favorable outcome over class I restoration. [ABSTRACT FROM AUTHOR]

Three-dimensional (3D) printing is increasingly used to fabricate dental restorations due to its enhanced precision, consistency and time and cost-saving advantages. The properties of 3D-printed resin materials can be influenced by the chosen printing orientation which can impact the mechanical characteristics of the final products. The objective of this study was to evaluate the influence of printing orientation and artificial ageing on the Martens hardness (HM) and indentation modulus (E IT) of 3D-printed definitive and temporary dental restorative resins. Disk specimens (20 mm diameter × 2 mm height) were additively manufactured in three printing orientations (0°, 45°, 90°) using five 3D-printable resins: VarseoSmile Crownplus (VCP), Crowntec (CT), Nextdent C&B MFH (ND), Dima C&B temp (DT), and GC temp print (GC). The specimens were printed using a DLP 3D-printer (ASIGA MAX UV), while LavaTM Ultimate (LU) and Telio CAD (TC) served as milled control materials. Martens hardness (HM) and indentation modulus (E IT) were tested both before and after storage in distilled water and artificial saliva for 1, 30, and 90 days at 37 °C. 90° printed specimens exhibited higher HM than the other orientations at certain time points, but no significant differences were observed in HM and E IT between orientations for all 3D-printed materials after 90 days of ageing in both aging media. LU milled control material exhibited the highest HM and E IT among the tested materials, while TC, the other milled control, showed similar values to the 3D printed resins. CT and VCP (definitive resins) and ND displayed higher Martens parameters compared to DT and GC (temporary resins). The hardness of the 3D-printed materials was significantly impacted by artificial ageing compared to the controls, with ND having the least hardness reduction percentage amongst all 3D-printed materials. The hardness reduction percentage in distilled water and artificial saliva was similar for all materials except for TC, where higher reduction was noted in artificial saliva. The used 3D printed resins cannot yet be considered viable alternatives to milled materials intended for definitive restorations but are preferable for use as temporary restorations. [ABSTRACT FROM AUTHOR]

Background: This study aimed to investigate the fracture behavior of upper premolars with deep MOD cavities that were restored with Ribbond resin-reinforced fibers (FRCs) placed in different orientations. Methods: A total of 54 extracted maxillary premolars were randomly divided into nine groups. The experimental groups underwent MOD cavity preparation with or without root canal treatment, followed by FRCs placed in the pulpal floor, proximal walls, or both. Fracture resistance was tested using an Instron Machine. The samples were visually inspected to analyze the fracture mode. Results: The highest fracture resistance was observed in intact teeth (1299.98 ± 284.66 MPa). Placing Ribbond fibers in the pulpal floor (1155.86 ± 244.21 MPa) or the proximal walls (1077.56 ± 260.60 MPa) significantly improved fracture resistance (p= < 0.05), compared to cavities restored with only resin composite (804.58 ± 93.34 MPa). However, placing Ribbond fibers in both the pulpal and proximal walls did not enhance fracture resistance. In the MOD-RCT groups, fracture resistance was improved only when Ribbond fibers were placed in the pulpal floor and the proximal walls. Fracture mode analysis revealed a combined fracture in most of the groups. Conclusion: This study concluded that using FRCs significantly improved the fracture resistance of MOD cavities in premolars and revealed that the placement site could be a determinant factor. Plain Language Summary: This study investigated the fracture behavior of upper premolars with deep MOD cavities restored with Ribbond resin-reinforced fibers (FRCs) placed in different orientations.Placing Ribbond fibers in the pulpal floor or the proximal walls significantly improved the fracture resistance of premolars with deep MOD cavities.In the MOD-RCT groups, fracture resistance was improved only when Ribbond fibers were placed in the pulpal floor and the proximal walls.Fracture mode analysis revealed a combined fracture in most of the groups. This study concluded that using FRCs significantly improved the fracture resistance of MOD cavities in premolars and revealed that the placement site could be a determinant factor. [ABSTRACT FROM AUTHOR]

The aim of this study was to evaluate the effect of rotation frequency (rpm) of different polishing discs on the surface roughness of a nanohybrid resin composite material. 126 specimens were prepared in metal molds of 10 mm diameter and 2 mm depth using a nanohybrid resin composite material. The prepared specimens were kept in distilled water for 24 hours. Polishing treatments at 5k, 10k, 15k, and 20k rpm were applied to the nanohybrid resin composite material by grouping different brand polishing discs: Sof-Lex Contouring and Polishing Discs (3M Espe, USA) (3M Group), Optidisc (Kerr Corporation, USA) (Kerr Group), Super-Snap Rainbow Technique Kit (Shofu Dental, Japan) (Shofu Group), Finishing Disc (Bisco Dental, USA) (Bisco Group). The surface roughness was evaluated at three different points by atomic force microscopy for all specimens and scanning electron microscopy was used for visual assessment. Data were evaluated by Two Way ANOVA and Tukey's HSD Test. The mean surface roughness (Ra, μm) of all prepared samples showed significant differences (α = 0.05). According to Two-Way ANOVA, there is a statistically significant relationship between the rpm values and the discs. The 3M group showed the highest roughness value at all rpm speeds. Shofu group at 15k, 20k rpm, Bisco group at 10k, 15k, 20k rpm, the Kerr group at 15k, 20k rpm showed the lowest roughness value and had roughness close to the surfaces finished with a mylar strip. The smoothest surfaces were obtained at 15k rpm, even though polishing discs from different brands were used. It was also observed that 5k and 20k rpm polishing speeds can increase the surface roughness of the nanohybrid resin composite material. [ABSTRACT FROM AUTHOR]

AbstractTo correlate µTBS of different resin cements with their film thickness (FT), Vickers hardness (HV), and ultimate tensile strength (UTS). Human molars (N = 30) were divided into six-groups according to 1: Resin cement: Bifix QM, (BF), GrandioSo Heavy Flow (GHF) and VisCalor Bulk (VB), and 2: Adhesive mode (Optibond Universal): Etch-and-rinse (E&R) or self-etching (SE). CAD/CAM blocks (7 × 7 × 4 mm3) were air-abraded using 50 μm Al2O3 and silane was applied (60 s), and air dried (10 s). For E&R, dentin was etched (15 s), rinsed (30 s), and blot-dried. For both modes, adhesive was applied (20 s), air-dried (5 s), and photo-polymerized (10 s). Sticks (1 × 1 mm2) were stored for 24-h or 6-months. Sticks were pulled in tension (1 mm/min). Debonded sticks were evaluated for failure mode analysis. For FT, nine-bonded slabs from each cement was prepared and evaluated. For UTS, eight-hourglass specimens from each cement were prepared and tested in tension. For HV, five-discs from each cement was prepared and evaluated using a HV tester. Data were analyzed using ANOVA/Pearson’s correlation tests (α = 0.05). No correlation between µTBS/HV was revealed (p > 0.05). A positive correlation between µTBS/FT and µTBS/UTS (p < 0.05) was observed. Three-way ANOVA revealed all experimental factors had a significant effect on µTBS (p < 0.05). The VB showed significantly lower µTBS (20.8 ± 9.3 MPa). The E&R mode showed higher µTBS (26.0 ± 10.9 MPa), and 24-h revealed a higher µTBS (27.4 ± 10.0 MPa). Mixed failure was the predominant type (42.51%). The VB showed the highest FT (122.2 ± 11.9 µm), with GHF revealed higher UTS and HV (112.5 ± 19.7 MPa and 91.6 ± 0.4 Kgf, respectively). Photo-polymerized flowable composite can substitute dual-polymerized cement for CAD/CAM composite bonding. [ABSTRACT FROM AUTHOR]

This study aimed to evaluate the micro-mechanical and macro-mechanical properties of self-cured and light-cured alkasite and to investigate how accelerated degradation in acidic, alkaline, and ethanol solutions affects the macro-mechanical properties of self-cured and light-cured alkasite. The specimens of the alkasite material (Cention Forte, Ivoclar Vivadent) were prepared according to the following three curing modes: (1) light-cured immediately, (2) light-cured after a 5-min delay, and (3) self-cured. Microhardness was tested before and after immersion in absolute ethanol to indirectly determine crosslink density, while flexural strength and flexural modulus were measured using a three-point bending test after accelerated aging in the following solutions: (1) lactic acid solution (pH = 4.0), (2) NaOH solution (pH = 13.0), (3) phosphate-buffered saline solution (pH = 7.4), and (4) 75% ethanol solution. The data were statistically analyzed using a two-way ANOVA and Tukey post hoc test. The results showed that the microhardness, flexural strength, and flexural modulus were significantly lower in self-cured specimens compared to light-cured specimens. A 5-min delay between the extrusion of the material from the capsule and light curing had no significant effect on any of the measured properties. A significant effect of the accelerated aging solutions on macro-mechanical properties was observed, with ethanol and alkaline solutions having a particularly detrimental effect. In conclusion, light curing was preferable to self-curing, as it resulted in significantly better micro- and macro-mechanical properties, while a 5-min delay between mixing the capsule and light curing had no negative effects. [ABSTRACT FROM AUTHOR]

To investigate the feasibility of optical coherence tomography (OCT)-based digital image correlation (DIC) analysis and to identify the experimental parameters for measurements of polymerization shrinkage. Class I cavities were prepared on bovine incisors and filled with Filtek Z350XT Flowable (Z350F). One OCT image of the polymerized restoration was processed to generate virtually displaced images. In addition, the tooth specimen was physically moved under OCT scanning. A DIC software analyzed these virtual and physical transformation sets and assessed the effects of subset sizes on accuracy. The refractive index of unpolymerized and polymerized Z350F was measured via OCT images. Finally, different particles (70–80 µm glass beads, 150–212 µm glass beads, and 75–150 µm zirconia powder) were added to Z350F to inspect the analyzing quality. The analyses revealed a high correlation (>99.99%) for virtual movements within 131 pixels (639 µm) and low errors (<5.21%) within a 10-µm physical movement. A subset size of 51 × 51 pixels demonstrated the convergence of correlation coefficients and calculation time. The refractive index of Z350F did not change significantly after polymerization. Adding glass beads or zirconia particles caused light reflection or shielding in OCT images, whereas blank Z350F produced the best DIC analysis results. The OCT-based DIC analysis with the experimental conditions is feasible in measuring polymerization shrinkage of RBC restorations. The subset size in the DIC analysis should be identified to optimize the analysis conditions and results. Uses of hyper- or hypo-reflective particles is not recommended in this method. [Display omitted] [ABSTRACT FROM AUTHOR]

The current study aimed to evaluate the effects of different combinations of chemical and mechanical challenges on the failure load, failure mode and composition of the resulting fracture surfaces of resin-composite restorations. Three resin composites were used to fill dentin disks (2 mm inner diameter, 5 mm outer diameter, and 2 mm thick) made from bovine incisor roots. The model restorations, half of which were preconditioned with a low-pH buffer (48 h under pH 4.5), were subjected to diametral compression with either a monotonically increasing load (fast fracture) or a cyclic load with a continuously increasing amplitude (accelerated fatigue). The load or number of cycles to failure was noted. SEM was performed on the fracture surfaces to determine the proportions of dentin, adhesive, and resin composite. Both cyclic fatigue and acid preconditioning significantly reduced the failure load and increased the proportion of interfacial failure in almost all the cases, with cyclic fatigue having a more pronounced effect. Cyclic fatigue also increased the amount of adhesive/hybrid layer present on the fracture surfaces, but the effect of acid preconditioning on the composition of the fracture surfaces varied among the resin composites. The adhesive or hybrid layer was found to be the least resistant against the chemomechanical challenges among the components forming the model restoration. Increasing such resistance of the tooth-restoration interface, or its ability to combat the bacterial actions that lead to secondary caries following interfacial debonding, can enhance the longevity of resin-composite restorations. • Resin-composite restorations modeled using dentin-composite discs. • Oral cavity conditions mimicked using accelerated fatigue and chemical preconditioning. • SEM analysis showed adhesive/hybrid layer prominent on fracture surfaces. • Cyclic fatigue had greater impact than preconditioning on degradation at interface. • Findings correlated with long-term clinical resin-dentin bond degradation studies. [ABSTRACT FROM AUTHOR]

Objective: This study aimed to evaluate the fracture strength of teeth restored using fiber-reinforced direct restorative materials after endodontic treatment with a conservative mesio-occlusal access cavity design. Materials and methods: A total of 100 extracted intact mandibular first molars were selected and distributed into a positive control group where teeth left intact and the following four test groups comprised of teeth with conservative mesio-occlusal access cavities that had undergone root canal treatment (n = 20/group): access cavity without restoration (negative control), bulk-fill resin composite with horizontal glass fiber post reinforcement, fiber-reinforced composite with bulk-fill resin and bulk-fill resin composite. Following thermocycling (10,000 cycles), fracture resistance was measured using a universal testing machine. Statistical analyses (one-way analysis of variance and the Tamhane test) were performed, and statistical significance was set at p < 0.05. Results: Groups with minimally invasive access cavities had lower fracture strength than intact teeth, regardless of the restoration material (p < 0.05). Fiber-reinforced composite groups demonstrated higher fracture strength than bulk-fill resin composite alone (p < 0.05). Fracture types varied among groups, with restorable fractures predominant in the fiber-reinforced composite groups. Conclusion: This study suggests that using fiber-reinforced composite materials, especially in combination with bulk-fill resin composites, can effectively enhance the fracture strength of endodontically treated teeth with conservative access cavities. However, using only bulk-fill resin composite is not recommended based on the fracture strength results. Clinical significance: When teeth that undergo endodontic treatment are restored using a conservative access cavity design and fiber-reinforced composite materials, especially in combination with bulk-fill resin composites, the fracture strength of the teeth can be effectively increased. [ABSTRACT FROM AUTHOR]

This clinical case report demonstrates the use of the Dahl Concept in the management of the repeated dislodgement of a posterior full coverage crown associated with a reduced restorative space. The described technique harnesses the addition of resin composite and a temporarily cemented provisional full coverage crown to create sufficient restorative space for the cementation of a definitive posterior full coverage crown restoration at the six-month review. [ABSTRACT FROM AUTHOR]

Aim: The study aimed to comparatively evaluate the effect of eugenol exposure time on the micro-shear bond strength (µ-SBS) of etch-and-rinse and a self-etch adhesive to dentin. Materials and Methods: One hundred and twelve teeth samples were prepared from bisectioning 56 freshly extracted human mandibular molars and were randomly divided into 14 subgroups of 8 samples each (n = 8). Three subgroups containing eugenol and a noneugenol-based restorative material were placed on the dentin surface and left for 24 h, 7 days, and 14 days, respectively, and were compared to a control. Two bonding systems were evaluated: one being etch-and-rinse and the other self-etch adhesive. The µ-SBS were calculated and expressed in MPa. Statistical Analysis: The data were analyzed using mixed model analysis of variance. The level of statistical significance was set at 5%. Results: There was a statistically significant reduction in the µ-SBS values when the self-etch adhesive was used, after the removal of eugenol-containing cement placed for 24 h. However, the reduction in the µ-SBS values after 7 days or 14 days was not significant. Conclusion: Exposure to eugenol containing temporary cement for 24 h significantly reduces the µ-SBS of self-etching adhesives to dentin. However, exposure for 1 week or more has minimal effects. [ABSTRACT FROM AUTHOR]

Purpose: To determine the polymerization kinetics and color stability of a self-adhesive and conventional resin composite after accelerated shelf-life simulation. Materials and Methods: Two composites were tested - universal Filtek Z250 (3M Oral Care) and self-adhesive Constic (DMG). They were stored for 2 months in an incubator to simulate an Arrhenius aging model (60°C) and tested at 5 different time points. Polymerization kinetics (n = 3) were studied using an attenuated total reflectance technique (ATR), through continuous FTIR spectral acquisition (20 min). Spectra were obtained before, during and after 20 s of light curing. With the spectral data, qualitative analysis was performed yielding chemical stability, and quantitative data including extrapolated degree of conversion (DCmax) and polymerization rate (Rpmax) were assessed. To evaluate color stability (n = 3), a spectrophotometer was used to record CIELAB color parameters. Inferential statistics, including repeated measures two-way ANOVA were carried out at a significance level of 5%. Results: The composites did not appear to undergo significant chemical changes after 2 months of accelerated aging. There was a significant impact of aging on the mean DCmax (p < 0.001). Similarly, a reduction in Rpmax, measured for both composites, was also noted (ANOVA; Z = 203.7; p < 0.001). The two-way ANOVA confirmed that the composite had no influence on the color stability (F = 0.94; p = 0.34), while aging did (p = 0.013). Conclusion: Minimal changes in absorbance levels were noted for both composites, without overly affecting their chemical composition. The presence of an acidic monomer did not seem to potentiate the degradation of the self-adhesive composite. This composite even showed greater color stability after aging. [ABSTRACT FROM AUTHOR]

Leonor Castro-Ramirez,1,2 María Espinoza-Salcedo,1 José Huamani-Echaccaya,3 Marysela Ladera-Castañeda,4 Luis Cervantes-Ganoza,5 Emily Hernández-Huamaní,3 Rosa Aroste-Andía,3 Percy Gavilán-Chávez,3 César Cayo-Rojas2 1Postgraduate School, Universidad Privada Antenor Orrego, Trujillo, Peru; 2School of Stomatology, Universidad Privada San Juan Bautista, Lima, Peru; 3School of Stomatology, Universidad Privada San Juan Bautista, Ica, Peru; 4Faculty of Dentistry and Postgraduate School, Research Team “Salud Pública – Salud Integral”, Universidad Nacional Federico Villarreal, Lima, Peru; 5Faculty of Stomatology, Universidad Inca Garcilaso de la Vega, Lima, PeruCorrespondence: César Cayo-Rojas, Universidad Privada San Juan Bautista, School of Stomatology, Av. José Antonio Lavalle 302-304 (Ex Hacienda Villa); Chorrillos, Lima, Peru, Email cesarcayorojas@gmail.comAim: This study aimed to evaluate the effects of polywave and monowave light-emitting diode curing units on the microtensile bond strength and failure types of three bulk-fill resin composites.Materials and Methods: This in vitro experimental study was performed on 180 microbars obtained from human third molars and were distributed into 12 groups according to the type of bulk-fill resin composite and the light-curing unit. Third molars were restored using Filtek One Bulk Fill Restorative, Tetric® N-Ceram Bulk Fill, and Opus Bulk Fill resin composites was light-cured with Elipar Deep Cure L and Valo in three modes: standard, high power, and extra power. Subsequently, microtensile analysis was carried out with a universal testing machine and the type of failure with an optical stereomicroscope. For statistical analysis, the Kruskal–Wallis H-test was used, with the Bonferroni post hoc test and Fisher’s exact test, considering a significance of p< 0.05.Results: There were significant differences in the microtensile bond strength between the Filtek One Bulk Fill restorative and Opus Bulk-Fill (p = 0.042) when light was cured with the polywave unit at standard power. On the other hand, the Filtek One Bulk Fill Restorative and Opus Bulk Fill resins showed significant differences in microtensile bond strength when light was cured with the monowave unit compared with the polywave unit (p< 0.05).Conclusion: The presence of alternative photoinitiator systems that are more reactive than camphorquinone produced higher microtensile bond strength in Tetric N-Ceram Bulk Fill and Opus Bulk Fill resins when light-cured with a high and standard polywave unit, respectively, compared to Filtek One Bulk Fill resins. Finally, Tetric N-Ceram Bulk Fill and Opus Bulk Fill resins had the highest percentage of mixed failures, while Filtek One Bulk Fill resin had adhesive failures, which was related to its lower microtensile bond strength.Keywords: dental materials, resin composite, bulk fill, bond strength, monowave, polywave, light curing units

Arni Irawaty Djais,1,&ast; Hasanuddin Thahir,2,&ast; Ernie Maduratna Setiawatie3,&ast; 1Department of Periodonsia, Faculty of Dentistry, University Hasanuddin, Makassar, Indonesia; 2Department of Periodontology, Faculty of Dentistry, Hasanuddin University, Makassar, Indonesia; 3Department of Periodontology, Faculty of Dentistry, Airlangga University, Surabaya, Indonesia&ast;These authors contributed equally to this workCorrespondence: Arni Irawaty Djais, Department of Periodonsia, Faculty of Dentistry, University Hasanuddin, Tamalanrea Indah, Tamalanrea District, Makassar, South Sulawesi, 90245, Indonesia, Email irawatyarni1975@gmail.com

(1) Background: currently, the advantages of bulk-fill resin composite and high-viscosity glass ionomer materials have increased their use in dentistry; accordingly, their mechanical, surface, and optical properties have become more important. This study aimed to evaluate the mechanical, surface, and optical properties of three different restorative materials (a high-viscosity bulk-fill resin composite (TNC), a flowable bulk-fill resin composite (EBF), and a high-viscosity glass ionomer (FIX)) after application using different techniques (control, heat application, and ultrasonic activation). (2) Methods: specimens were prepared to assess the color stability and surface roughness (n = 12). The specimens were immersed in two different solutions for 14 days. For the compressive strength test, specimens were prepared using a Teflon mold (n = 12). (3) Results: among the specimens applied according to the manufacturer's instructions and immersed in distilled water, it was observed that the surface roughness values of FIX on the 7th day were statistically significantly higher than the other materials (p < 0.05). The compressive strength values of EBF applied using ultrasonic activation were significantly lower than those of EBF applied using the other techniques (p < 0.05). (4) Conclusions: coffee can negatively affect the color stability of restorative materials, but discoloration may vary depending on differences in the content of the material. All materials evaluated in this study exhibited clinically acceptable surface roughness values. It can be concluded that flowable bulk-fill resin composite is the most durable material in terms of compressive strength, so it can be used in the restoration of posterior teeth, especially those exposed to intensive stress. [ABSTRACT FROM AUTHOR]

This study aims to develop multi-functional bio-safe dental resin composites with capabilities for mineralization, high in vitro biocompatibility, and anti-biofilm properties. To address this issue, experimental resin composites consisting of UDMA/TEGDMA-based dental resins and low quantities (1.9, 3.8, and 7.7 vol%) of 45S5 bioactive glass (BAG) particles were developed. To evaluate cellular responses of resin composites, MC3T3-E1 cells were (1) exposed to the original composites extracts, (2) cultured directly on the freshly cured resin composites, or (3) cultured on preconditioned composites that have been soaked in deionized water (DI water), a cell culture medium (MEM), or a simple HEPES-containing artificial remineralization promotion (SHARP) solution for 14 days. Cell adhesion, cell viability, and cell differentiation were, respectively, assessed. In addition, the anti-biofilm properties of BAG-loaded resin composites regarding bacterial viability, biofilm thickness, and biofilm morphology, were assessed for the first time. In vitro biological results demonstrated that cell metabolic activity and ALP expression were significantly diminished when subjected to composite extracts or direct contact with the resin composites containing BAG fillers. However, after the preconditioning treatments in MEM and SHARP solutions, the biomimetic calcium phosphate minerals on 7.7 vol% BAG-loaded composites revealed unimpaired or even better cellular processes, including cell adhesion, cell proliferation, and early cell differentiation. Furthermore, resin composites with 1.9, 3.8, and 7.7 vol% BAG could not only reduce cell viability in S. mutans biofilm on the composite surface but also reduce the biofilm thickness and bacterial aggregations. This phenomenon was more evident in BAG7.7 due to the high ionic osmotic pressure and alkaline microenvironment caused by BAG dissolution. This study concludes that multi-functional bio-safe resin composites with mineralization and anti-biofilm properties can be achieved by adding low quantities of BAG into the resin system, which offers promising abilities to mineralize as well as prevent caries without sacrificing biological activity. [ABSTRACT FROM AUTHOR]

Objectives A comparable performance between bulk-fill composites (BFCs) and progressively inserted conventional resin composite (CRC) has been observed in previous studies. However, a significant number of dental institutions in India continue to employ incremental techniques for RC restorations during preclinical studies. But as BFCs are gaining popularity, they may soon be a part of the curriculum for dental students. The aim of this study was to assess the microhardness and the polymerization efficiency of bulk-fill composites versus CRC in class II slot preparations restored by second-year dental students on ivorine mandibular first molar teeth with high-intensity (HI) and low-intensity (LI) light-curing units using the standard mesial slot preparation technique. Material and Methods Fifty preclinical dental students of second year of a dental college were recruited for the study on a voluntary basis. During their preclinical instructions, all participants were taught and made to practice the handling and curing techniques for two-surface RC restorations for 4 months. Each student was asked to perform four RC restorations: CRC-HI, CRC-LI, BFC-HI, and BFC LI. Assessment of microhardness was done using the Vickers microhardness (VMH) test. Statistical analysis One-way and multivariate analysis of variance and Bonferroni 's post hoc test tests were used for data analysis. Results The results showed a significant decrease in the VMH readings in the horizontal axis, progressing from the uppermost to the lowermost positions (p > 0.05). In all the examined groups, the VMH values at the deepest reading locations were found to be higher than 80% of the values observed at the occlusal surface reading locations. Statistically significant associations were seen between the RC type and the light source used in the VMH readings conducted (p > 0.05). However, no significant correlation was identified between the type of light source and the vertical VMH readings (p > 0.05). Conclusion Instructing dental students to place RC restorations using CRC or BFC materials together with both HI and LI light-curing protocols is safe and can be considered for preclinical studies. [ABSTRACT FROM AUTHOR]

The purpose was to evaluate the degree of conversion (DC), internal adaptation (IA) and closed porosity (CP) of short-fiber reinforced resin composites (SFRC) associated with layered or bulk restorative procedures in deep MOD cavities. Eighty third molars with standardized MOD cavities (5-mm-depth, 2.5-mm-width) were randomly divided into four groups and restored as follows: 1) bulk SFRC; 2) layered SFRC; 3) flowable bulk-fill resin-based composites (RBC); 4) layered conventional RBC. After one-month wet storage the samples were subjected to micro-computed tomography measurements and scanning electron microscopy to assess the IA and CP. Micro-Raman spectroscopy was used to determine the DC in different depths. Data were subjected to ANOVA and Tukey's post-hoc test, multivariate analysis and partial eta-squared statistics (p < 0.05). Pearson correlation coefficient was determined to assess the relationship among the parameters of interest. Gap/total interface volume ratio ranged between 0.22–0.47%. RBCs applied in bulk revealed significantly lower gap volume (p < 0.001) and CP (p < 0.05). Each group showed complete detachment on the pulpal and partial on the lateral walls, except for group3. While the highest DC% was achieved by the conventional RBC (87.2%), followed by the flowable bulk-fill (81.2%), SFRC provided the best bottom to top DC ratio (bulk: 96.4%, layered: 98.7%). The effect of factors studied (RBC type, filling technique) on IA and DC was significant (p < 0.001). Bulk placement of RBCs exhibited lower interfacial gap volume and achieved satisfactory DC without significant correlation between these parameters. Incremental insertion of SFRC had no advantage over bulk placement in terms of IA and DC. • Bulk placement of resin composites exhibits better internal adaptation. • Resin composites in bulk placement achieves satisfactory degree of conversion in deep cavities. • Degree of conversion and internal adaptation are influenced by the type of material and filling technique. • Incremental insertion of short-fiber reinforced resin composite has no advantage over bulk placement. [ABSTRACT FROM AUTHOR]

Context: Long-term color stability of composite resins is one of the most important factors influencing the clinical longevity of aesthetic restorations. Aims: This study evaluated the effect of novel reduced steps and gold standard multiple steps polishing systems of two composite resins; a nano-filled (Filtek Z350XT) versus a supra-nanofill (Palfique LX5) on their color stability after submitting to thermocycling with common beverages. Materials and Methods: Sixty disc-shaped specimens were fabricated from both composite resins (n = 30). From each material, ten specimens acted as the control group (Mylar strip), ten specimens were polished with Sof-Lex Diamond spirals, and ten were polished with Super-Snap X-Treme discs. All the specimens were thermocycled with staining solutions. Color was measured by a spectrophotometer before and after thermocycling and color difference (ΔE*) was calculated. Statistical Analysis Used: One-way analysis of variance followed by Tukey's post-hoc test and independent t-test (α = 0.05) were used. Results: A significantly highest color change was recorded for both control subgroups (P < 0.05), and the Sof-Lex Diamond spiral showed significantly the lowest color change (P < 0.05). Both the control and Sof-Lex Diamond spiral subgroups of Palfique LX5 produced significantly lower color change compared with subgroups of Filtek Z350 (P < 0.05). Conclusions: Sof-Lex Diamond spiral polishing system provided the least color difference for both composites, while there was no significant difference between the materials when the Super-Snap X-Treme polishing system was used. [ABSTRACT FROM AUTHOR]

To assess visually and quantitatively the contributions of the adhesive layer photopolymerization and the subsequent resin composite increment to spatio-temporal maps of temperature at five different cavity locations, subjected to two irradiance curing protocols: standard and ultra-high. Caries-free molars were used to obtain 40, 2 mm thick dentin slices, randomly assigned to groups (n = 5). These slices were incorporated within 3D-printed model cavites, 4 mm deep, restored with Adhese® Universal bonding agent and 2 mm thick Tetric® Powerfill resin composite, and photocured sequentially, as follows: G1: control-empty cavity; G2: adhesive layer; G3 composite layer with no adhesive; and G4 composite layer with adhesive. The main four groups were subdivided based on two curing protocols, exposed either to standard 10 s (1.2 W/cm2) or Ultra high 3 s (3 W/cm2) irradiance modes using a Bluephase PowerCure LCU. Temperature maps were obtained, via a thermal imaging camera, and numerically analyzed at 5 locations. The data were analyzed using two-way ANOVA followed by multiple one-way ANOVA, independent t-tests and Tukey post-hoc tests (α = 0.05). T max , ΔT, T int (integrated area under the curve) and time-to-reach-maximum-temperature were evaluated. Two-way ANOVA showed that there was no significant interaction between light-curing time and location on the measured parameters (p > 0.05), except for the time-to-reach-maximum-temperature (p < 0.05). Curing the adhesive layer alone with the 10 s protocol resulted in a significantly increased pulpal roof temperature compared to 3 s cure (p < 0.05). Independent T-tests between G3 and G4, between 3 s and 10 s, confirmed that the adhesive agent caused no significant increases (p > 0.05) on the measured parameters. The ultra-high light-curing protocol significantly increased ΔT in composite compared to 10 s curing (p < 0.05). When the adhesive layer was photocured alone in a cavity, with a 2 mm thick dentin floor, the exothermal release of energy resulted in higher temperatures with a 10 s curing protocol, compared to a 3 s high irradiance. But when subsequently photocuring a 2 mm layer of composite, the resultant temperatures generated at pulpal roof location from the two curing protocols were similar and therefore there was no increased hazard to the dental pulp from the immediately prior adhesive photopolymerization, cured via the ultra-high irradiation protocol. [ABSTRACT FROM AUTHOR]

The objective of this study is to evaluate the impact of the thickness and translucency of various computer-aided design/computer-aided manufacturing (CAD/CAM) materials on the polymerization of dual-cure resin cement in endocrown restorations. Three commercially available CAD/CAM materials—lithium disilicate glass (e.max CAD), resin composite (CERASMART), and a polymer-infiltrated ceramic network (ENAMIC)—were cut into plates with five different thicknesses (1.5, 3.5, 5.5, 7.5, and 9.5 mm) in both high-translucency (HT) and low-translucency (LT) grades. Panavia V5, a commercial dual-cure resin cement, was polymerized through each plate by light irradiation. Post-polymerization treatment was performed by aging at 37 °C for 24 h under light-shielding conditions. The degree of conversion and Vickers hardness measurements were used to characterize the polymerization of the cement. The findings revealed a significant decrease in both the degree of conversion and Vickers hardness with increasing thickness across all CAD/CAM materials. Notably, while the differences in the degree of conversion and Vickers hardness between the HT and LT grades of each material were significant immediately after photoirradiation, these differences became smaller after post-polymerization treatment. Significant differences were observed between samples with a 1.5 mm thickness (conventional crowns) and those with a 5.5 mm or greater thickness (endocrowns), even after post-polymerization treatment. These results suggest that dual-cure resin cement in endocrown restorations undergoes insufficient polymerization. [ABSTRACT FROM AUTHOR]

Background: Glass fibre‐reinforced composite (GFRC) has the potential to enhance the mechanical properties of resin‐based restorations. Nevertheless, the application technique can influence the cervical margin porosity, potentially reducing the mechanical strength of restorations. Methods: In an in vitro setup, mould specimens underwent six different treatments to assess the effects of snowplow and incremental curing techniques on the properties of GFRC (EverX) and universal resin composite (Filtek). Mechanical properties, namely flexural strength (FS), compressive strength (CS) and Vickers hardness (VH), were evaluated following ISO 4049 standards. Data interpretation utilized the Kruskal–Wallis tests. Results: No significant difference emerged across groups for FS. CS in the snowplow method with lesser EverX thickness (SnPl_1) was comparable with only EverX and Filtek (P > 0.05). The CS was reduced in the snowplow technique with greater EverX thickness (SnPl_2) (P < 0.05) and further decreased with the incremental method (P < 0.001). VH results showed that EverX Posterior was consistently softer than Filtek, with specific patterns of hardness variations among different application methods. Conclusions: Applying EverX and Filtek using the snowplow technique delivers superior CS and VH for restorations in contrast to the incremental method. Utilizing the snowplow approach in high‐stress areas can make restorations more fracture‐resistant. [ABSTRACT FROM AUTHOR]