Northern South America is identified as one of the most vulnerable regions to be affected by climate change. Furthermore, recent extreme wet seasons over the region have induced socioeconomic impacts of wide proportions. Hence, the evaluation of rainfall simulations at seasonal and interannual time scales by the CMIP5 models is urgently required. Here, we evaluated the ability of seven CMIP5 models (selected based on literature review) to represent the seasonal mean precipitation and its interannual variability over northern South America. Our results suggest that it is easier for models to reproduce rainfall distribution during boreal summer and fall over both oceans and land. This is probably due to the fact that during these seasons, incoming radiation and ocean-atmosphere feedbacks over Atlantic and Pacific oceans locate the ITCZ on the Northern Hemisphere, as suggested by previous studies. Models exhibit the worse simulations during boreal winter and spring, when these processes have opposite effects locating the ITCZ. Our results suggest that the models with a better representation of the oceanic ITCZ and the local low-level jets over northern South America, such as the Choco low-level jet, are able to realistically simulate the main features of seasonal precipitation pattern over northern South America.

Calcium silicate hydrates are compounds of SiO2 – CaO – H2O system. These materials are used to make lime-sand bricks concretes, or “cellular concretes”, lime-flint brices and as fillers in rubber, paint and plastic products industries, among others. Undoubtedly, the tobermoritas is the most interesting group given its important role in concrete hydration: hydrated calcium silicate (C – S- H) is the main concrete hydration product and its primary bounding phase. The hydrothermal method is the most frequently used in the synthesis of these materials. This work shows the synthesis of hydrated calcium silicates through the controlled precipitation method using silicon dioxide SiO2, as raw material obtained from rice husk. The physicochemical phenomena that occur during the calcium silicates synthesis process were analized. The crystalline phases of the final product when exposed to thermic treatments were studied as well using x-ray diffraction and Infrared spectroscopy.Los silicatos de calcio hidratados son compuestos del sistema SiO2-CaO-H2O. Estos materiales se utilizan para fabricar ladrillos de cal-arena, hormigones aireados (espumados) u “hormigón celular”, ladrillos de cal-flint, como material de relleno en las industrias de productos de caucho, pinturas y plásticos, entre otros posibles usos. Indudablemente el grupo de las tobermoritas es el más interesante debido a su papel importante en la hidratación del cemento: los silicatos tricálcico (3CaO. SiO2-C3S) y dicálcico (2CaO, SiO2-C2S) son los principales constituyentes del cemento Pórtland. En este trabajo se muestra la obtención de compuestos de silicato de calcio a través del método de precipitación controlada usando como fuente de silicio el dióxido de silicio, SiO2 obtenido de la cascarilla de arroz. Se analizan los fenómenos fisicoquímicos que ocurren durante el proceso de síntesis y se estudia la evolución de las fases cristalinas del producto obtenido, al ser sometido a tratamientos térmicos, utilizando para ello Difracción de Rayos X (DRX) y espectroscopía infrarroja (FTIR).

Se comparan resultados respecto al comportamiento eléctrico del material sinterizado, a partir de polvos precursores de materiales cerámicos con propiedades eléctricas no lineales, conocidos como varistores. Los rutas de síntesis investigadas buscando reducir el tamaño de partícula a distribuciones nanométricas, son de precipitación controlada, método Pechini y el método tradicional de mezcla de óxidos. La matriz de los polvos se basa en ZnO dopado con óxidos de Bi, Mn y Sb y se realizan seguimientos en etapas intermedias y finales del proceso por medio de las técnicas Difracción de Rayos X y microscopía electrónica de barrido. Se analizan los resultados del proceso de sinterización establecido según programas de temperatura-tiempo del material precursor, tomando como base las técnicas de Análisis Termogravimétrico y Análisis Térmico Diferencial. Se muestra la superioridad de las rutas químicas respecto a la mezcla de óxidos ya que permiten obtener menores tamaños de partícula, menores temperaturas de densificación, y mejores respuestas eléctricas las cuales están dadas por coeficientes de no linealidad mayores y corrientes de fuga menores. Results are compared with respect to electrical performance of the sintered material from ceramics precursor powders with nonlinear electrical properties, known as varistors. The synthesis routes investigated to reduce the particle size to nanometer distributions are controlled precipitation, Pechini method and the traditional method of mixed oxides. The matrix of the powders is based on ZnO doped with Bi, Mn and Sb and monitoring is made on intermediate and final stages of the process by X-ray diffraction and scanning electron microscopy. We analyze the results of the sintering process established under temperature-time programs of the precursor material, based on Thermo gravimetric Analysis techniques and Differential Thermal Analysis. The results show the superiority of the chemical routes compared to the mixture of oxides since with the former it is possible to obtain smaller particle sizes, lower densification temperature, and improved electrical responses given by higher nonlinearity coefficients and lower leakage currents. Comparamos os resultados respeito ao comportamento eléctrico do material sinterizado, a partir de pós precursores de materiais cerâmicos com propriedades eléctricas no lineais, conhecido como varistores. As rotas de síntese investigadas procurando reduzir o tamanho de partícula a distribuição nanométricas, são de precipitação controlada, método Pechini e o método tradicional de mistura de óxidos. A matriz dos pós é baseada em Zno dopado com óxidos de Bi, Mn e Sb e realizam-se seguimentos em etapas intermediarias e finais do processo por meio de difração de raios X e Microscopia Eletrônica de Barrido. Analisam-se os resultados de processo de sinterização estabelecidos segundo programas de temperatura-tempo no material precursor, com base as técnicas de Análise Termogravimétrica e Análise Térmica Diferencial. Mostra-se a superioridade das rotas químicas respeito à mistura de óxidos já que permitem obter menores tamanho de partícula, menores temperaturas de densificação e menores respostas elétricas dadas por coeficiente de no linearidade mais altos e corrente de fuga menores.

Se comparan resultados respecto al comportamiento eléctrico del material sinterizado, a partir de polvos precursores de materiales cerámicos con propiedades eléctricas no lineales, conocidos como varistores. Los rutas de síntesis investigadas buscando reducir el tamaño de partícula a distribuciones nanométricas, son de precipitación controlada, método Pechini y el método tradicional de mezcla de óxidos. La matriz de los polvos se basa en ZnO dopado con óxidos de Bi, Mn y Sb y se realizan seguimientos en etapas intermedias y finales del proceso por medio de las técnicas Difracción de Rayos x y microscopía electrónica de barrido. Se analizan los resultados del proceso de sinterización es- tablecido según programas de temperatura-tiempo del material precursor, tomando como base las técnicas de Análisis Termogravimétrico y Análisis Térmico Diferencial. Se muestra la superioridad de las rutas químicas respecto a la mezcla de óxidos ya que permiten obtener menores tamaños de partícula, menores temperaturas de densificación, y mejores respuestas eléctricas las cuales están dadas por coeficientes de no linealidad mayores y corrientes de fuga menores.Abstract: Results are compared with respect to electrical performance of the sintered material from ceramics precursor powders with nonlinear electrical properties, known as varistors. The synthesis routes investigated to reduce the particle size to nanometer distributions are controlled precipitation, Pechini method and the traditional method of mixed oxides. The matrix of the powders is based on ZnO doped with Bi, Mn and Sb and monitoring is made on intermediate and final stages of the process by x-ray diffraction and scanning electron microscopy. We analyze the results of the sintering process established under temperature-time programs of the precursor material, based on Thermo gravimetric Analysis techniques and Differential Thermal Analysis. The results show the superiority of the chemical routes compared to the mixture of oxides since with the former it is possible to obtain smaller particle sizes, lower densification temperature, and improved electrical responses given by higher nonlinearity coefficients and lower leakage currents. Se comparan resultados respecto al comportamiento eléctrico del material sinterizado, a partir de polvos precursores de materiales cerámicos con propiedades eléctricas no lineales, conocidos como varistores. Los rutas de síntesis investigadas buscando reducir el tamaño de partícula a distribuciones nanométricas, son de precipitación controlada, método Pechini y el método tradicional de mezcla de óxidos. La matriz de los polvos se basa en ZnO dopado con óxidos de Bi, Mn y Sb y se realizan seguimientos en etapas intermedias y finales del proceso por medio de las técnicas Difracción de Rayos x y microscopía electrónica de barrido. Se analizan los resultados del proceso de sinterización es- tablecido según programas de temperatura-tiempo del material precursor, tomando como base las técnicas de Análisis Termogravimétrico y Análisis Térmico Diferencial. Se muestra la superioridad de las rutas químicas respecto a la mezcla de óxidos ya que permiten obtener menores tamaños de partícula, menores temperaturas de densificación, y mejores respuestas eléctricas las cuales están dadas por coeficientes de no linealidad mayores y corrientes de fuga menores.Abstract: Results are compared with respect to electrical performance of the sintered material from ceramics precursor powders with nonlinear electrical properties, known as varistors. The synthesis routes investigated to reduce the particle size to nanometer distributions are controlled precipitation, Pechini method and the traditional method of mixed oxides. The matrix of the powders is based on ZnO doped with Bi, Mn and Sb and monitoring is made on intermediate and final stages of the process by x-ray diffraction and scanning electron microscopy. We analyze the results of the sintering process established under temperature-time programs of the precursor material, based on Thermo gravimetric Analysis techniques and Differential Thermal Analysis. The results show the superiority of the chemical routes compared to the mixture of oxides since with the former it is possible to obtain smaller particle sizes, lower densification temperature, and improved electrical responses given by higher nonlinearity coefficients and lower leakage currents.

En este trabajo se utilizó el método de precipitación controlada para sintetizar ZrO2 tetragonal estabilizado con óxido de calcio, CaO. Los sólidos obtenidos se caracterizaron utilizando análisis térmico diferencial y gravimétrico (ATD/TG), Espectroscopia Infrarroja con transformada rápida de Fourier (FT-IR), Difracción de Rayos X (DRX), y microscopia electrónica de transmisión (MET). Los resultados indican que al tratar el polvo cerámico a una temperatura de 600 ºC se obtiene ZrO2 con fase cristalina tetragonal; además las partículas de ZrO2 presentaron tamaño nanométrico (< 100 nm). Se prestó especial atención a los posibles mecanismos de formación de las partículas. In this work, ZrO2 tetragonal stabilized with calcium oxide was synthesized by the controlled precipitation method. Ceramics powders were characterized using Differential Thermal Analysis and Thermal Gravimetry Analysis, (DTA/TG), Fourier Transform Infrared Spectroscopy (FT-IR), X-ray diffraction (XRD) and Transmission Electron Microscopy (TEM). Results show that ceramic powders treatment thermally at 600 ºC, presents ZrO2 in tetragonal crystalline phase; this powder contained particles of nanometric size. The mechanism formation of particles was discussed.

En este trabajo se utilizó el método de precipitación controlada para sintetizar ZrO₂ tetragonal estabilizado con óxido de calcio, CaO. Los sólidos obtenidos se caracterizaron utilizando análisis térmico diferencial y gravimétrico (ATD/TG), Espectroscopia Infrarroja con transformada rápida de Fourier (FT-IR), Difracción de Rayos X (DRX), y microscopia electrónica de transmisión (MET). Los resultados indican que al tratar el polvo cerámico a una temperatura de 600 ºC se obtiene ZrO₂ con fase cristalina tetragonal; además las partículas de ZrO₂ presentaron tamaño nanométrico ( and lt; 100 nm). Se prestó especial atención a los posibles mecanismos de formación de las partículas.

En este trabajo se presenta el proceso de síntesis de ZrO2 empleando el método de precipitación controlada. Como precursor se utilizó la sal metálica ZrOCl2 • 8H2O. Los polvos cerámicos se caracterizaron con diferentes técnicas para determinar su composición química, estructura cristalina, morfología y tamantilde;o de partícula. Las partículas presentaron un tamantilde;o nanométrico inferior a

El óxido de estaño es un compuesto ampliamente utilizado en aplicaciones tecnológicas destacándose como catalizador,sensor de gas, en fabricación de varistores, dispositivos electrónicos, electrodos electrocatalíticos y celdas fotovoltaicas, entre otros. En el presente trabajo se utilizó el método de precipitación controlada (MPC) para sintetizar óxido de estaño de tamaño nanométrico, empleando como precursor sulfato de estaño. El control de las diferentes etapas del proceso de síntesis se realizó a través de los registros de variación de pH, valoración potenciométrica, del sistema. Con base a esta información y el estudio de espectroscopía infrarroja realizada en la fase sólida, a diferentes valores de pH, se propone un mecanismo de formación de las partículas donde las reacciones de hidrólisis y condensación son muy importantes. Se analizó, además, el efecto del lavado del precipitado con etilendiamina y se verificó la eliminación del anión sulfato con este proceso, obteniéndose al final óxido de estaño, SnO y SnO2, como principales fases cristalinas, a temperatura ambiente. Las características del óxido de estaño nanométrico se determinaron utilizando espectroscopía infrarroja de transmisión FTIR, difracción de rayos X (DRX), y microscopía electrónica de transmisión (MET). Tin oxide, is a compound used in many technological applications among them as gas sensor and in the production of varistors, electronic devices, electrocatalitic electrodes and fotovoltaic cells, among others. In this work the controlled precipitation method was used to synthesize tin oxide of nanometric size using tin sulfate precursor. The control of different stages of the synthesis process was carried out through the variation of the system pH registrations, potentiometric titration,; This curve contain information on the different processes that take place in the system and it can be used to guarantee the process reproducibility. Additionally we propose a mechanism to explain the nucleation of solid phase in the solution. The hydrolysis and policondensation reactions are very important for this mechanism. Precipitate washing with an ethylendiamine solution permitted eliminated of SO4 2- and it permitted to obtain the tin oxide as the principal crystalline phase at room temperature. The characteristics of the obtained ceramic powder were determined using infrared espectroscopy (FTIR), X-ray diffraction (XRD), and transmission electron microscopy (TEM). Fil: Montenegro Hernandez, Alejandra. Comisión Nacional de Energía Atómica. Gerencia de Área de Aplicaciones de la Tecnología Nuclear. Gerencia de Investigación Aplicada; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina Fil: Castro, Miriam Susana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Rodriguez Paez, Jorge Enrique. Universidad del Cauca; Colombia

La alúmina se obtiene normalmente utilizando el proceso Bayer, ella se emplea industrialmente para obtener abrasivos, aisladores eléctricos, soporte para catalizadores, refractarios, material de relleno para polímeros, entre otros usos, y sus propiedades se pueden modificar variando la temperatura de calcinación y el tamaño de partícula. Actualmente, se analizan diversos métodos de síntesis para la obtención de a-Al2O3 con el fin de favorecer una u otra característica exigida para una aplicación en particular. Ellos presentan ventajas y desventajas y tienen en común una completa descripción del mismo pero no se hace mención de los posibles mecanismos de formación de las partículas. A continuación se hace un análisis del proceso de obtención de las partículas de alúmina a partir del Al2(SO4)3.18H2O utilizando el método de precipitación controlado (MPC), poniendo especial interés en la conformación de los complejos y compuestos intermedios de aluminio que se forman a medida que se desarrolla el proceso de síntesis. Los resultados obtenidos por microscopía óptica, FTIR, ATD, TG, DRX, y MET indican que factores tales como el pH, velocidad de agitación y la naturaleza del solvente de lavado inciden en la conformación de los distintos complejos intermedios de Alúmina y las propiedades finales de las partículas de a-Al2O3. Alumina is normally obtained employing the Bayer process, it is employed industrially in order to obtain abrasives, electrical insulators, catalysts supports, refractory materials, filling material for polymers, among other uses, and its properties can be modified by varying its calcination temperature and particle size. Nowadays, several synthetic methods for a-Al2O3 are being analyzed in order to meet the demands of particular applications. These methods have advantages and disadvantages and they have in common a complete description of the method in question but they do not mention the possible formation mechanisms of the particles. In what follows an analysis is made of the Alumina particle production from Al2(SO4)3.18H2O by the use of the controlled precipitation method (CPM), placing special interest in the conformation of the complexes and intermediate compounds of Aluminum that are formed throughout the synthesis process. Results obtained by optical microscopy, FTIR, ATD, TG, XRD and TEM indicate that factors such as pH, stirring speed and the nature of the washing solvent influence the conformation of the different intermediate Alumina complexes and the final properties of the a-Al2O3 particles.

El óxido de estaño, SnO2, es un compuesto utilizado en muchas aplicaciones tecnológicas entre ellas como sensor de gas y en la fabricación de desviadores de sobretensiones, varistores, entre otros. En el presente trabajo se utilizó el método de precipitación controlada, MPC, para sintetizar óxido de estaño de tamaño nanométrico empleando como precursor sulfato de estaño. El control de las diferentes etapas del proceso de síntesis se realizó a través de los registros de variación de pH, valoración potenciométrica, y de la conductividad específica y valoración conductimétrica del sistema. Estas curvas contienen información sobre los diferentes procesos que ocurren en el sistema y se pueden utilizar para garantizar la reproducibilidad del proceso. Las características del polvo cerámico obtenido se determinaron utilizando difracción de rayos X (DRX), espectroscopia infrarroja (FTIR), y Microscopía Electrónica de Transmisión (MET). Tin oxide, SnO2, is a compound used in many technological applications among them as gas sensor and in the production of diverters surges, varistors, among others. In the present work the controlled precipitation method, MPC, was used to synthesize tin oxide, using tin sulfate as precursor. The control of the different stages of the synthesis process was carried out through the registrations of pH variation, potentiometric titration, and specific conductivity of the system. These curves contain information on the different processes that taking place in the system and they can be used to guarantee the reproducibility of the process. The characteristics of the obtained ceramic powder were determined using X rays diffraction (XRD), infrared spectroscopy (FTIR), and transmission electron microscopy (TEM).

Los silicatos de calcio hidratados son compuestos del sistema SiO2 -CaO-H2 O. Estos materiales se utilizan para fabricar ladrillos de cal-arena, hormigones aireados (espumados) u “hormigón celular”, ladrillos de cal-flint, como material de relleno en las industrias de productos de caucho, pinturas y plásticos, entre otros posibles usos. Indudablemente el grupo de las tobermoritas es el más interesante debido a su papel importante en la hidratación del cemento: los silicatos tricálcico (3CaO. SiO2 -C3 S) y dicálcico (2CaO, SiO2 -C2 S) son los principales constituyentes del cemento Pórtland. En este trabajo se muestra la obtención de compuestos de silicato de calcio a través del método de precipitación controlada usando como fuente de silicio el dióxido de silicio, SiO2 obtenido de la cascarilla de arroz. Se analizan los fenómenos fisicoquímicos que ocurren durante el proceso de síntesis y se estudia la evolución de las fases cristalinas del producto obtenido, al ser sometido a tratamientos térmicos, utilizando para ello Difracción de Rayos X (DRX) y espectroscopía infrarroja (FTIR).