Search

In this study, a corrosion pit test using notched bar specimens was conducted to investigate the effect of stress magnitude on the pit growth rate. To produce the notched bar specimens, 304 austenitic stainless steel was used, which is a material used for spent nuclear fuel canisters. Furthermore, three levels of stresses were generated using different notch radii. The corrosion pits were quantitatively measured through scanning electron microscopy and analyzed by finite element analysis. Based on experimental data, the pit growth rate model is suggested in terms of the stress and exposure time.

Pit dissolution rate on samples of an AISI 304 stainless steel (SS) in natural sea water was assessed using a scanning reference electrode technique (SRET) and compared with chronoamperometric measurements. Corrosion pits generated in AISI 304 SS samples under potentiostatic control at room temperature and smooth surface presented an empirical exponential growth rate law. The quantity of dissolved metal per pit as a function of polarisation time determined using SRET and chronoamperometric measurements presented acceptable agreement. Considering the capabilities and limitations of scanning techniques, this study presents an approach of the pit growth rate determination from SRET measurements demonstrating the possibility to perform real time quantitative determination of localised dissolution rate. [ABSTRACT FROM AUTHOR]

In this study, a corrosion pit test using notched bar specimens was conducted to investigate the effect of stress magnitude on the pit growth rate. To produce the notched bar specimens, 304 austenitic stainless steel was used, which is a material used for spent nuclear fuel canisters. Furthermore, three levels of stresses were generated using different notch radii. The corrosion pits were quantitatively measured through scanning electron microscopy and analyzed by finite element analysis. Based on experimental data, the pit growth rate model is suggested in terms of the stress and exposure time. [ABSTRACT FROM AUTHOR]

This paper presents experimental data for a 0.2%C steel/artificial seawater system showing the influence of shear loading on corrosion response, via measurements of electrochemical variables, e.g. anodic/cathodic Tafel slopes and polarization resistance. Based on the results of these tests, several corrosion fatigue tests were conducted at different stress levels under potentiostatic control. Analysis of the results shows there to be a dependence of corrosion rate on the ratio of applied/yield strain and test frequency. In addition, the corrosion current associated with corrosion fatigue (CF) damage appears to be dependent upon the crack size, which in turn shows a relationship with fatigue crack growth rate. This paper sets out to determine the influence of stress on electrochemical parameters, i.e. free corrosion potential, Ecorr , polarization resistance, Rp , anodic, τa and cathodic, τc Tafel constants. Based upon these results, it is found that a simple linear relationship between stress and corrosion damage does not exist. Furthermore, analysis of the corrosion current fluctuations during corrosion fatigue crack growth shows a minimum current coincident with the point at which a crack is growing at its slowest rate. [ABSTRACT FROM AUTHOR]