Search

Improving current injection into r- and m-planes of nanowires (NWs) is essential to realizing efficient GaInN/GaN multiple quantum shell (MQS) NW-based light-emitting diodes (LEDs). Here, we present the effects of different p-GaN shell growth conditions on the emission characteristics of MQS NW-LEDs. Firstly, a comparison between cathodoluminescence (CL) and electroluminescence (EL) spectra indicates that the emission in NW-LEDs originates from the top region of the NWs. By growing thick p-GaN shells, the variable emission peak at around 600 nm and degradation of the light output of the NW-LEDs are elaborated, which is attributable to the localization of current in the c-plane region with various In-rich clusters and deep-level defects. Utilizing a high growth rate of p-GaN shell, an increased r-plane and a reduced c-plane region promote the deposition of indium tin oxide layer over the entire NW. Therefore, the current is effectively injected into both the r- and m-planes of the NW structures. Consequently, the light output and EL peak intensity of the NW-LEDs are enhanced by factors of 4.3 and 13.8, respectively, under an injection current of 100 mA. Furthermore, scanning transmission electron microscope images demonstrate the suppression of dislocations, triangular defects, and stacking faults at the apex of the p-GaN shell with a high growth rate. Therefore, localization of current injection in nonradiative recombination centers near the c-plane was also inhibited. Our results emphasize the possibility of realizing high efficacy in NW-LEDs via optimal p-GaN shell growth conditions, which is quite promising for application in the long-wavelength region.

The morphology and crystalline quality of p-GaN shells on coaxial GaInN/GaN multiple quantum shell (MQS) nanowires (NWs) were investigated using metal-organic chemical vapor deposition. By varying the trimethylgallium (TMG) flow rate, Mg doping, and growth temperature, it was verified that the TMG supply and growth temperature were the dominant parameters in the control of the p-GaN shape on NWs. Specifically, a sufficiently high TMG supply enabled the formation of a pyramid-shaped NW structure with a uniform p-GaN shell. The ratio of the growth rate between the c - and m -planes on the NWs was calculated to be approximately 0.4545. High-angle annular dark-field scanning transmission electron microscopy characterization confirmed that no clear extended defects were present in the n-GaN core and MQS/p-GaN shells on the sidewall. Regarding the p-GaN shell above the c -plane MQS region, only a few screw dislocations and Frank-type partial dislocations appeared at the interface between the serpentine c -plane MQS and the p-GaN shell near the tips. This suggested that the crystalline quality of the MQS structure can trigger the formation of screw dislocations and Frank-type partial dislocations during the p-GaN growth. The growth mechanism of the p-GaN shell on NWs was also discussed. To inspect the electronic properties, a prototype of a micro light-emitting diode (LED) with a chip size of 50 × 50 μm 2 was demonstrated in the NWs with optimal growth. By correlating the light output curve with the electroluminescence spectra, three different emission peaks (450, 470, and 510 nm) were assignable to the emission from the m -, r -, and c -planes, respectively.