Search

Pervious concrete is an innovative eco-friendly construction material. Through the application of mineral admixtures and microscopic analysis to optimize its performance and analyze its mechanisms, its traits as a sustainable building option may be further improved. This study primarily examines the impact of the optimal blend quantities of fly ash, silica fume, and reinforcing agent on the attributes, micro-morphology, and phase composition of porous concrete. The optimal admixture was chosen after analyzing the effects of various factors on the mix ratio and properties of permeable concrete. To understand the degree of impact, performance tests were conducted on the 28-day compressive strength, water permeability coefficient, and porosity. Furthermore, the micro-mechanisms of the admixtures and reinforcing agents on the properties of permeable concrete were analyzed from a microscopic point of view using scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. This research found that the advantageous properties of permeable concrete were enhanced by the simultaneous integration of appropriate quantities of fly ash, silica fume, and reinforcing agent. This resulted in a 28-day compressive strength of 18.33 MPa and a permeability coefficient of 8.27 mm/s. Compared with the unadulterated mineral admixture, the optimal admixture of fly ash, silica fume, and reinforcing agent at the same time increased the 28-day compressive strength by about double; the permeability coefficient was reduced by 36%, but it was still at a high level; and the measured porosity did not differ much from the designed porosity. Through thorough microanalysis, the hydration reaction was significantly improved, which could enhance the microstructure and pore structure of the concrete. This was supported by a substantial increase in the macroscopic compressive strength and a decrease in the water permeability coefficient, which were consistent with the aforementioned enhancement found in the microanalysis. [ABSTRACT FROM AUTHOR]

Pervious concrete is an innovative eco-friendly construction material. Through the application of mineral admixtures and microscopic analysis to optimize its performance and analyze its mechanisms, its traits as a sustainable building option may be further improved. This study primarily examines the impact of the optimal blend quantities of fly ash, silica fume, and reinforcing agent on the attributes, micro-morphology, and phase composition of porous concrete. The optimal admixture was chosen after analyzing the effects of various factors on the mix ratio and properties of permeable concrete. To understand the degree of impact, performance tests were conducted on the 28-day compressive strength, water permeability coefficient, and porosity. Furthermore, the micro-mechanisms of the admixtures and reinforcing agents on the properties of permeable concrete were analyzed from a microscopic point of view using scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. This research found that the advantageous properties of permeable concrete were enhanced by the simultaneous integration of appropriate quantities of fly ash, silica fume, and reinforcing agent. This resulted in a 28-day compressive strength of 18.33 MPa and a permeability coefficient of 8.27 mm/s. Compared with the unadulterated mineral admixture, the optimal admixture of fly ash, silica fume, and reinforcing agent at the same time increased the 28-day compressive strength by about double; the permeability coefficient was reduced by 36%, but it was still at a high level; and the measured porosity did not differ much from the designed porosity. Through thorough microanalysis, the hydration reaction was significantly improved, which could enhance the microstructure and pore structure of the concrete. This was supported by a substantial increase in the macroscopic compressive strength and a decrease in the water permeability coefficient, which were consistent with the aforementioned enhancement found in the microanalysis.

To solve the leakage problem of concrete cracking and seepage in the freezing shaft lining of deep topsoil, it is proposed to use hybrid fibers and micro expansion high-performance concrete. Based on the normal concrete mix ratio of the frozen shaft lining, the orthogonal test method was used to investigate the effect of the water-to-binder ratio, the amount of expansion agent, the amount of polyvinyl alcohol fiber and the amount of imitation steel fiber on the compressive strength and splitting tensile strength of fiber hybrid and micro expansion high performance concrete. Comprehensive balance determines that the best mix ratio of this test is water: cement: NF-F: expansion agent: polyvinyl alcohol fiber: polypropylene imitation steel fiber: sand: basalt gravel =166.112:410:130:32.8:1.092:5:615.992:1 095.096. The crack resistance test results show that the fiber hybrid and expansion agent composite concrete has excellent crack resistance.