Search

Nickel (Ni) nanoparticles can be enriched on the surface of iron-based frictional pairs, which provides the possibility to get rid of the competitive adsorption between the polar species of vegetable oil and the surface-active nano-additives thereon. In this paper, nickel acetylacetonate was used as a precursor to in-situ synthesize nickel nanoparticles with an average diameter of about 12 nm in rapeseed oil (RO) as the reducing agent, surface modifier, and solvent as well. The tribological properties of the as-synthesized Ni nanoparticles were evaluated with a four-ball tribometer, and their tribomechanism was investigated based on the characterizations of the tribofilm on rubbed steel surfaces by the scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). It was found that the Ni nanoparticles in-situ prepared in the RO with a mass fraction of 0.3% can reduce the wear scar diameter (WSD) of the steel ball by 36%. This is because, on the one hand, the Ni nanoparticles are adsorbed on the rubbed steel surfaces to repair or fill up the micro-pits and grooves thereon. On the other hand, Ni nanoparticles participate in tribochemical reactions with atmospheric O and steel substrate to form the tribochemical reaction film on the rubbed steel surfaces with the assistance of friction-induced heat and applied normal load. In addition, an amorphous carbon film is formed on the rubbed surface via the carbonization of base oil under the catalysis of Ni nanoparticles. The adsorbed Ni layer, the tribochemical reaction film, and the carbon layer comprise a composite tribofilm composed of amorphous carbon, polar fatty acid, metallic nickel, iron oxides, and nickel oxides on the rubbed steel surfaces, which contributes to significantly improving the antiwear ability and load-carrying capacity of the RO for the steel–steel sliding pair. [ABSTRACT FROM AUTHOR]

Abstract Nickel (Ni) nanoparticles can be enriched on the surface of iron-based frictional pairs, which provides the possibility to get rid of the competitive adsorption between the polar species of vegetable oil and the surface-active nano-additives thereon. In this paper, nickel acetylacetonate was used as a precursor to in-situ synthesize nickel nanoparticles with an average diameter of about 12 nm in rapeseed oil (RO) as the reducing agent, surface modifier, and solvent as well. The tribological properties of the as-synthesized Ni nanoparticles were evaluated with a four-ball tribometer, and their tribomechanism was investigated based on the characterizations of the tribofilm on rubbed steel surfaces by the scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). It was found that the Ni nanoparticles in-situ prepared in the RO with a mass fraction of 0.3% can reduce the wear scar diameter (WSD) of the steel ball by 36%. This is because, on the one hand, the Ni nanoparticles are adsorbed on the rubbed steel surfaces to repair or fill up the micro-pits and grooves thereon. On the other hand, Ni nanoparticles participate in tribochemical reactions with atmospheric O and steel substrate to form the tribochemical reaction film on the rubbed steel surfaces with the assistance of friction-induced heat and applied normal load. In addition, an amorphous carbon film is formed on the rubbed surface via the carbonization of base oil under the catalysis of Ni nanoparticles. The adsorbed Ni layer, the tribochemical reaction film, and the carbon layer comprise a composite tribofilm composed of amorphous carbon, polar fatty acid, metallic nickel, iron oxides, and nickel oxides on the rubbed steel surfaces, which contributes to significantly improving the antiwear ability and load-carrying capacity of the RO for the steel–steel sliding pair.

This article reports a simultaneous synthesis of polyaniline (PANI) and nickel (Ni) nanoparticles embedded in polyvinyl alcohol (PVA) film matrix by gamma radiolytic method. The mechanism of formation of PANI and Ni nanoparticles were proposed via oxidation of aniline and reduction of Ni ions, respectively. The effects of dose and Ni ions concentration on structural, optical, and electrical properties of the final PVA/PANI/Ni nanocomposites film were carefully examined. The structural and morphological studies show the presence of PANI with irregular granular microstructure and Ni nanoparticles with spherical shape and diameter less than 60 nm. The average particle size of Ni nanoparticles decreased with increasing dose and decreasing of precursor concentration due to increase of nucleation process over aggregation process during gamma irradiation. The optical absorption spectra showed that the absorption peak of Ni nanoparticles at about 390 nm shifted to lower wavelength and the absorbance increased with increasing dose. The formation of PANI was also revealed at 730 nm absorption peak with the absorbance increasing by the increase of dose. The electrical conductivity increased with increasing of dose and chlorine concentration due to number of polarons formation increases in the PVA/PANI/Ni nanocomposites. [ABSTRACT FROM AUTHOR]