Search

The understanding of the mechanical fixation behavior of coatings is crucial for a better comprehension of the bonding systems, especially at the interface between the mortar and the substrate. Physical adherence is related, among other things, to the contents of the materials used in the roughcast and mortar coatings, due to the colloidal water penetration into the pores of the substrate. This work evaluated the influence of different lime solution additions replacing the kneading water in the preparation of roughcast and mortar coatings. Two types of substrates were investigated:ceramic bricks and concrete blocks. Three wall masonry panels were constructed, with dimensions of 220 × 180 cm2, one of concrete block and two of ceramic bricks, followed by the application of roughcast and mortar coating with an average thickness of 5 mm and 20 mm, respectively. Direct tensile bond strength tests were performed and the results, with a 95% confidence level, showed that substrate ceramic and treatment in the roughcast exhibited a better behavior regarding the distribution of the tensile bond strength of the tested specimens. However, no significant differences of the amount of addition used (0%, 5%, 10% and 15%) on the tensile bond strength were observed.

Abstract: Lime-mortars to be used in restoration works of Cultural Heritage are being more and more studied. The knowledge on the lime-pastes allows understanding the behaviour of the binder fraction. The aim of this work is to study the influence of the kneading water on two critical aspects of the lime-pastes: pore structure and capillary porosity, because both of them are related to the service life of the material, particularly with the moisture transport. Mercury intrusion porosimetry has been performed to establish the pore size distribution: one pore range has been checked in the different pastes tested, setting linear relationships between the pore diameter and the water/lime ratio. Fractal geometry has been used from the MIP results in order to evaluate the pore surface complexity, as a function of the kneading water. From the results, it can be concluded that kneading water is only responsible for a swelling of the structure, but it does not change the pore surface (keeping constant the surface fractal dimension). DIA analysis has been carried out, confirming the previous results. Finally, the correlation obtained between the capillary coefficient and the water/lime ratio confirms the postulated pore structure for the different amount of kneading water in lime-pastes. [Copyright &y& Elsevier]

The understanding of the mechanical fixation behavior of coatings is crucial for a better comprehension of the bonding systems, especially at the interface between the mortar and the substrate. Physical adherence is related, among other things, to the contents of the materials used in the roughcast and mortar coatings, due to the colloidal water penetration into the pores of the substrate. This work evaluated the influence of different lime solution additions replacing the kneading water in the preparation of roughcast and mortar coatings. Two types of substrates were investigated:ceramic bricks and concrete blocks. Three wall masonry panels were constructed, with dimensions of 220 × 180 cm2, one of concrete block and two of ceramic bricks, followed by the application of roughcast and mortar coating with an average thickness of 5 mm and 20 mm, respectively. Direct tensile bond strength tests were performed and the results, with a 95% confidence level, showed that substrate ceramic and treatment in the roughcast exhibited a better behavior regarding the distribution of the tensile bond strength of the tested specimens. However, no significant differences of the amount of addition used (0%, 5%, 10% and 15%) on the tensile bond strength were observed. [ABSTRACT FROM AUTHOR]