Copyright of Eurasian Physical Technical Journal is the property of E.A. Buketov Karaganda University and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Using the method of high-frequency ion-plasma sputtering (magnetron high-frequency deposition under conditions of ion-plasma assisted using a gas (argon) plasma generator «PINK») on the surface of a high-entropy CoFeCrMnNi alloy of non-equiatomic composition. Boron-containing coatings of the elemental composition Al – Mg – B and Mg – Ti – B with a thickness of 3 μm are formed. Using transmission electron diffraction microscopy, it was found that the coatings are amorphous-crystalline, i.e. contain nanosized 1.5-2 nm islands of the crystalline phase located in an amorphous matrix. It is shown that the coating deposition is accompanied by the formation in the substrate layer (high-entropy alloy) adjacent to the coating of a nanocrystalline structure with a crystallite size of 25-40 nm. At the boundaries of the crystallites, particles of iron boride of the FeB and Fe3B compositions are revealed, which indicate the penetration of boron into the substrate. The particle size of iron boride is 5-8 nm.

Modern industry makes ever-growing demands towards decorative characteristics and protective properties of manufactured products, as well as requires increasing level of environmental friendliness. One of the most efficient technologies for improving durability of a product is applying different coatings on the effective area. Due to their flexibility ion-plasma methods of applying decorative and protective coatings are becoming more widely used in modern industry. Methods differ with high controllability of the process; capability of getting chemical compounds and alloys of given composition including films from refractory materials; better film adhesion to the surface, etc. [ABSTRACT FROM AUTHOR]