Search

Objective: Evaluating the contraction of polymerization effect of silorane-based composite on dental interface in enamel. Materials and Methods: Eighty class V cavities were confectioned in forty extracted molar teeth and restored with different combinations of resinous-based and bond system. They were divided into the following groups: (G1) three-step etch-and-rinse adhesive system and methacrylate-based resin, (G2) two-step etch-and-rinse adhesive system and methacrylate-based resin, (G3) Filtek P-90 self-conditioning adhesive system and methacrylate-based resin, (G4) Adper SE Plus self-conditioning adhesive system and methacrylate-based resin, (G5) three-step etch-and-rinse adhesive system and silorane-based resin, (G6) two-step etch-and-rinse adhesive system and silorane-based resin, (G7) Filtek P-90 self-conditioning adhesive system and silorane-based resin, (G8) Adper SE Plus self-conditioning adhesive system and silorane-based resin. Results: Group 7 showed lower marginal leakage when compared with all other groups (p = 0.001). Conclusions: The results allows suggesting that silorane-based resinous system is adequate to promote more satisfactory marginal sealing than any other combination, since the system is combined with its own bond system.

Evaluating the contraction of polymerization effect of silorane-based composite on dental interface in enamel. Eighty class V cavities were confectioned in forty extracted molar teeth and restored with different combinations of resinous-based and bond system. They were divided into the following groups: (G1) three-step etch-and-rinse adhesive system and methacrylate-based resin, (G2) two-step etch-and-rinse adhesive system and methacrylate-based resin, (G3) Filtek P-90 self-conditioning adhesive system and methacrylate-based resin, (G4) Adper SE Plus self-conditioning adhesive system and methacrylate-based resin, (G5) three-step etch-and-rinse adhesive system and silorane-based resin, (G6) two-step etch-and-rinse adhesive system and silorane-based resin, (G7) Filtek P-90 self-conditioning adhesive system and silorane-based resin, (G8) Adper SE Plus self-conditioning adhesive system and silorane-based resin. Group 7 showed lower marginal leakage when compared with all other groups (p = 0.001). The results allows suggesting that silorane-based resinous system is adequate to promote more satisfactory marginal sealing than any other combination, since the system is combined with its own bond system. [ABSTRACT FROM AUTHOR]

Aims and Objectives: Nowadays, the material that offers the best sealing characteristic in the field of endodontic treatment is the mineral trioxide aggregate (MTA), nevertheless, this material necessities an adhesive bonding agent to perfectly join to the dental surface. The aim of this study was to analyze using a scanning electron microscope (SEM) the possible microgap between the adhesive, MTA, and the dental surface. Material and Methods: Fourteen extracted molars were divided into two groups - group A was prepared with MTA-component adhesive and group B was prepared with MTA and composite dual etching. The observations were carried out with a SEM Phenom G2 Pro mode S.E.I. JMP® software was used for statistical analysis, and a t-test was used for evaluating the difference between the two groups. Results: The gap of the areas at higher magnification (1000×) with a size greater than 5 microns in width and 20 microns in length were considered significant, and only group A recorded significant data. Conclusions: The SEM analysis performed in the group A with interposition of adhesive and flow between the dental pulp chamber and MTA demonstrates the presence of a marginal gap of considerable amplitude in the all of the samples investigated. [ABSTRACT FROM AUTHOR]