Search

Poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) nanofibers embedded with borate glasses of 45B5 composition doped with Co2+, Cu2+, and Zn2+(46.1 B₂O₃26.9‐X CaO24.4 Na₂O2.6 P₂O₅, X CoO/CuO/ZnO mol % (X = 0–5)) were produced by electrospinning for wound healing applications. Prior to their addition, the glasses exhibited two broad halos typical of a vitreous borate network, which were mainly composed of ring‐type metaborate structural units. The particle distribution in the PHBV nanofibers embedded with 45B5 borate bioactive glasses is present in isolated and agglomerated states, being partially coated by a polymeric layer—except for the cobalt‐doped glass, which resulted in a successful encapsulation with 100% embedding efficiency. The incorporation of the glasses reduced the PHBV crystallinity degree and its decomposition temperature, as well as its mechanical properties, including Young's modulus, tensile strength, and elongation at break. The neat PHBV fibers and those containing the cobalt‐doped glasses demonstrated great cytocompatibility with human keratinocytes (HaCat), as suggested by the high cell viability after 7 days of exposure. Further studies are needed to fully understand the wound healing potential of these fibers, but our results significantly contribute to the area. [ABSTRACT FROM AUTHOR]

The development of bioactive membranes with bone repair properties is great interest in the field of tissue engineering. In this study, we aimed to fabricate and characterize a composite membrane composed of sol–gel synthesized bioceramics and electrospun polycaprolactone (PCL) fibers for bone tissue regeneration applications. The bioceramics were prepared using the sol–gel method with nitrate (N) and chloride (CL) as precursors. PCL and bioceramic solutions were electrospun to obtain ultrafine fiber mats. Raman spectroscopy, x‐ray diffraction (XRD), Fourier Transform Infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM) were used to characterize the materials. The results showed that both chlorinated and non‐chlorinated bioceramics contained NBOs (non‐bridge bonds) and crystallized the α‐wollastonite phase, with the chlorinated version doing so at lower temperatures. In vitro tests were performed to evaluate cytotoxicity, cell adhesion, and mineralized matrix formation on the membranes. The composite membranes showed improved cell viability and promoted mineralization nodules formation. This study presents a promising approach for the development of bioactive membranes for bone tissue engineering, with potential applications in bone regeneration therapies. [ABSTRACT FROM AUTHOR]

The development of nanoscale biomaterials associated with polymers has been growing over the years, due to their important structural characteristics for applications in biological systems. The present study aimed to produce and test polymeric scaffolds composed of polylactic acid (PLA) fibers associated with a 58S bioglass doped with therapeutic ions for use in tissue engineering. Three 58S Bioglass was obtained by the sol–gel route, pure and doped with 5% strontium and cobalt ions. Solutions of 7% PLA was used as control and added the three different bioglass, 4% of 58S bioglass (PLA‐BG), 4% bioglass‐doped strontium (PLA‐BGSr) and 4% bioglass‐doped cobalt (PLA‐BGCo). Scaffolds were produced through electrospinning process, and was characterized chemical and morphologically. The in vitro tests were performed using mesenchymal cells cultures from femurs of nine rats, grown in osteogenic supplemented total culture medium. After osteoblastic differentiation induction cell viability, alkaline phosphatase activity, total protein content quantification, and visualization of mineralization nodule tests were performed. Analysis of normal distribution used the Shapiro–Wilk test (nanofibers diameter and biological assay). Data were compared using the Kruskal–Wallis nonparametric test (p = 0.05). The bioglasses produced proved to be free of nitrate, chlorinated and nano‐sized, with effective incorporation of therapeutic ions in their structure. All materials showed cell viability (>70%), total protein production, and alkaline phosphatase activity. It was possible to develop polylactic acid scaffolds associated with 58S bioglass doped with therapeutic ions without cytotoxicity. Scaffolds characteristics appear to sustain its application in bone tissue engineering. [ABSTRACT FROM AUTHOR]

The objective was to synthesize and characterize fine polycaprolactone (PCL) fibers associated with a new 58S bioglass obtained by the precipitated sol–gel route, produced by the electrospinning process in order to incorporate therapeutic ions (Mg and Li). In PCL/acetone solutions were added 7% pure bioglass, bioglass doped with Mg(NO3)2 and Li2CO3 and were subjected to electrospinning process. The fibers obtained were characterized morphologically, chemically and biologically. The results showed the presence of fine fibers at the nanometric scale and with diameters ranging from 0.67 to 1.92 μm among groups. Groups containing bioglass showed particles both inside and on the surface of the fibers. The components of the polymer, bioglass and therapeutic ions were present in the fibers produced. The produced fibers showed cell viability and induced the formation of mineralization nodules. It was observed the applicability of that methodology in making an improved biomaterial, which adds the osteoinductive properties of the bioglass to PCL and to those of therapeutic ions, applicable to guided bone regeneration. [ABSTRACT FROM AUTHOR]

Copyright of Universidade Estadual Paulista. Revista de Odontologia is the property of Universidade Estadual Paulista. Revista de Odontologia and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)