Search

This study evaluated the microhardness of two resin cements and a low-viscosity resin composite when light-cured under different ceramic thicknesses. A total of 20 samples (10.0 × 1.0 mm) of each material were polymerized by means of a LED light source with an intensity of 1,100 mW/cm 2 for 20 seconds. For each experimental group, different ceramic thicknesses (0.5 mm, 1.0 mm, and 1.5 mm) were applied to each sample. For the control group, the samples were polymerized without the presence of ceramics. Each material was then stored in dry vials that inhibited the passage of light for a period of 24 hours. After that time, each sample underwent Vickers hardness test (HMV, Shimadzu: 25 g/10 seconds). The data were collected and analyzed using analysis of variance and Tukey test (P < .05). For the control group, RelyX Veneer (3M ESPE), Filtek Flow Z350XT (3M ESPE), and Allcem Veneer (FGM) showed mean microhardness values and standard deviations of 44.42 ± 4.9, 44.25 ± 2.4, and 31.71 ± 2.4, respectively. The lowest microhardness value (24.13) was found when the greatest ceramic thickness (1.5 mm) was used on the Allcem Veneer cement (P < .01). The microhardness of resin-based materials was affected when the 1.5-mm-thick ceramic material was interposed during photoactivation.

This study evaluated the influence of relining fiber posts on the bond strength (BS) of resin cements in the root canal. Forty bovine teeth were divided in four groups (n = 10): G1 (ARC)-fiber post cemented with resin cement RelyX ARC; G2 (ARC+Z350)-relined fiber post cemented with RelyX ARC; G3 (U200)-fiber post cemented with self-adhesive cement RelyX U200; G4 (U200+Z350)-relined fiber post cemented with RelyX U200. The roots were sectioned in six 1.2-mm slices and the push-out test was performed. Data were analyzed by three-way analysis of variance (ANOVA), and Tukey's test (a = 0.05). For the conventional resin cement, there was no significant difference between groups G1-ARC (15.5 ± 3.8) and G2-ARC+Z350 (16.1 ± 4.5). For the self-adhesive cement, the results revealed higher BS values for relined posts G4-U200 + Z350 (19.9 ± 7.9) as compared to non-relined posts G3-U200 (14.4 ± 4.5). For both cements, in groups of relined posts, the apical and the cervical thirds presented similar BS. Relining enhances the performance of the self-adhesive resin cement, and the interaction between relining and root third influences the BS to the conventional resin cement.

Unlabelled: Ideally projected to be applied on soft tissues, infrared lasers were improved by restorative dentistry to be used in hard dental tissues cavity preparations--namely enamel and dentin. This paper evidentiates the relevant aspects of infrared Erbium laser's action mechanism and its effects, and characterizes the different effects deriving from the laser's beams emission. The criteria for use and selection of optimal parameters for the correct application of laser systems and influence of supporting factors on the process, such as water amount and its presence in the ablation process, protection exerted by the plasma shielding and structural factors, which are indispensable in dental tissues cavity preparation related to restorative technique, are subordinated to optical modifications caused by the interaction of the energy dissipated by these laser light emission systems in the targeted tissue substrate., Clinical Relevance: Differences in the action of infrared Erbium laser system in regard to the nature of the ablation process and variations on the morphological aspects observed in the superficial structure of the target tissue irradiated, may be correlated to the structural optical modifications of the substrate produced by an interaction of the energy propagated by laser systems.

This study evaluated the transdentinal cytotoxicity (TC) and the bond strength (BS) of a resin-modified glass-ionomer cement (RMGIC) applied to dentin covered with smear layer (SL) of different thicknesses. Forty dentin discs had thick (TSL) or thin (THSL) smear layer created on their occlusal side. In artificial pulp chambers, MDPC-23 cells were seeded on the pulpal side of the dentin discs and divided into five groups: G1TC: no treatment (control); G2TC: TSL + RMGIC; G3TC: THSL + RMGIC; G4TC: TSL removal + RMGIC; G5TC: THSL removal + RMGIC. After 24 h, cell metabolism and morphology were evaluated by the methyltetrazolium (MTT) assay and by scanning electron microscopy (SEM), respectively. For BS, the following groups were determined: G1BS: TSL removal + RMGIC; G2BS: THSL removal + RMGIC; G3BS: TSL + RMGIC; G4BS: THSL + RMGIC. Shear bond strength was tested to failure in a mechanical testing machine MTS (0.5 mm/min). Statistically significant difference was observed only between the control and experimental groups (Kruskal-Wallis, p<0.05). The metabolic activity of the viable MDPC-23 cells in G2TC, G3TC, G4TC and G5TC decreased by 54.85%, 60.79%, 64.12% and 62.51%, respectively. Mean shear bond strength values for G1BS, G2BS, G3BS and G4BS were 7.5, 7.4, 6.4 and 6.7 MPa, respectively, without significant difference among them (ANOVA, p>0.05). RMGIC presented moderate transdentinal cytotoxic effects. Maintenance or removal of smear layer did not affect the bond strength of RMGIC to dentin substrate.

Objective: The present study evaluated the cytotoxic effects of hard setting applied on the odontoblastlike cells MDPC-23., Study Design: Eighty round-shaped samples were prepared with the following experimental materials: calcium hydroxide, Vitrebond, RelyX Luting, and RelyX Unicem. The samples were placed in serum-free culture medium and incubated for 24 hours or 7 days at 37 degrees C with 5% CO2 and 95% air. The odontoblast cells were plated in the wells and incubated for 72 hours. After this period, the complete culture medium was replaced by the extracts obtained from every sample, and the methyltetrazolium assay was carried out to evaluate the cell metabolism., Results: For the 24-hour period, the experimental materials calcium hydroxide, Vitrebond, RelyX Luting, and RelyX Unicem decreased the cell metabolic activity by 91.52%, 81.14%, 78.17%, and 2.64%, respectively. For the 7-day period, calcium hydroxide, Vitrebond, RelyX Luting, and RelyX Unicem decreased the metabolic activity of the MDPC-23 cells by 91.13%, 87.27%, 79.04%, and 10.51%, respectively., Conclusion: RelyX Unicem presented the lowest cytopathic effects to the cultured odontoblast cell line.