Search

Fungal mycelium is an emerging bio-based material. Here, mycelium films are produced from liquid shaken cultures that have a Young’s modulus of 0.47 GPa, an ultimate tensile strength of 5.0 MPa and a strain at failure of 1.5%. Treating the mycelial films with 0–32% glycerol impacts the material properties. The largest effect is observed after treatment with 32% glycerol decreasing the Young’s modulus and the ultimate tensile strength to 0.003 GPa and 1.8 MPa, respectively, whereas strain at failure increases to 29.6%. Moreover, glycerol treatment makes the surface of mycelium films hydrophilic and the hyphal matrix absorbing less water. Results show that mycelium films treated with 8% and 16–32% glycerol classify as polymer- and elastomer-like materials, respectively, while non-treated films and films treated with 1–4% glycerol classify as natural material. Thus, mycelium materials can cover a diversity of material families.

We report on the role of temperature and shear on the melt behavior of iPP in the presence of the organic compound N1,N1′-(propane-1,3-diyl)bis(N2-hexyloxalamide) (OXA3,6). It is demonstrated that OXA3,6 facilitates a viscosity suppression when it resides in the molten state. The viscosity suppression is attributed to the interaction of iPP chains/subchains with molten OXA3,6 nanoclusters. The exact molecular mechanism has not been identified; nevertheless, a tentative explanation is proposed. The observed viscosity suppression appears similar to that encountered in polymer melts filled with solid nanoparticles, with the difference that the OXA3,6 compound reported in this study facilitates the viscosity suppression in the molten state. Upon cooling, as crystal growth of OXA3,6 progresses, the decrease in viscosity is suppressed. Retrospectively, segmental absorption of iPP chains on the surface of micrometer-sized OXA3,6 crystallites favors the formation of dangling arms, yielding OXA3,6 crystallites decorated with partially absorbed iPP chains. In other words, the resulting OXA3,6 particle morphology resembles that of a hairy particle or a starlike polymer chain. Such hairy particles effectively facilitate a viscosity enhancement, similar to branched polymer chains. This hypothesis and its implications for the shear behavior of iPP are discussed and supported using plate-plate rheometry and slit-flow experiments combined with small-angle X-ray scattering analysis.

We report on the effect of an aliphatic oxalamide based nucleating agent (OXA3,6) on the melt and crystallization behavior of isotactic polypropylene (iPP) under defined shear conditions. Through polarized optical microscopy, we demonstrate that OXA3,6 self-assembles from the iPP melt into rhombic crystals whereas their size and distribution proved highly dependent on the employed cooling rates. The presence of 0.5 wt % of OXA3,6 in iPP results in a significant suppression in iPP melt viscosity, which could not be explained via molecular modeling. A possible cause for the drop in viscosity in the presence of OXA3,6 is attributed to the interaction (absorption) of high molecular weight iPP chains with the nucleating agent, thereby suppressing their contribution to the viscoelastic response of the melt. This proposed mechanism for the suppression in melt viscosity appears similar to that encountered by the homogeneous distribution of nanoparticles such as CNTs, graphene, and silica. Shear experiments, performed using a slit flow device combined with small-angle X-ray diffraction measurements, indicate that crystallization is significantly enhanced in the presence of OXA3,6 at relatively low shear rates despite its lowered sensitivity to shear. This enhancement in crystallization is attributed to the shear alignment of the rhombic OXA3,6 crystals that provide surface for iPP kebab growth upon cooling. Overall, the suppression in melt viscosity in combination with enhanced nucleation efficiency at low as well as high shear rates makes this self-assembling oxalamide based nucleating agent a promising candidate for fast processing.

We report on the effect of an aliphatic oxalamide based nucleating agent (OXA3,6) on the melt and crystallization behavior of isotactic polypropylene (iPP) under defined shear conditions. Through polarized optical microscopy, we demonstrate that OXA3,6 self-assembles from the iPP melt into rhombic crystals whereas their size and distribution proved highly dependent on the employed cooling rates. The presence of 0.5 wt % of OXA3,6 in iPP results in a significant suppression in iPP melt viscosity, which could not be explained via molecular modeling. A possible cause for the drop in viscosity in the presence of OXA3,6 is attributed to the interaction (absorption) of high molecular weight iPP chains with the nucleating agent, thereby suppressing their contribution to the viscoelastic response of the melt. This proposed mechanism for the suppression in melt viscosity appears similar to that encountered by the homogeneous distribution of nanoparticles such as CNTs, graphene, and silica. Shear experiments, performed using a slit flow device combined with smallangle X-ray diffraction measurements, indicate that crystallization is significantly enhanced in the presence of OXA3,6 at relatively low shear rates despite its lowered sensitivity to shear. This enhancement in crystallization is attributed to the shear alignment of the rhombic OXA3,6 crystals that provide surface for iPP kebab growth upon cooling. Overall, the suppression in melt viscosity in combination with enhanced nucleation efficiency at low as well as high shear rates makes this self-assembling oxalamide based nucleating agent a promising candidate for fast processing.