Search

Purpose: To quantify hydrogen peroxide (H2O2) penetration into restored bovine teeth subjected to whitening treatment. Materials and Methods: Seventy-five enamel/dentin disks were divided into 5 groups (n = 15): intact disks (G1); cavity preparation only (G2); conventional adhesive system and composite resin (G3); resin-modified glass-ionomer cement (G4); and self-etching adhesive only (G5). After 24 h, the disks were placed into artificial pulp chambers containing an acetate buffer solution, and the first whitening session was performed using a 35% H2O2 (hydrogen peroxide) product. The disks were submitted to 10,000 thermal cycles and then stored for 1 year in deionized water. After this period, a second whitening session was performed. After each whitening procedure, the buffer solutions were analyzed for optical density in a spectrophotometer to assess the amount of H2O2 that had diffused. ANOVA and Tukey's test were used to compare the different groups and a Student's t-test was used to compare the different times (p ≤ 0.05). Results: Prior to aging, group 2 had the highest penetration of H2O2; the other groups showed similar, lower penetration. After thermocycling and aging, all groups showed a significant increase in H2O2 penetration. The greatest penetration of H2O2 into the pulp chamber was found in groups 2 and 5. Conclusion: Aged restorations allowed greater H2O2 permeation through the tooth structure. [ABSTRACT FROM AUTHOR]

Copyright of Revista Dental Press de Estética is the property of Dental Press International and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Purpose: To quantify hydrogen peroxide (H2O2) penetration into restored bovine teeth subjected to whitening treatment., Materials and Methods: Seventy-five enamel/dentin disks were divided into 5 groups (n = 15): intact disks (G1); cavity preparation only (G2); conventional adhesive system and composite resin (G3); resin-modified glass-ionomer cement (G4); and self-etching adhesive only (G5). After 24 h, the disks were placed into artificial pulp chambers containing an acetate buffer solution, and the first whitening session was performed using a 35% H2O2 (hydrogen peroxide) product. The disks were submitted to 10,000 thermal cycles and then stored for 1 year in deionized water. After this period, a second whitening session was performed. After each whitening procedure, the buffer solutions were analyzed for optical density in a spectrophotometer to assess the amount of H2O2 that had diffused. ANOVA and Tukey's test were used to compare the different groups and a Student's t-test was used to compare the different times (p ≤ 0.05)., Results: Prior to aging, group 2 had the highest penetration of H2O2; the other groups showed similar, lower penetration. After thermocycling and aging, all groups showed a significant increase in H2O2 penetration. The greatest penetration of H2O2 into the pulp chamber was found in groups 2 and 5., Conclusion: Aged restorations allowed greater H2O2 permeation through the tooth structure.