To optimize the gas transfer, adsorption and photo-generated charge separation in the process of photocatalytic CO2 reduction by g-C3N4, the photocatalytic materials were designed from the aspects of foam pore structure and heterojunction construction. The typical g-C3N4 foam was first constructed using surfactant foaming method, and then Cu(OH)2 nanosheets were loaded to prepare the Cu(OH)2/CNF composites with projects of electroless copper plating and hydrogen oxidation treatment. The structure and photocatalytic properties of the as-prepared samples were investigated. The results show that g-C3N4 foam and Cu(OH)2/CNF all demonstrate developed structures with 3D micron pore frameworks, which is conducive to improving CO2 diffusion and adsorption at dynamics during gas-solid catalytic process. The adsorption amounts of CO2 for g-C3N4 foam and Cu(OH)2/CNF are respectively 3.97 cm3/g and 3.59 cm3/g, which are 2.96 times and 2.68 times respectively higher than that of pure g-C3N4 powder. Moreover, many Cu(OH)2 nanosheets are also formed in the Cu(OH)2/CNF samples which provide a way to simultaneously broaden light absorption and form heterojunction between g-C3N4 and Cu(OH)2. This heterojunction can accelerate the separation of photo-generated e--h+ and make photo-generated electrons transfer from g-C3N4 to Cu(OH)2. As a result, the Cu(OH)2/CNF has demonstrated optimal photocatalytic activity with CO production rate at 11.041 μmol·g-1·h-1, which is 2.76 times and 6.83 times respectively higher than that of g-C3N4 foam and g-C3N4 powder.

Copyright of Journal of Materials Engineering / Cailiao Gongcheng is the property of Journal of Materials Engineering Editorial Office and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)