Search

This article presents the results of studies of the features of the development of thermoelastic martensitic transformations during cooling/heating in the free state and under load of Ti50Ni49.7−XNbXMo0.3 alloys (X = 0.5, 1.0 and 1.5 at% Nb) with shape memory effects. Using X-ray diffraction analysis, it was found that all the alloys studied at room temperature contained a multiphase mixture consisting of intermetallic compounds with the TiNi (B2, B19′), Ni56Ti29Nb15, and Ti2Ni compositions. Scanning electron microscopy was used to study the microstructure of TiNi (Nb,Mo) alloys and it was found that the distribution of fine Ni56Ti29Nb15 particles in the matrix depends significantly on the concentration of the alloying element. A correlation was established between changes in the structural-phase state in TiNi (Nb,Mo) alloys and the occurrence of the B2↔B19′ martensitic transition in the free state and under load. Based on physical and mechanical studies, the temperature ranges of the martensitic transformations (MT) in the free state and under load were established. Based on the thermodynamic description of the MT and the analysis of the characteristic temperatures of the MT, it was found that the MT mechanism is strongly dependent on the concentration of the alloying element. [ABSTRACT FROM AUTHOR]

Digital light processing (DLP) or stereolithography is the most promising method of additive manufacturing (3D printing) of products based on high-energy materials due to, first of all, the absence of a high-temperature impact on the material. This paper presents research results of an ultraviolet (UV)-cured urethane methacrylate polymer containing 70 wt.% of high-energy solid powder based on ammonium salts, which is intended for digital light processing. Polymerization of the initial slurry is studied herein. It is shown that the addition of coarse powder transparency for the UV radiation to resin increases its curing depth. The thickness of the layer, which can polymerize, varies from 600 µm to 2 mm when the light power density ranges from 20 to 400 mJ/cm2, respectively. In DLP-based 3D printing, the obtained material density is 92% of the full density, while the compressive strength is 29 ± 3 MPa, and the ultimate tensile strength is 13 ± 1.3 MPa. The thermogravimetric analysis shows the decrease in the thermal decomposition temperature of UV-cured resin with high-energy additives compared to the thermal decomposition temperatures of the initial components separately. Thermal decomposition is accompanied by intensive heat generation. The burning rate of obtained samples grows from 0.74 to 3.68 mm/s, respectively, at the pressure growth from 0.1 to 4 MPa. Based on the results, it can be concluded that DLP-based 3D printing with the proposed UV photocurable resin is rather promising for the fabrication of multicomponent high-energy systems and complex profile parts produced therefrom. [ABSTRACT FROM AUTHOR]

In this work, the impact of ErF3 submicroparticles on the microstructure and mechanical properties of the A359 alloy was studied. ErF3 particles provided a homogeneous structure in castings produced via the casting method. The modifying effect of ErF3 particles on the structure of Al–Si alloys is realized through the mechanism of restraining the crystallization front and is achieved through the reduction in the formation of clusters of iron phases and eutectic lamellar silicon. It was found that the addition of 1 wt% ErF3 to the A359 alloy leads to a decrease in the average grain size by 21% and an increase in the yield strength by 14%, in tensile strength by 16%, in the microhardness of Al15(FeMn)3Si2 phase by 34% and in the Al15(FeMnCr)3Si2 phase by 7%. The heat treatment of the A359 alloy with ErF3 particles increased the yield strength by 36% and the tensile strength by 34%. The absence of an effect of ErF3 particles on the hardness values of the A359 alloy, as well as on the fracture process of the A359 alloy, was observed. The negative influence of ErF3 particle agglomerates and clusters on the strength characteristics of the investigated alloys was observed. Approaches for further exploring the potential of ErF3 particles as a strengthening phase in cast aluminum alloys of the Al–Si system were proposed. [ABSTRACT FROM AUTHOR]

In work studies of phase composition, hardness and density of materials based on AlMgB14 synthesized by hot pressing method at temperatures of 1300 and 1400 °C under pressure 50 MPa from aluminum, magnesium and boron powders (E1 mixture), as well as from original powder of aluminum-magnesium alloy (E2 mixture) were conducted. AlMgB14 phase content of obtained bulk samples is ~ 95 wt. %. The maximum hardness of 14GPa and density of 2.1 g/cm3, respectively, has a sample, marked as E1, synthesized at a temperature of 1400 °C.

This paper presents the results of studies on AlMgB14-based ceramic coatings deposited on WC-Co hard alloy substrates using RF plasma sputtering. The aim of this work is to study the structure, phase composition, and mechanical properties of AlMgB14-based coatings depending on the sputtering mode. According to the results of the microstructural study, the bias voltage applied to the substrate during the sputtering process significantly contributed to the formation of the coating morphology. Based on the results of compositional and structural studies by energy dispersive X-ray spectroscopy, X-ray diffraction, and Raman spectroscopy, it was found that the coatings are composed of nanocrystalline B12 icosahedrons distributed in an amorphous matrix consisting of Al, Mg, B, and O elements. The nanohardness of the coatings varied from 24 GPa to 37 GPa. The maximum value of the hardness together with the lowest coefficient of friction (COF) equal to 0.12 and wear resistance of 7.5 × 10−5 mm3/N·m were obtained for the coating sputtered at a bias voltage of 100 V. Compared with the COF of the original hard alloy substrate, which is equal to 0.31, it can be concluded that the AlMgB14-based coatings could reduce the COF of WC-based hard alloys by more than two times. The hardness and tribological properties of the coatings obtained in this study are in good agreement with the properties of AlMgB14-based materials obtained by other methods reported in the literature. [ABSTRACT FROM AUTHOR]