Here we present a magnetic thin film with a weak ferrimagnetic (FIM) phase above the N\'eel temperature ($T_{N}$ = 240 K) and a non-collinear antiferromagnetic (AFM) phase below, exhibiting a small net magnetisation due to strain-associated canting of the magnetic moments. A long-range ordered FIM phase has been predicted in related materials, but without symmetry analysis. We now perform this analysis and use it to calculate the MOKE spectra in AFM and FIM phases. From the good agreement between the form of the measured and predicted MOKE spectra, we propose the AFM and FIM phases share the magnetic space group C2'/m' and that the symmetry driven magneto-optic and magneto-transport properties are maximised at room temperature in the FIM phase due to the non-zero intrinsic Berry phase contribution present in these materials. A room temperature FIM phase with large optical and transport signatures, as well as sensitivity to lattice strain and magnetic field, has useful prospects for high-speed spintronic applications., Comment: 21 pages 4 figures 1 table 4 supplementary figures 1 supplementary table Co-first author: F. Johnson and J. Z\'azvorka Corresponding authors: L. F. Cohen and M. Veis; Typos corrected and discussion of symmetry added; title changed to be concise; text on figures made larger

Despite belonging to a well-studied family of transition metal trihalides, VI_3 has received significant attention only recently. As a hard ferromagnetic van der Waals compound with a large coercivity, it attracted much attention because of its potential use in atomically thin spintronic and optoelectronic devices. However, practical exploration of VI_3 is challenging due to its instability under ambient conditions. Here, we present a comprehensive set of optical, x-ray diffraction, magnetization, and ellipsometric measurements of VI3 and demonstrate that, similarly to the related van der Waals ferromagnet CrI_3, the degradation process is accelerated by the presence of moisture. The VI_3 surface was covered by selected media commonly used in physical measurements to test its stability and lower the degradation rate three times or higher, providing practical information for experimentalists interested. The decomposition study at ambient conditions shows that the VI_3 single crystal can be used for most of the bulk, magnetization, and optical measurements without any noticeable change of physical properties, as the significant degradation appears first after ~ 2 hours of exposition as illustrated, e.g., by the evolution of the ferromagnetic T_1 and T_2 transitions. The ellipsometric measurement demonstrates that even the surface remains optically stable for at least 5 minutes., Comment: 14 pages, 6 figures