Search

This study investigates the morphology and properties of biocomposites based on a blend of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) and poly (lactic acid) (PLA) 50/50 (w/w) reinforced with untreated (UNDF) and alkali‐treated (ATDF) Diss (Ampelodesmos mauritanicus) fibers at 20 wt. %. Moreover, PHBV‐g‐MA used as the compatibilizer was added at 5 wt. % to the alkali‐treated biocomposites. Morphology, and crystallinity, thermal, thermo‐mechanical, rheological and mechanical properties of PHBV/PLA biocomposites were studied. The study showed that the treated Diss fibers were uniformly dispersed in both PLA and PHBV phases. This results in a good interfacial adhesion between the components, as observed by scanning electron microscopy (SEM). Further, the results also indicated that the compatibilized biocomposite samples showed an enhancement in crystallinity degree and heat deflection temperature (HDT) passing from 48.7% to 62.4% and 119.2 to 132.9°C, respectively, in comparison with the neat blend. Similar trend is also observed with the tensile data indicating a significant increase in Young's modulus by almost 48.5% compared to PHBV/PLA matrix. This is due to better interactions between Diss fibers and PHBV/PLA matrix. The results suggest the occurrence of a synergistic effect between PHBV‐g‐MA and alkali‐treated Diss fibers in the development of materials with interesting properties and could be a potential means to expand their applications. [ABSTRACT FROM AUTHOR]

Highlights The present research investigates the influence of chemical modifications on the surface of Diss fibers (Ampelodesmos mauritanicus) as an effective reinforcing agent for biocomposites based on poly (3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV). The Diss fiber surface underwent three different chemical treatments: alkaline, alkaline/peroxide, and alkaline/silane. Changes in morphology, mechanical properties, thermomechanical behavior, and contact angle measurements of the biocomposite materials were studied according to the following weight ratio PHBV/Diss fibers 80/20. Scanning electron microscopy (SEM) analysis of the fractured surface of the biocomposite samples revealed improved adhesion between Diss fibers and the PHBV matrix after surface modification, compared with the unmodified sample. The study demonstrated that the incorporation of Diss fibers leads to an enhancement in the mechanical performances of PHBV‐based biocomposites. The tensile properties of the modified biocomposites showed a significant increase in Young's modulus compared with the biocomposites with untreated fiber. Similar trends were observed in the data obtained from dynamic mechanical analysis (DMA) and contact angle measurement. Overall, the study highlights the beneficial effects of Diss fibers modification, particularly with the alkali–silane combination, in enhancing the properties of PHBV biocomposites, there by broadening their potential application fields. The study explores the potential of Diss fibers as an effective reinforcement for PHBV‐based biocomposites. Fully biodegradable biocomposites based on PHBV/Diss fibers are melt‐compounded. Diss fibers are chemically modified by alkaline, alkaline/peroxide, and alkaline/silane. The chemical treatment has considerably enhanced the properties and morphology of the biocomposites, being however much higher for alkaline/silane treatment. The method can be used for specific applications and large‐scale production. [ABSTRACT FROM AUTHOR]