Search

In this study, a novel biodegradable polymer electrolyte membrane with reduced fuel crossover, high selectivity, and high conductivity compared with Nafion 117 membrane in direct ethanol fuel cells (DEFCs) has been reported. Herein, polyvinyl alcohol/epoxidized natural rubber (PVA/ENR) blend membranes were synthesized via a simple solution casting method and applied in DEFCs. The structural and physicochemical features of the PVA/ENR blend membranes were examined using FESEM, FTIR, XRD, water absorption, ethanol uptake, swelling ratio and oxidative stability. ENR enhances the chemical, structural, and mechanical characteristics of PVA, making it a valuable material in fuel cell applications. The incorporation of ENR into the PVA matrix results in a compact morphology, excessive multifunctional groups, low fuel crossover, and high selectivity. The optimum membrane thickness achieves the highest selectivity, reaching up to 12.32 × 104 S s cm−3 at 30°C. Additionally, the maximum power density achieved is 19.52 mW cm−2, surpassing that of the Nafion membrane, which is only 14.55 mW cm−2 at 90°C. Furthermore, this biodegradable membrane can sustain operation for 1000 h at 90°C, owing to its ability to maintain hydration for an extended period. This study represents the first attempt to combine PVA and ENR in fuel cells. [ABSTRACT FROM AUTHOR]

This manuscript elucidates the preparation and utilization of liquid epoxidized natural rubber (LENR) with 50 mol% epoxidation level (LENR50) as a polymeric plasticizer for poly(vinyl chloride) (PVC), and further immobilization of the plasticizer in the plastic matrix through subsequent ultraviolet (UV)‐curing treatment. The plasticizing effect induced by LENR50 at 50 wt% loading was evident with a reduction of Tg from a high of 72.0 to 11.4°C. Positive enhancements were also documented in the mechanical properties of the LENR50‐plasticized PVC, specifically the big improvement in elongation at break and elastic modulus, from 106% to 430%, and from 646 to 7 MPa, respectively. The UV‐treated PVC/LENR film also exhibited superior resistance to migration compared with formulations with conventional plasticizers such as di‐2‐ethylhexyl phthalate (DEHP) and triethyl‐2‐acetyl citrate (ATEC). A similar outcome was recorded in the leaching resistance test, where LENR50 had the best resistance to leaching in four different solvents (water, soap solution, ethanol, and toluene). The LENR50‐plasticized PVC film recorded the lowest weight loss following 24 h immersion in both hydrophilic and lipophilic solvents. The findings from this study suggest that LENR50 could serve as an efficient bio‐based polymeric plasticizer for PVC. Highlights: LENR as bio‐based polymeric plasticizer for PVC.Significant reduction in Tg and elastic modulus of PVC plasticized with LENR.UV treatment improved tensile strength and elongation at break of LENR/PVC film.UV‐treated PVC/LENR has superior plasticizer migration and leaching resistance. [ABSTRACT FROM AUTHOR]

In this work, a pure gum mould made of prevulcanized natural rubber/cloisite-Na+ nanocomposite (PVNR/CN) was prepared and characterized for ornament application. The suitable conditions to prepare PVNR/CN latex mixtures and the properties of the resulting PVNR/CN nanocomposites were investigated. The optimum CN concentration in the latex mixture was 1.0 phr, with the properties of 60 wt% total solid content, more than 600 sec mechanical stability time, lower than 350 cP Brookfield viscosity, and pH 10. The properties of PVNR/CN nanocomposite showed high strength, moderate hardness, and good thermal stability. The morphology by TEM showed well dispersion of CN particles in between the rubber dispersoid. The PVNR/CN nanocomposite as a mould was evaluated by shrinkage measurement. The presence of 1.0 phr CN in the PVNR/CN nanocomposite achieved the least shrinkage. The reproduced object using the PVNR/ CN nanocomposite as a mould showed complete fine details similar to the original object via visual observation. [ABSTRACT FROM AUTHOR]

The degradation of epoxidized natural rubber (ENR-50) and liquid epoxidized natural rubber (LENR) was done via oxidative degradation method for the production of hydroxyl terminated epoxidized natural rubber (HTENR) and hydroxyl terminated liquid epoxidized natural rubber (HTLENR) has been analysed. Cobalt (II) acetylacetonate (CAA) were used as an oxidizing agent for chain scission reaction at temperature 60 °C in the presence of ethanol. The reaction temperature was fixed at 60 °C meanwhile reaction time and the amount of CAA were varied according to the reaction formulation. The HTENR and HTLENR obtained have been characterized using Gel Permeation Chromatography (GPC), Fourier Transform Infrared (FTIR) and Nuclear Magnetic Resonance (NMR). GPC were used to determine the molecular weight before and after the oxidative degradation of respected HTENR and HTLENR were compared with ENR-50 and LENR. The lowest Mn and Mw of HTLENR that were obtained from the oxidative degradation method were found to be 5,163 g/mol and 58,087 g/mol. The appearances of OH end groups were verified by FTIR and NMR analyses to validate the position of each OH functional groups. FTIR analysis confirmed that HTENR and HTLENR contained OH group with the appearance of a broad peak around 3,400 cm-1 to 3,550 cm-1 after the reaction. The presence of OH end groups was verified by NMR analysis with the appearance at 3.39 ppm and 3.66 ppm, corresponding to methylene proton adjacent to hydroxyl group in HOCH2CH2CH2 and methane proton adjacent to OH group in CH2CH2CH(OH)CH3. [ABSTRACT FROM AUTHOR]

Polylactic acid (PLA) is a potential polymer to be used in various applications due to biodegradable and biocompatible characteristics. However, its brittle nature limits the usage of PLA. In order to improve the brittleness of PLA, liquid epoxidized natural rubber (LENR) was incorporated with PLA. The objective of this study is to investigate the effect of LENR as toughening agent on rigid PLA matrix in term of mechanical and thermal properties. Polylactic acid/liquid epoxidized natural rubber (PLA/LENR) blends were prepared by melt blending method using Brabender internal mixer with temperature 160 °C, mixing speed of 60 rpm and molded into test samples by compression molding. The LENR content was varied from 0, 5, 10, 15 and 20 wt%. It was found that the addition of LENR increased the impact strength of PLA.10 wt% of LENR showed the optimum impact strength which was 86.05 J/m. However, tensile strength and tensile modulus decreased slightly with increasing of LENR content. The morphology of PLA/LENR blends showed a good dispersion of LENR on PLA matrix at 10 wt% LENR. The differential scanning calorimeter (DSC) showed a gradual drop in melting temperature (Tm) as well as glass transition temperature (Tg) as LENR content increased. [ABSTRACT FROM AUTHOR]