Search

On the one hand, cermet has the advantages of metal materials, and on the other hand, it maintains the excellent properties of ceramic materials, and is a very important new engineering material. In this paper, the alumina/aluminum cermet material composite powder was prepared by ball milling, and its densification properties were characterized and studied to provide reference for the preparation of high-performance cermet materials. When the ball milling time is more than 6h, the distribution of alumina particles around the aluminum powder is relatively uniform. The research shows that: with the extension of the ball milling time, the number of pinning of Al2O3 particles on the surface of the Al ball first increases and then decreases; The trend of decreasing; with the increase of ball-to-powder ratio, the distribution of Al2O3 particles on the surface of Al balls is more uniform. Considering its cost-effectiveness, it is more suitable to prepare pinned alumina/aluminum-ceramic composite powder under the conditions of ball milling speed of 360r/min, ball-to-material ratio of 2:1 and ball milling time of 12h. When the Al content gradually decreased, the density and hardness of the cermet material also decreased gradually. When the Al content gradually decreased, the density and hardness of the cermet material also decreased gradually. When Al accounts for 75% in the sample, the microstructure is dense and the hardness is higher. When the molding pressure is 20MPa, the unevenness of the surface of the material is greatly relieved, relatively flat, and the densification effect is better. When the sintering temperature is 800°C, the fired sample is very dense, and the particles have relatively high bonding strength, but a small amount of aluminum is precipitated on the surface of the sample, forming a silver-white spherical substance.

In view of the low performance of porous ceramics on the wall, the heavy task of saving clay resources, and the major problems of dredging the Yangtze River, this thesis uses low-grade quartz sand along the Yangtze River as the main raw material and kaolin as the plasticizer. Drying, sintering and other processes prepare high-performance porous quartz ceramics, and improve the performance of porous quartz ceramics by studying the control conditions and the control mechanism related to the performance of the sintered body. Quartz porous ceramic bodies were sintered at 1100 °C and 1200 °C, and no obvious gradient structure was found. However, the quartz porous ceramic bodies had obvious gradient structures after sintering at 1300°C. The quartz porous ceramic bodies were sintered. When the temperature is 1400 °C, the green body is not found to have a pore gradient structure. When the water-to-material ratio is 1.2 and 1.3, the quartz porous ceramic body has no obvious gradient structure; when the water-to-material ratio is 1.4, 1.5, the sample has an obvious gradient structure. Combining the cost performance between material performance and energy consumption, in order to obtain a better bonding point, porous silica ceramics should be prepared with a water-to-material ratio of 1.4 and a sintering temperature of 1300 °C to prepare porous silica ceramics with a better pore gradient structure. Its porosity is 32.45%, and its compressive strength is 5.23 MPa.

In this paper, the YAG powder is prepared by the co-precipitation method. In addition, the sintering aid to aid sintering and the high temperature foaming agent that becomes gas released during the heating process so that the sample has pores, the ball mill mixes the material, and the sample press is extruded. Box-type resistance furnace sintering. Through this process, porous ceramics can be made. Study the effect of sintering aid content, foaming agent type, sintering temperature on the properties of YAG porous materials. The analysis and discussion can lead to the following conclusions: as the content of sintering aid silica in the sample increases, the sintering temperature of the sample decreases. It is best when the ratio of sintering aid alumina to silica is 3:1. The moldability of the sample whose foaming agent is wood chips is worse than that of the sample whose foaming agent is fiber and carbon powder. The ratio of sintering aid alumina to silica is 3:1, and the sintering temperature of the sample with carbon powder as the blowing agent is best when the sintering temperature is 1400 °C.

The effect of forming technology on the properties of quartz sand porous materials were researched with the low grade quartz sand along the Yangtze River via the pressureless sintering method in this paper, which lay technology foundation for researching new heat insulating materials. The wear of ball milling media is investigated through adjusting the ball milling parameter via the weigh methods. The results are shown that the porosity of quartz sand porous materials are decreased with increasing a forming pressure. The porosities of Φ30 and Φ50 materials are decreased with increasing a holding pressure time, however, the porosity decreasing rate of Φ30 is slower than that of Φ50. The porosity of Φ50 is higher than that of Φ30 under same forming conditions. Through optimized the forming conditions, the porosity of sintered Φ50 quartz matrix porous materials reaches 54.52% under the forming pressure for 5MPa and the holding pressure time for 5min.

In order which aim to save land resource and use low grade nature resource to realize high cost performance product. In this paper, the molding method of quartz sand fired brick is discussed. As the plastic (hand pressing) is only used to manually beat the mud mass, the sludge is squeezed by hand. Into the mold and molding and cold isostatic pressure molding pressure of 100 MPa, The difference is far away, which makes the gaps between the particles close to each other greatly different, the pressure of hand-press molding is small, the voids in the blank after molding are large and the hole diameter is large, and the green compact density of the brick body is small. The compact densities of the 65MPa and 150MPa pressed brick bodies are all lower than 100MPa, but 150MPa is still denser than 65MPa. The compressive strength is first increased and then decreased with increasing the molding pressure, when the pressure is 100 MPa, the maximum compressive strength is achieved at 100 MPa achieves the highest point.

Given the shortage of energy reserves, new energy sources must be identified. In this regard, improving the efficiency of solar cell conversion and simplifying the solar cell technology have become the focus of research. In this study, tin oxide nanometer thin film was fabricated on FTO conductive glass as photocathode through hydrothermal method. The synthesis condition was regulated, and performance test was also conducted. Results show that the crystallization driving force, crystallization rate, and grain size of tin dioxide crystal increase with increasing alkali ratio, leading to disorganized accumulation of tin oxide. Under prolonged holding time, tin oxide crystal became complete, and the surface area of the crystal increased. The crystallization driving force and rate also increased with increasing salt concentration and accompanied by clutter of tin oxide. The optimized process condition included 1:4 molar ratio of salt to alkali, 0.05 mol/L salt concentration, 200 °C reaction temperature, and 8 days of reaction. The highest specific surface area of the tin oxide nanometer film was obtained under the optimized condition.

This work investigated the effects of molar ratio of salt to alkali on the properties of tin oxide nanofilms to provide reference for optimizing its photoelectric conversion efficiency. The tin oxide film grown by hydrothermal method exhibited poor film-forming property. The macroscopic analysis revealed the formation of a thick film. The bonding force to the FTO substrate was poor, its brittle, and easy to fall off. When the molar ratio of salt to alkali was 1:8, the tin oxide film exhibited improved microstructure and large specific surface area, which could benefit electron transport. Moreover, the film showed excellent photoelectric conversion performance. However, mechanical properties, such as adhesion between the tin oxide film and the conductive glass FTO, remain to be improved.

Alumina ceramics with good mechanical and corrosion resistance are the ones of the most widely used engineering ceramics. The aluminum has high strength, high conductivity and high plasticity etc. so that aluminum ceramics are used in more and more industries. In this paper, the mass fraction of 25% Al2O3 powder and the mass fraction of 75% Al powder were mixed in the blender. Mixer speed is100r/min with mixing time of 3.5 h. Forming, sintering and a series of processes for preparing the alumina/aluminum metallic ceramic materials, through performance testing and analysis, found that the density of the sample firstly increased and then decreased with the increase of sintering temperature. A melting point is close to the sintering temperature and the density of the cermet can be made relatively high. When the sintering temperature is about 600°C and 700°C, the macro performance of sample is better. The cermet is sintered at 700°C and its microstructure is relatively better.

YAG has many excellent features and therefore has a wide range of applications. Preparation and properties of YAG porous ceramics via the casting method is investigated. Through analysis and discussion, the following conclusions can be obtained. With the increase of the content of foaming agent, in the foaming process of the slurry, bubbles generated by the foaming agent and water are gradually increased, the more pores are left in the body after casting, and when the blowing agent is too much, excessive bubbles are generated, which can lead to a very low strength of the green body and can not be formed and operated later. As the ratio of water to material increases, the porosity of the porous material increases. This is because when the blowing agent is constant, the amount of water required for foaming is constant, and the amount of foam generated is also constant. When the content of foaming agent and the ratio of water to material is both 1, the porosity and compressive strength is better.

A composite complex salt—(NH4)1.91(In0.91Sn0.09)Cl5· ?H2O—was synthesized from the starting materials InCl3, HCl, SnCl4 and NH4HCO3. The hydrolyzate of (NH4)1.91(In0.91Sn0.09)Cl5· ?H2O were prepared under the condition of room temperature and fiercely stirring, using NH4HCO3 as precipitator and polyethylene glycol as disperser. Indium-tin oxide (ITO) nanoparticles were prepared by calcined the hydrolyzate at 700°C for 1 h in air. The prepared ITO particles were characterized via X-ray diffractometry, scanning electron microscopy and laser particle size analyzer. The results indicated the average crystalline grain size, a primary particle size and an average aggregation size of prepared ITO powders is 34.6 nm, 50–100 nm and of 107 nm, respectively.