Search

This paper highlights the sound absorption performance of microperforated panel (MPP) made from coconut fiber and polylactic acid (PLA) composite named as biocomposite microperforated panel (BMPP). Coconut fiber was used to produce BMPP specimen and PLA was used as matrix. Impedance tube method was employed to identify the sound absorption performance of BMPP specimen while a porosity tester was used to determine the porosity of BMPP specimen. Comparison on the sound absorption performance between BMPP and steel MPP will be discussed in this paper. It has been found that BMPP with different composition percentage of coconut fiber and PLA possessed different sound absorption performance mainly due to the existence of pores and tortuous structure within the specimen itself. Scanning electron microscope (SEM) scan was performed to further analyze the structure of BMPP specimen. [ABSTRACT FROM AUTHOR]

This paper investigates the sound absorption of biodegradable composite micro-perforated panel (BC-MPP) made from kenaf fibre and biodegradable polymer known as polylactic acid (PLA). BC-MPP samples were made through conventional machining method such as mixing, drilling, and hot pressing process. Sound absorption of BC-MPP samples were measured by using impedance tube. The porosity and tensile strength of BC-MPP samples were determined by using porosity tester and universal testing machine respectively. The effects of material composition and air gap thickness behind the panel towards the sound absorption coefficient of BC-MPP samples along with the porosity and tensile strength of BC-MPP samples will be presented in this paper. Results indicate that the sound absorption coefficient of BC-MPP samples could be affected by the difference of composition percentage of kenaf fibre and PLA. The porosity of BC-MPP sample increases along with the increment of kenaf fibre composition. However, the increment of kenaf fibre composition causes the reduction of tensile strength of BC-MPP sample. As the air gap thickness behind the panel increases, the peak absorption of BC-MPP sample shifts nearer to lower frequency range. The maximum sound absorption coefficient of BC-MPP sample can be varied as well by altering the air gap thickness behind the panel. [ABSTRACT FROM AUTHOR]

Both natural and synthetic fibers do not perform well at low frequencies and are also subjected to erosion, moisture, fire, etc., when used as an interior finish of room walls. To overcome these problems, micro-perforated plate with different thickness is used in a multilayer sound absorber configuration to improve its sound absorption. Firstly, the acoustic properties of five natural wastes including sheep wool, goat wool, camel wool as well as pith and fiber bundles of sugarcane bagasse were determined by using an impedance tube following ISO 10534–2. Secondly, the effect of Panel thickness was investigated. The maximum sound absorption coefficient (SAC) of natural waste materials is at middle to high-frequency range and this shifted to lower frequency as the porous layer thickness increases. The sound absorption performance depends on the thickness of perforated plate and porous layer in a compound sound absorber. It is observed that the using perforated plate in the front of low thickness porous materials significantly improve the SAC and absorption bandwidth. However, it should be noted that this reduces the SAC at high frequencies. Accordingly, the thick micro-perforated panels backed by porous layer are not recommended to control sounds with frequency higher than 3000 Hz. [ABSTRACT FROM AUTHOR]