Hydrogen peroxide chemo-mechanical pulp (APMP), sulfonated chemo-mechanical pulp (SCMP), and chemical thermomechanical pulp (CTMP) were used as raw materials to explore the effects of hydrogen peroxide (HP), Fenton pretreatment (FP), and ethanol pretreatment (EP) on the enzymatic hydrolysis of high-yield bamboo mechanical pulp (HBMP). The surface lignin distribution and contents of different HBMPs were determined using confocal laser scanning microscopy (CLSM) and X-ray photoelectron spectroscopy (XPS). The correlation between the surface lignin and the enzymatic hydrolysis of HBMP was also investigated. The residue of enzymatic hydrolysis was used to adsorb methylene blue (MB). The results showed that the cracks and fine fibers on the surface of APMP, SCMP, and CTMP increased after FP, when compared to HP and EP. The total removal content of hemicellulose and lignin in SCMP after FP was higher than with HP and EP. Compared to SCMP, the crystallinity increased by 15.4%, and the surface lignin content of Fenton-pretreated SCMP decreased by 11.7%. The enzymatic hydrolysis efficiency of HBMP after FP was higher than with HP and EP. The highest enzymatic hydrolysis of Fenton-pretreated SCMP was 49.5%, which was higher than the enzymatic hydrolysis of Fenton-pretreated APMP and CTMP. The removal rate of MB reached 94.7% after the adsorption of the enzymatic hydrolysis residue of SCMP. This work provides an effective approach for a high value-added utilization of high-yield bamboo pulp.

Hot water (HW), green liquor (GL), and sodium chlorite (SC) pretreatments were used to pretreat sugarcane bagasse (SCB) and spruce (SP) and then to prepare cellulose nanofibers (CNFs) through high-pressure homogenization to explore the effect of physicochemical properties on the thermal stability and ultraviolet (UV) resistance performance of CNF films. The results indicated that the lignin content of HW-pretreated CNFs was higher than that of GL- and SC-pretreated CNFs, and the hemicellulose content of HW-pretreated CNFs was lower than that of GL- and SC-pretreated CNFs. The synergy of lignin and hemicellulose impacted the thermal stability of CNF films. The thermal stability of all the SP CNF films was higher than that of all the SCB CNF films. Hot water pretreatment improved the thermal stability of CNF films, and green liquor and sodium chlorite pretreatment decreased the thermal stability of CNF films. The highest thermal stability of SP-HW CNF films reached 392 °C, which was 5.4% higher than that of SP-SC CNF films. Furthermore, the ultraviolet resistance properties of different CNF films were as follows: SCB-HW &gt, SCB-GL &gt, SCB-SC and SP-HW &gt, SP-GL &gt, SP-SC. Green liquor pretreatment is an effective method to prepare CNFs. Conclusively, this research provides a basic theory for the preparation of CNFs and allows the improvement of CNF films in the application of thermal stability management and UV resistance fields.