Search

A complex study of the adhesion of multi-walled carbon nanotubes to a titanium surface, depending on the modes of irradiation with He+ ions of the "MWCNT/Ti" system, was conducted using atomic force microscopy and X-ray photoelectron spectroscopy. A quantitative assessment of the adhesion force at the interface, performed using atomic force microscopy, demonstrated its significant increase as a result of treatment of the "MWCNT/Ti" system with a beam of helium ions. The nature of the chemical bonding between multi-walled carbon nanotubes and the surface of the titanium substrate, which causes this increase in the adhesion of nanotubes to titanium as a result of ion irradiation, was investigated by X-ray photoelectron spectroscopy. It was established that this bonding is the result of the formation of chemical C–O–Ti bonds between titanium and carbon atoms with the participation of oxygen atoms of oxygen-containing functional groups, which are localized on defects in the nanotube walls formed during ion irradiation. It is significant that there are no signs of direct bonding between titanium and carbon atoms. [ABSTRACT FROM AUTHOR]

A comparative study of the electronic structure of the salen ligand in the H2(Salen) molecule and the [Ni(Salen)] complex was performed using the experimental methods of XPS, UV PES, and NEXAFS spectroscopy along with DFT calculations. Significant chemical shifts of +1.0 eV (carbon), +1.9 eV (nitrogen), and −0.4 eV (oxygen) were observed in the 1s PE spectra of the salen ligand atoms when passing from a molecule to a complex, unambiguously indicating a substantial redistribution of the valence electron density between these atoms. It is proposed that the electron density transfer to the O atoms in [Ni(Salen)] occurred not only from the Ni atom, but also from the N and C atoms. This process seemed to be realized through the delocalized conjugated π-system of the phenol C 2p electronic states of the ligand molecule. The DFT calculations (total and partial DOS) for the valence band H2(Salen) and [Ni(Salen)] described well the spectral shape of the UV PE spectra of both compounds and confirmed their experimental identification. An analysis of the N and O 1s NEXAFS spectra clearly indicated that the atomic structure of the ethylenediamine and phenol fragments was retained upon passing from the free salen ligand to the nickel complex. [ABSTRACT FROM AUTHOR]

The results of studies of marine sponge carbonization processes during thermal treatment in an argon atmosphere in the temperature range from room temperature to 1200 °C are presented. The spatial structure, atomic composition of native and carbonized sponges, and their changes during pyrolysis were characterized using a set of methods that are informative at the macro- (thermogravimetric analysis, derivative thermogravimetric analysis, differential scanning calorimetry), micro- (Raman spectroscopy, scanning electron microscopy, energy dispersive spectroscopy), and nanoscales (X-ray absorption and photoelectron spectroscopy using synchrotron radiation and a sample charge compensation system). Preservation of the 3D architecture at the macro- and microlevels and graphitization of the interfibril medium with the formation of turbostratic graphite at the nanolevel were demonstrated. It was shown that the atomic contents of nitrogen, carbon, and oxygen in the spongin were ~2–3 at.%, ~5 at.%, and ~4 at.%, respectively. The matter concentrated in the space between the spongin fibrils included ~70 at.% carbon and ~11 at.% oxygen, with a large proportion of carbon (~63 at.%) involved in the formation of aromatic and C–C bonds and the remainder in carbon monoxide compounds. After the decomposition of spongin at 400 °C, this substance transformed into turbostratic graphite, preserving the 3D architecture of the original marine sponge as the temperature rose. [ABSTRACT FROM AUTHOR]