Search

Beech wood has a high frequency of defects such as red heartwood, reaction wood (tension wood). For the experimental measurements four logs without visible defects like red heartwood, which can noticeably affects the measurements' results were qualified. The drying medium temperature in the first phase of the process before the moisture content of the specimens fell below the FSP was maintained at 45 °C. Then, the temperature was gradually increased to the maximum value 65 °C. The results showed that different initial wood moisture content does not affect to final value of tension and normal wood. The colorimetric parameter L* was much higher for tension wood. After steaming, there were greater differences in the colorimetric parameters, respectively, a* and b*. After drying the difference of all colorimetric parameters between tension and normal wood was significantly less. The color changes were only noticed in the surface layers of specimens. Differences were small, and thus, the impact of the tension wood on the color changes was not confirmed. However, since the lightness of tension wood plays a key role for its visual detection, it may be adequate to only measure the lightness parameter (L*). [ABSTRACT FROM AUTHOR]

The color changes of compression and opposite spruce (Picea abies L. Karst) wood were evaluated as a function of different drying conditions. Compression wood samples and their corresponding opposite wood samples from the opposite part of the log were compared after three different drying modes. The color of the samples before and after the drying was characterized using the color coordinates L*, a*, b*, C*ab, C, h*, Sab, and the color difference (ΔE*) in the standard color space according to the International Commission on Illumination (CIELAB). The drying temperature was the most remarkable factor for discoloration of the samples. The lightness (L*) of the samples decreased with increased temperature. However, darkening was more pronounced in the opposite wood samples. The overall color difference (ΔE*) was found to be higher in the opposite wood. The compression wood was more statured in color with a deeper hue angle due to the drying process. [ABSTRACT FROM AUTHOR]

The article presents the impact of drying process and selected parameters on the color changes on the surface of pine wood (Pinus sylvestris L.). Three predetermined process conditions (modes), mild, normal, and intensive, were investigated. The experiments were conducted using a semi-industrial scale dryer designed at the Gdańsk University of Technology with a loading capacity of 0.55 m3. The drying process was applied to pine wood grown in the northern part of Pomeranian region in Poland. The specimens were selected taking into consideration the radial angle of the growth rings. During each drying mode, 25 pieces of wood with dimensions (thickness, width, length) of 0.03 m, 0.2 m, and 1.5 m, respectively, were dried. The total color change (E) after drying process and color saturation (h*) before and after drying processes of the wood surface was determined using the normalized CIELAB methods. The obtained results indicated that the color change of the pine wood surface increased simultaneously with the intensification of the drying process. However, the normalized wood quality after drying under intensive drying process conditions remained within the standard limits. The application of intensive drying process conditions remarkably changes the surface color of the obtained material, while remarkably reducing the drying process duration. [ABSTRACT FROM AUTHOR]

This study focused on the impact of the wood sawing pattern on 50 mm thick beech timber, followed by cross-cutting on the 3 m long, 50 x 50 mm beech blanks. The study analyzed two methods of cutting patterns of beech blanks (parallel to the surface of the timber and parallel to the grain fiber of the timber) regarding yield values and the size of longitudinal warping after air-drying. The yield values were higher (from 65.14 to 72.70 %) when producing long beech blanks using the method of sawing parallel to the timber's axis (B) compared to parallel to the edge of the blank (from 60.38 to 68.40 %). Results showed that a crucial factor for choosing the cutting method (A or B) is the taper of the logs. For blanks with a taper ≥ 1.3 cm.m-1, it is more advantageous in terms of longitudinal warping and yield to use the method of sawing parallel to the timber's axis. [ABSTRACT FROM AUTHOR]

The mechanical properties of wood have remarkable influence on its use in buildings. The improvement of the mechanical properties enables the reduction in the cross-sections of structural elements, particularly the increase in their load. The paper deals with the change in the mechanical properties of beech wood through the process of contact drying. Plate pressures of 1.0, 1.4, and 1.6 MPa at a temperature of 160 °C were used. It was found that contact drying increased the bending strength by more than 30% compared to convection drying. The value of Brinell's hardness measured on the surface of the samples increased by 80 to 98% after contact drying, and the measured values of impact toughness were higher, about 31.1% compared to the samples dried by the convection drying method. As a result of contact drying, the density in the absolutely dry state increased for radial samples by 102.3 kg·m−3 and for tangential samples by 83.1 kg·m−3. The pressure of the plates also had an effect on the change in density. [ABSTRACT FROM AUTHOR]

The subject of this paper is the analysis of the influence of laser cutting of oak wood on its drying process. The subject of the research was the comparison of the drying process and the quality of the dried wood in samples cut by classical technology (sawing) and samples cut with the use of laser. The research was carried out on two sets of samples which were subjected to an identical drying process. Continuous moisture loss and final moisture attained, moisture gradients before and after drying, and internal tensions before and after drying were monitored by means of the fork test and the cut-test. The final moisture content at the end of drying was 8.09% for the saw-cut samples and 8.22% for the laser-cut samples, a difference of only 0.13%. The analysis of the individual characteristics observed showed that the influence of the cutting technology did not have a significant effect on the drying process or the quality of the dried oak sawn timber. [ABSTRACT FROM AUTHOR]

This study examined the changes in the properties of beech wood (Fagus sylvatica L.) after intense drying. Beech wood with false red heartwood was selected as the test specimen. The test samples had dimensions of 50 mm thickness, 180 mm width, and 350 mm length. The specimens were divided into two groups, false red heartwood and sapwood. These specimens were selected with different angles of the growth rings (radial and tangential). The results showed that samples with red heartwood, in comparison to samples with sapwood content, had a remarkable effect in covering. Observation of specimens with false red heartwood and sapwood before and after drying process revealed significant differences in color changes and measured values during the covering-slicing test, but not between samples with different growth ring angles. [ABSTRACT FROM AUTHOR]

The influence of the impregnation process of pine wood (Pinus sylvestris L.) samples on the electrical resistance changes and the moisture-content measurement accuracy is presented in this paper. In this study, the resistances of impregnated and nonimpregnated green pine timber harvested from northern Poland were compared. An impregnation method based on a vacuum-pressure chamber was used. Copper salts were applied as the impregnated solutions. The obtained results of the electrical resistance comparison showed a dependence of wood resistance on the moisture content. Higher conductivity occurred in impregnated wood samples filled with copper salt compared with wood samples without impregnation. Noticeable differences in the electrical resistance values were observed when the wood moisture content was significantly above the Fibre Saturation Point (FSP). [ABSTRACT FROM AUTHOR]