Search

This recommendation is devoted to testing the resistance of natural stone and fired-clay brick units against salt crystallization. The procedure was developed by the RILEM TC 271-ASC to evaluate the durability of porous building materials against salt crystallization through a laboratory method that allows for accelerated testing without compromising the reliability of the results. The new procedure is designed to replicate salt damage caused by crystallization near the surface of materials as a result of capillary transport and evaporation. A new approach is proposed that considers the presence of two stages in the salt crystallization test. In the first, the accumulation stage, salts gradually accumulate on or near the surface of the material due to evaporation. In the second, the propagation stage, damage initiates and develops due to changes in moisture content and relative humidity that trigger salt dissolution and crystallization cycles. To achieve this, two types of salt were tested, namely sodium chloride and sodium sulphate, with each salt tested separately. A methodology for assessing the salt-induced damage is proposed, which includes visual and photographical observations and measurement of material loss. The procedure has been preliminarily validated in round robin tests.

Natural cement, called "Roman” cement, was invented at the end of the 19th century and played an important role in the development of civil engineering works until the 1860s. More surprisingly, it was also used to restore historic buildings, such as gothic cathedrals. This paper deals with the mineralogy and the durability of natural cement in the particular case of the Bourges Cathedral in France. This study illustrates the interest of this material particularly adapted in stone repair or substitution. Contrary to traditional mortars, the present samples are made of neat cement paste, revealed by the absence of mineral additions as quartz or carbonate sand. Several combined techniques (SEM-EDS, TGA, XRD) were carried out to determine the composition of the hydraulic binder rich in calcium aluminate hydrates. The raw marl at the origin of the cement production contains oxidized pyrites which consist in a potential source of sulphate pollution of the surrounding limestone. The exposition of the cement in urban environment leads to some weathering features as atmospheric sulfation. Finally a petrophysical approach, based on water porosity, capillary sorption and compressive strength, has been performed to demonstrate the durability and the compatibility of natural cement applied as an historical building restoration mortar

Natural cement, called "Roman” cement, was invented at the end of the 19th century and played an important role in the development of civil engineering works until the 1860s. More surprisingly, it was also used to restore historic buildings, such as gothic cathedrals. This paper deals with the mineralogy and the durability of natural cement in the particular case of the Bourges Cathedral in France. This study illustrates the interest of this material particularly adapted in stone repair or substitution. Contrary to traditional mortars, the present samples are made of neat cement paste, revealed by the absence of mineral additions as quartz or carbonate sand. Several combined techniques (SEM-EDS, TGA, XRD) were carried out to determine the composition of the hydraulic binder rich in calcium aluminate hydrates. The raw marl at the origin of the cement production contains oxidized pyrites which consist in a potential source of sulphate pollution of the surrounding limestone. The exposition of the cement in urban environment leads to some weathering features as atmospheric sulfation. Finally a petrophysical approach, based on water porosity, capillary sorption and compressive strength, has been performed to demonstrate the durability and the compatibility of natural cement applied as an historical building restoration mortar