Search

In this work, the syntheses and characterization by mechanical and dielectric spectroscopies of (1-x) Bi0.5Na0.5TiO3-xBaTiO3 (BNT-100xBT), with x = 0.05, 0.06 and 0.07, lead-free piezoelectric ceramics is reported. Ceramic samples of BNT-BT have been prepared by mixed-oxide method and then conventionally sintered. X-ray diffraction patterns of sintered samples, indicated for BNT-7BT the presence of tetragonal (P4mm) complex perovskite structure, whereas for BNT-5BT and BNT-6BT the samples exhibit a mixture of tetragonal (P4mm) and rhombohedral (R3c) crystalline phases, which reveal the presence of a morphotropic phase boundary (MPB) in the BNT-BT system. Measurements of internal friction, Q-1, and the storage modulus, E’, as a function of temperature at various frequencies were carried out in a Dynamic Mechanical Analyzer (DMA), in the temperature range from 0ºC to 600ºC. Dielectric profiles are recorded in the frequency range from 1kHz to 100kHz and the temperature range from room temperature to 475ºC. Mechanical loss spectra obtained for investigated compositions of BNT-BT samples showed different frequency-independent anomalies. Two main anomalies for BNT-5BT and BNT-6BT, observed around 100ºC and 430ºC were associated with the ferroelectric-antiferroelectric and antiferroelectricparaelectric phase transitions, respectively. The results obtained from mechanical loss measurements were supported by dielectric relaxation spectra. For BNT-7BT, outside the MPB, four different frequency-independent processes were observed.

A study was conducted to analyze the dielectric behavior of lead niobate ferroelectric, Pb[Nb.sub.2][O.sub.6] (PN) ceramics in the frequency range of 20 Hz-2 GHz. The two dielectric dispersion processes, the low- and high-frequency dispersions were found to be associated with the contribution of the point defects, related to the lead losses during the sintering process and to the dynamics of polar regions boundaries, respectively.

Characteristics of phase transitions of lead barium niobate compositions around the morphotropic phase boundary were investigated. Using structural characterizations, it was found that the morphotropic phase boundary extends toward a wide composition range, in which both tetragonal (4mm) and orthorhombic (m2m) tungsten bronze phases coexist. In addition, on heating, two phase transitions were observed for all the studied compositions. First, the fraction with m2m symmetry phase transforms into the 4mm symmetry one and, second, the 4mm symmetry phase, which represents the whole material, transforms into the paraelectric phase (4/mmm symmetry). The phase transition temperatures were determined from dielectric characterizations. These results helped to improve the phase diagram of the pseudobinary PbNb2O6–BaNb2O6 system around the morphotropic phase boundary region. [ABSTRACT FROM AUTHOR]

High Curie temperature ferroelectrics are promising materials to construct transducers for high-temperature piezoelectric applications. Among them, the lead niobate system is one that displays such characteristic. In this work, the dielectric behavior of lead niobate ferroelectric ceramics was analyzed in the frequency range of 20 Hz-2 GHz. Ceramic samples with nominal formula PbNb2O6 (PN) were prepared by the solid-state reaction method. The phase transition was investigated with the Santos-Eiras’ phenomenological model. The values of the parameter, which determine the phase transition character (ξ), are close to 1, indicating a conventional ferroelectric phase transition. The PN materials showed two different dispersion processes: (1) a typical high-frequency dispersion process, which may be associated with the polar region boundaries dynamics, as observed in ferroelectric materials in the microwave frequency region, and (2) that associated with the charge carrier conduction, observed in the lowest frequencies and high-temperature region. An additional dispersion process, in the intermediate frequency range (around 2 MHz), was identified, which may be related to the overlapping between both the normal dipolar process (characteristic of the dipolar materials) and the strong low-frequency conductive process. [ABSTRACT FROM AUTHOR]

The characteristics of phase transitions of lead barium niobate compositions around the morphotropic phase boundary are examined. The phase transition temperatures are determined from dielectric characterizations and the results have improved the phase diagram of the pseudobinary Pb[Nb.sub.2][O.sub.6]-Ba[Nb.sub.2][O.sub.6] system around the morphotropic phase boundary region.