Search

Background/Objective The objective of this study is to determine the effect of aging on tensile strength and surface condition of orthodontic aligners on days 0, 1, 5, 7, 10, and 14. Materials/Methods The total sample of 80 aligners included five brands (Accusmile®, Angel®, GRAPHY®, Invisalign® and Suresmile®) were placed in a thermocycler to imitate the temperature variations of the oral cavity and accelerate aging for 50, 250, 350, 500, and 700 cycles. The mechanical tensile properties (Young's modulus E, yield strength YS, maximum elastic stress MES, Ultimate Tensile Strength UTS, and maximum stress MS) were measured by Universal Testing Machine at a rate of 5 mm of deformation per minute for 4 minutes. Microscopic observations were made under a voltage of 10 kV at magnifications times 50, 250, 500, 1000, and 2500 after cleaning with ethanol and ultrasound then metallization with gold. Results YS and MES of Angel® aligners are statistically reduced after five days of aging (P  = .003). Aligners from the most rigid to the most flexible are (decreasing E): Accusmile® > GRAPHY® > Suresmile® > Invisalign® > Angel®. Surface conditions also deteriorated with aging (appearance of scratches, porosity, cracks, etc.). GRAPHY® aligners are more heterogeneous and weaker than others. Limits In vitro study Conclusion Mechanical properties of Accusmile®, GRAPHY®, Invisalign®, and Suresmile® were not affected by aging. YS and MES were reduced from day 5 for Angel® aligners. Surface conditions are also altered by aging. [ABSTRACT FROM AUTHOR]

This article discusses a case report on the treatment of multiple-tooth agenesis, retention, and impaction. It explains the causes and diagnostic methods for maxillary canine impaction and presents three treatment options. The article also discusses the best approach for treating patients with maxillary lateral-incisor agenesis. The treatment resulted in satisfactory esthetics and dental alignment. The article acknowledges that further improvements could have been made and includes images and analysis of a patient with multiple tooth agenesis. [Extracted from the article]

Background Taking into account radiation doses, safety, and protection, we highlighted the features in which cone-beam computed tomography (CBCT) can offer an advantage compared to the conventional two-dimensional imaging in paediatric dentistry before orthodontic treatment. Objective The aim of this article was to conduct a systematic review to assess the diagnostic efficacy of CBCT in the paediatric population at a pre-orthodontic phase. Search methods MEDLINE via PubMed was searched to identify all peer-reviewed articles potentially relevant to the review until 1 July 2018. Relevant publications were selected by two reviewers independently. Selection criteria The literature selection for this systematic review was carried out according to the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement and was based on predetermined inclusion criteria. Data collection and analysis Data were collected on overall study characteristics and examination characteristics of the selected studies. Methodological quality of the selected studies was evaluated. Original studies were assessed using the Quality Assessment of Diagnostic Accuracy Studies (QUADAS) tool. Thereafter, levels of evidence were obtained according to Grading of Recommendations Assessment, Development and Evaluation criteria. Results As a result of the QUADAS assessment, a total of 37 articles were included in the protocol. Following a proper protocol, CBCT was regarded as a reliable tool for assessment and management of impacted canine and root fracture. It provided a better evaluation of normal and pathological condylar shape and volume. CBCT was a superior choice for pre-surgical diagnostic applications in cleft lip and/or palate over a medical computed tomography based on its lower radiation exposure, shorter investigation time, and low purchase costs. Conclusions CBCT is justified only in those cases where conventional radiography fails to provide a correct diagnosis of pathology. Therefore, it cannot be regarded as a standard method of diagnosis. CBCT imaging may also be justified when it positively affects treatment options or provides treatment optimization. Registration None. Conflict of interest None to declare. [ABSTRACT FROM AUTHOR]

Objectives: The aim of this paper was to compare failure differences in precious metal customized lingual brackets bonded with three adhesive systems. Also, differences in failure of non-precious metal brackets with and without a silicatized base layer bonded with the same adhesive, as well as the influence of enamel etching prior to using a self-etching dual cure resin were explored. Materials/methods: Five different groups were defined in a semi-randomized approach. Group 1 (IME): Maxcem Elite with 378 Incognito brackets and etched teeth, Group 2 (IMNE): Maxcem Elite with 193 Incognito brackets on non-etched teeth, Group 3 (INE): Nexus+Excite with 385 Incognito brackets, Group 4 (IRE): Relyx with 162 Incognito brackets, Group 5 (HRME) and Group 6 (HNRME): Maxcem Elite with 182 Harmony brackets with silicatized and non-slicatized bases respectively. Bracket failures were recorded over a 12-month period. Results: The number of failures during the observation period was small in the various adhesives types of groups, as well as in HRME and HNRME groups, and the comparisons among those groups were non-significant (P > 0.05). A statistically significant difference (P < 0.05) was found between the IME and IMNE groups. Conclusions: 1. During the first year of treatment customized lingual brackets failure frequencies (rates) are not different for the three adhesive materials tested. 2. Eliminating the etching stage when using self-etch/self-adhesive adhesives, may lead to a dramatic increase in the failure rates. 3. Silicoating of stainless steel customized lingual brackets does not seem to influence the failure of the bonds. [ABSTRACT FROM AUTHOR]

Mini-implants and miniscrews are commonly used in orthodontics to provide additional temporary intraoral anchorage. Partial osseointegration represents a distinct advantage in orthodontic applications, allowing effective anchorage to be combined with easy insertion and removal. This article reports the histomorphometric findings of the osseointegration of bracket screw bone anchors (BSBAs). In an experimental animal study, four BSBAs were inserted in the alveolar process of the lower jaw in each of five male beagle dogs, aged 6.5 months from the same mother. Eleven screws were lost during the study, nine of them due to lack of primary stability. One screw was removed at the end of the examination period for evaluation of ease of removal. After 6 months, histological evaluation of the eight remaining screws was performed to evaluate the extent of osseointegration. All eight screws showed partial osseointegration (mean 74.48 per cent, standard deviation ± 15.33 per cent). The amount of osseointegration was independent of loading time and location (anterior or posterior), as tested with an independent samples t-test (P> 0.05). Analysis of the data indicated that small titanium screws were able to function as rigid osseous anchors against an orthodontic load of 200 cN for 6, 12, 18, or 24 weeks after a minimal healing period or no healing period. These findings show that miniscrews, used for temporary anchorage in orthodontics, partially osseointegrate. [ABSTRACT FROM AUTHOR]

The aim of the present study was to determine whether there is a difference in toxicity and loss of viability of three dimensional (3D) reconstructed human oral epithelium (RHOE) cell cultures induced by point welded (PW), laser welded (LW), and silver-soldered (SIS) orthodontic wires. Three types of soldered stainless steel (SS) wires: PW, LW, and SiS were prepared (n = 3) and subjected to multiple end-point analysis (MEA), Six pieces were cut from each wire. Each piece was placed on the triplicate cell cultures (RHOE model based on TR 146 cells). After 24 hours of topical exposure, the cell cultures were cut and stained with haematoxylin/eosin, Toxicity was assessed by evaluating the morphological changes and classifying these as mild, moderate, or severe. The in vitro cell cultures were subjected to a 3-(4,5-dimethylthiazol-2-yl)2,5-diphenyl tetrazolium bromide (MTT) assay in order to quantify viability. Copper wires served as the control to determine severe toxicity and native cell cultures were used as a baseline. Untreated SS wire (0.9 mm) was included for comparison with the welded wires. Histological evaluation with respect to toxicity and measurement of viability in the 3D cell cultures showed no severe toxicity or toss of viability for any of the wires. The morphological ranking of the tested wires from mild to severe toxicity was: SS = PW LW < SiS. MTT tests revealed the following mean viability values: native cell line (negative control) 99,1 per cent, SS 96.8 per cent, PW 95.5 per cent, LW 95.5 per cent, SiS 85.7 per cent, and copper wires (positive control) 51.2 per cent. Relative comparison between the different welding techniques tested on RHOE revealed, however, that LW and PW wires induced less toxicity/loss of viability compared with SiS wires. [ABSTRACT FROM AUTHOR]

The aim of the present study was to determine whether used orthodontic wires made of different materials cause toxicity and loss of viability on three-dimensional (3D) cell cultures. Three types of orthodontic wires, stainless steel, Nitinol, and TMA (n = 9) which had been used clinically in fixed appliances for a period of 1 month, were retrieved at random from five patients, Both upper and lower archwires were collected and subjected to two different protocols: to assess toxicity, two pieces of each wire were placed on 3D cell cultures (reconstituted human epithelium); to investigate the possibility of cell damage, the 3-(4,5-dimethylthiazol-2-yl)2,5-diphenyl tetrazolium bromide (MTT) assay was used and haematoxylin and eosin staining was performed to evaluate morphological changes. Copper wire served as the centre/to determine the morphology of severe toxicity, and native cell cultures and silk were used as the negative controls. Morphological evaluation of the native cell cultures revealed no toxic reactions. The ranking, from mild to severe toxicity was as follows: stainless steel < Nitinol = TMA. There were no significant differences between TMA and Nitinol. The MTT assay revealed the following mean percentage values for viability: native cell line (negative control), 100; stainless steel, 102.25; TMA, 87.4; Nitinol, 85.3; and copper wire (positive control) 57.2. Histological evaluation of the 3D cell cultures showed no severe toxicity or loss of viability for any of the wires. However, relative comparison between the different wires revealed that stainless steel induced less toxicity/loss of viability compared with TMA and Nitinol wire. [ABSTRACT FROM AUTHOR]