Search

To understand and model performance in supercritical CO2 (sCO2) for high-efficiency, concentrating solar power (CSP) and fossil energy power cycles, reaction rates are compared at 750°C in 0.1 MPa CO2 and 30 MPa sCO2 as well as laboratory air as a baseline on structural materials such as Ni-based alloy 625. Due to the thin reaction products formed even after 5000 h, scanning transmission electron microscopy was used to study the Cr-rich surface oxide scale. The scales formed in CO2 and sCO2 had a much finer grain size with more voids observed in CO2. However, the observations on alloy 625 were complicated by Mo and Nb-rich precipitates in the adjacent substrate and Al internal oxidation. To simplify the system, a binary Ni-22Cr alloy was exposed for 1000 h in similar environments. After exposure in sCO2, there was an indication of carbon segregation detected on the Cr2O3 grain boundaries. After exposure in air, metallic Ni precipitates were observed in the scale that were not observed in the scale formed on alloy 625. The scale formed in air on a second Ni-22Cr model alloy with Mn and Si additions did not contain Ni precipitates, suggesting caution when drawing conclusions from model alloys. [ABSTRACT FROM AUTHOR]

Initial experimental work at 700°-800 °C is in progress to develop a lifetime model for supercritical CO2 (sCO2) compatibility for a 30-year lifetime of a >700 °C concentrated solar power system. Nickel-based alloys 282, 740H and 625 and Fe-based alloy 25 are being evaluated in 500-h cycles at 1 and 300 bar, and 10-h cycles in 1 bar industrial grade CO2. The alloys showed similar low rates of oxidation in 1 and 300 bar CO2 in 500-h cycles at 750 °C. However, in 10-h cycles, alloy 25 showed accelerated attack at 700° and 750 °C. Transmission electron microscopy scale cross-sections on alloy 25 after 1000 h at 700 °C in sCO2 and in air only showed a small row of carbides beneath the scale in the former environment. Similar characterisation was performed on alloys 625 and 282 after sCO2 exposure at 750 °C. [ABSTRACT FROM AUTHOR]

To fabricate oxide dispersion strengthened bond coatings, commercial Co-30wt-%Ni-20Cr-8Al-0•4Y powder was milled with 2% additions of Al2O3, Y2O3 or Y2O3 + HfO2. Low-pressure plasma sprayed, free-standing specimens were oxidised in air + 10%H2O at 1100 °C both isothermally (100 h) and in 500, 1−h cycles. Dry air cyclic testing conducted at both ORNL and FZJ showed remarkably similar results. In general, the water vapour addition caused more scale spallation. Two LPPS specimens without oxide additions were tested for comparison. The specimens with 2%Al2O3 addition exhibited the best behaviour as the powder already contained 0•4%Y. Additions of 2%Y2O3 and especially 1%Y2O3 + 1%HfO2 resulted in over-doping as evidenced by high mass gains and the formation of Y- and Hf-rich pegs. Scanning transmission electron microscopy of the isothermal specimens showed no Hf and/or Y segregation to the alumina scale grain boundaries in the over-doped specimens. [ABSTRACT FROM AUTHOR]

Preliminary research has demonstrated the ability to utilise novel scan strategies in the electron beam melting (EBM) process to establish control of crystallographic texture within Inconel 718 deposits. Conventional EBM scan strategies and process parameters yield coarse columnar grains aligned parallel to the build direction. Through varying process parameters such as beam power, beam velocity, beam focus and scan strategy, the behaviour of the electron beam can be manipulated from a line source to a point source. The net effect of these variations is that the resulting crystallographic texture is controlled in a manner to produce either epitaxial deposits or fully equiaxed deposits. This research demonstrates the ability to change the crystallographic texture on the macroscale indicating that EBM technology can be used to create complex geometric components with both site-specific microstructures and material properties. [ABSTRACT FROM AUTHOR]

Small angle neutron scattering (SANS) and scanning transmission electron microscopy (STEM) were used to study film formation by magnesium alloys AZ31B (Mg-3Al-1Zn base) and ZE10A (Elektron 717. E717: Mg-1Zn + Nd, Zr) in H2O and D20 with and without 1 or 5 wt% NaCl. No SANS scattering changes were observed after 24 h D2O or H2O exposures compared with as-received (unreacted) alloy, consistent with relatively dense MgO-base film formation. However, exposure to 5 wt% NaCl resulted in accelerated corrosion, with resultant SANS scattering changes detected. The SANS data indicated both particle and rough surface (internal and external) scattering, but with no preferential size features. The films formed in 5 wt% NaCl consisted of a thin, inner MgO-base layer, and a nano-porous and filamentous Mg(OH)2 outer region tens of microns thick. Chlorine was detected extending to the inner MgO-base film region, with segregation of select alloying elements also observed in the inner MgO, but not the outer Mg(OH)2. Modeling of the SANS data suggested that the outer Mg(OH)2 films had very high surface areas, consistent with loss of film protectiveness. Implications for the NaCl corrosion mechanism, and the potential utility of SANS for Mg corrosion, are discussed. [ABSTRACT FROM AUTHOR]